Synthesis and photoluminescence properties of novel red-emitting Ca14Mg2(SiO4)8:Eu3+/Sm3+ phosphors

Novel red-emitting Eu3+, Sm3+ singly doped and co-doped Ca14Mg2(SiO4)8 phosphors were prepared by conventional solid- state reaction. Powder X-ray diffraction patterns were employed to confirm phase pu...     

Thermoluminescence characteristics of NaSr4（BO3）3：Ce^3＋ under β-ray irradiation

The thermoluminescence (TL) properties of Ce3+ doped NaSr4(BO3)3 phosphor under the β-ray irradiation were reported. The polycrystalline sample was synthesized by high temperature solid-state reaction. The TL glow curve of NaSr4(BO3)3:Ce3+ phosphor was com-posed of only one peak. TL kinetic parameters of NaSr4(BO3)3:Ce3+ were deduced by the peak shape method, the activation energy (E) was 0.590 eV and the frequency factor was 1.008×106s-1. TL dose response was linear in the range of measurement. The 3-dimensional (3D) TL emission spectrum was also recorded, the emission spectrum consisted of two bands located at 441 and 479 nm respectively, corresponding to the characteristic 4f05d1→2F(5/2,7/2) transitions of the Ce3+ ion. The fading behavior of the NaSr4(BO3)3:Ce3+ phosphor over a period of 15 d was also studied.     

Long-lasting phosphorescence study on Y_3Al_5O_（12） doped with different concentrations of Ce~（3＋）

Long-lasting phosphorescence (LLP) was observed in Ce-doped Y3Al5O12 phosphors synthesized in reducing atmosphere. The characteristic emission of the 2D-2F5/2 and 2D-2F7/2 transition of Ce3+ in photoluminescence (PL) and LLP spectra was studied. It was interesting that the ratio between the peak areas of 2D-2F5/2 and 2D-2F 7/2 transitions in the PL spectrum was different from the ratio of that in LLP emission spectrum. And the ratios had different change regularities with increased Ce3+ concentration. The p...     

Luminescent properties of blue long-lasting phosphorescence phosphors Sr6Al18Si2O37：Eu2＋,RE3＋

A series of novel blue long-lasting phosphorescence phosphors Sr6A118Si2037：Eu^2＋,RE^3＋ （RE3＋=Ho^3＋, Gd^3＋, Dy^3＋ and Pr^3＋） were prepared by the conventional high-temperature solid-state reaction in a reductive atmosphere. Their properties were systemati- cally investigated utilizing X-ray diffraction （XRD）, photoluminescence, phosphorescence and thermoluminescence （TL） spectra. The phosphors emitted blue light that was related to the emission of E~＋ due to 5d-4f transition. Bright blue long-lasting phosphorescence （LLP） could be observed after the excitation source was switched off. For the optimized sample, the blue long-lasting phosphores- cence could last for nearly 4 h in the light perception of the dark-adapted human eye （0.32 mcd/m2）. The effects of RE3＋ ions on phosphorescence properties of the phosphors were studied, and the results showed that the co-doping of RE^3＋ ions greatly enhanced the intensity of the peak around 315 K which was related to the long lasting phosphorescence of the phosphors at room temperature and consequently improved the performance of the blue phosphorescence such as intensity and persistent time.