用Ti—Cu—Ni，Ti-Cr-Zr钎料在TIG电弧加热条件对TA2和Ti—6Al—4V钛合金进行钎焊。结果表明：用Ti—Cu—Ni钎料钎焊TA2和Ti—6Al—4V钛合金的搭接接头强度分别是418．3MPa和439．6MPa；用Ti—Cr—Zr钎料钎焊TA2和Ti—6Al—4V钛合金的搭接接头强度分别是575．2MPa和656．1MPa。对Ti-Cu-Ni钎料／母材界面分析认为固液异分化合物η相((Cu，Ni)Ti2)生成时呈笋状生长，嵌入钎缝对钎缝的强度提高有利。对Ti-Cr-Zr钎料／母材界面分析，认为主要是固溶体β-Ti(Cr)存在提高了钎缝强度。     

Bonding of Al2O3 ceramic and Nb using transient liquid phase brazing

The brazing of Al2O3 to Nb was achieved by the method of transient liquid phase (TLP) bonding. Ti foil and Ni-5V alloy foil were used as interlayers for the bonding. The base materials were brazed at 1423-1573 K for 1-120 min. The results show that the shear strength of the joint first increases and then decreases with increasing holding time and brazing temperature. The joint interface microstructure and elements distribution were investigated. It can be concluded that a composite structure, in which the base metals are solid solution Nb(V) and Nb(Ti) reinforced by Ni3Ti, is formed when the brazing temperature is 1473 K and holding time 15 min, and a satisfactory joint strength can be achieved. The interaction of Ti foil and Ni-5V foil leads to the formation of liquid eutectic phase with low melting point, at the same time the combination of Ti come from the interlayer with O atoms from Al2O3 results in the bonding of Al2O3 and Nb.     

面向服务的综合电子信息系统软件策略

针对SOA在综合电子信息系统中的应用,介绍了SOA的概念,分析了应用需求,研究了基于SOA的系统软件结构和主要特征;从标准化、构件化、工具化、数据模型、服务总线、治理和管理等方面提出了SOA软件发展策略;探索了SOA软件的实现方法.     

冷金属过渡加脉冲电弧增材制造4043铝合金薄壁件的组织与拉伸性能

采用冷金属过渡加脉冲(CMT+P)电弧增材制造4043铝合金薄壁件,对比了不同工艺参数下薄壁件的成形性能,研究了成形性能良好薄壁件的组织与拉伸性能,并与CMT工艺下的进行了对比。结果表明:CMT+P工艺下,当焊接速度为8 mm·s-1和送丝速度4 m·min-1时,薄壁件的成形性能最好,且其成形效果接近CMT工艺下的; CMT+P工艺下薄壁件的单层组织由焊道上层的细晶区和焊道下层的粗晶区组成,焊道间存在穿过界面生长的粗大柱状枝晶,CMT工艺下的显微组织为分布均匀的细小柱状晶; CMT+P工艺下薄壁件的拉伸性能优于CMT工艺下的; CMT+P工艺下横向和纵向拉伸试样断裂方式均为韧性断裂,横向与纵向抗拉强度各向异性百分比仅为4%,说明薄壁件的力学性能不存在各向异性。     

注射级药用小苏打制备工艺研究

简要介绍了注射级药用小苏打的生产方法,结合公司情况,进行了纯碱法制备药用小苏打的实验研究,探讨了不同因素对产品质量的影响,成功制备出符合标准的产品。依靠公司现有装置,建设药用小苏打项目具有较大优势。     

Interfacial structure and joint strengthening in arc brazed galvanized steels with copper based filler

1 Introduction Arc brazing is a brazing method that the specimens are heated by arc[1]. It is the generic terms of GMA brazing and GTA brazing[2], and has both the characteristics of brazing and welding. Compared with traditional arc fusion welding, the s…     

磁力泵在醋酸生产中的应用及故障分析

磁力泵因具有运行稳定、使用寿命长及无泄漏等优点,在石油化工生产中应用越来越广泛。本文介绍了醋酸生产中的磁力泵使用情况,分析了醋酸生产中磁力泵容易出现故障的原因及防范措施。     

新中国妆风格及形式探究

近年来，“眯眯眼”妆事件频上热搜，引起全民舆论抨击。这事件的背后既体现了国人文化自信的崛起，又反映了当前中国妆容仍存在认知偏差的现状。相较于中国妆容风格，国人对于欧美妆，日韩妆的特征更加了解，认知也更加清晰，并且深深影响着中国女性的化妆习惯。本文立足于中国传统文化的精髓，通过对历史上各个朝代妆容的分析提炼和十多年上万张面孔化妆的总结和尝试，以“自信，独立，优雅”为妆容风格，用“细长眉”，“眼下彩”和“点珠唇”为妆容形式，代表新中国妆容的标准，为中国人的文化自信撑腰，也为中国女性的妆容之美拿回定义权。     

铜和铜合金表面激光熔覆最新研究及进展

激光熔覆由于瞬间加热温度高,对工件热影响小而广泛应用于铜及其合金的表面改性。从熔覆材料体系、熔覆层质量与制备工艺、熔覆层组织与性能(主要包括耐磨性、耐电蚀性、耐腐蚀性和导电性)三方面综述了铜和铜合金表面激光熔覆的最新研究进展,指出了铜表面激光熔覆存在的主要问题是铜对激光的反射率,并对今后的研究方向进行了展望。     

送丝速度对镀锌钢激光钎焊接头性能影响研究

激光钎焊过程中有很多影响焊接接头质量的因素,如激光功率,焊接速度,离焦量等,主要研究了送丝速度对焊接接头力学性能的影响。实验结果显示:焊接接头中有Fe-Si(Cu)弥散相的析出,这些析出相呈现颗粒状,小岛状或者花瓣状分布。当送丝速度达到2.0m/min时,弥散相的分布最为密集,焊接接头的力学性能最好,并高于母材,在母材处发生断裂;当送丝速度为1.7m/min和2.3m/min时,Fe-Si(Cu)相只是零星的分布在焊接接头内,接头力学性能比母材差,拉伸实验断裂在焊缝处,断裂方式属于韧性-塑性型。