Preparation and application of pharmaceutical wastewater treatment by praseodymium doped SnO2/Ti electrocatalytic electrode

Praseodymium was selected as a promoter for SnO2/Ti electrode to improve the electrocatalytic performance by electrodeposition in pharmaceutical wastewater treatment; the micrograph and the structure were characterized by SEM and XRD. Mixture uniform design was used in the optimization of the electrolytic conditions; mathematical model was established according to the rate of wiping COD off, which revealed the relationship between the current intensity, time of electrolysis, the amount of doped Pr, and the ratio of area （SnOJTi：Al）. On the basis of the analysis of the empirical model, the optimized parameters had been obtained; the rate of wiping COD off was up to 94.9%, it decreased from 392 to 20 mg/L. Experimental results showed that the electrocatalytic performance of the electrode doped with Pr was superior for the treatment of pharmaceutical wastewater.     

Co改性PbO2/Ti电催化电极处理模拟染料废水

以脱色率为考察指标,研究了自制Co改性PbO2/Ti电催化电极处理亮绿、结晶紫和甲基橙3种模拟染料废水的最佳条件:控制电流分别为0.30、0.30、0.15 A,处理7、7、9 min,加入电解质NaCl 0.5、0.7、0.5 g。动力学实验结果表明:亮绿和甲基橙的降解过程符合一级反应动力学关系,结晶紫符合零级反应动力学关系。紫外分光光度法测试结果表明:3种染料分子在电解催化过程中生色基团被破坏,发生了降解,揭示了Co改性PbO2/Ti电催化电极降解机理。     

均匀设计法在Pr改性SnO2/Ti电催化电极处理制药厂废水中的应用

为了提高制药厂废水处理效果,采用均匀设计方法优化自制Pr改性SnO_2/Ti电催化电极处理制药厂废水的降解条件。以COD去除率为考察指标,建立了COD去除率与电流强度、时间、Pr的掺杂量、面积比(SnO_2/Ti:Al)之间的数学模型。在回归分析的基础上,筛选出降解条件的优化参数,此时废水的COD去除率达94.9%。实验结果表明,采用均匀设计法得出最佳降解条件的配方,用Pr改性SnO_2/Ti电极和装置处理制药厂废水,处理效果良好。     

3,5-二溴水杨醛缩甲硫氨基酸席夫碱镍(Ⅱ)配合物修饰碳糊电极的制备及对甲醇的电催化氧化研究

制备了3,5-二溴水杨醛缩甲硫氨基酸席夫碱镍(Ⅱ)配合物修饰碳糊电极,研究了该电极催化甲醇的电化学行为。实验结果表明,电极材料组成中电活性物质BrTMSBNi为0.06g、石墨用量为0.30g时,电极有最大的氧化峰电流值;电极反应主要受扩散控制。利用循环伏安法测定了氧化峰电流值与甲醇浓度的关系,在1.2～2.0g/L范围内线性关系良好,相关系数为0.9997,检出限为0.04g/L。加标回收实验表明,该电极测定溶液中的甲醇具有较高的准确度。     

钛-铁双阳极电絮凝法去除电镀废水中的铬(Ⅵ)

对采用钛-铁双阳极电絮凝技术去除电镀废水中铬(Ⅵ)进行了研究.以铬(Ⅵ)去除率为考察指标,利用单因素试验和正交试验,详细研究了不同阳极材料及组合方式、电流密度、电解时间、废水pH、电导率、静置时间等因素对其去除废水中铬(Ⅵ)效果的影响,经正交试验的极差分析和方差分析表明:对质量浓度为0.2 g/L的含铬(Ⅵ)模拟废水,当电流密度控制在1.5 A/dm2,电解时间为1.5 h,电解质NaCl质量浓度为1.0 g/L及废水pH=9时,铬(Ⅵ)的去除率最高,达96.57%.在此基础上应用于处理实际镀铬废水,获得了满意的结果.同时,初步探讨了钛-铁双阳极电絮凝法除铬(Ⅵ)机理,得出氧化和絮凝作用,是废水中铬(Ⅵ)被有效去除的主要原因.     

Pr改性SnO2/Ti电催化电极制备、表征及性能的研究

通过电沉积法制备SnO2/Ti电极,同时掺杂Pr对其进行改性,获得Pr改性SnO2/Ti电极.利用SEM和XRD分析方法表征了电极的形貌及结构,以制药厂废水为目标污染物,控制电流强度为0.3A,3.5h后COD由392mg/L降至20mg/L,去除率达94.9%.实验结果表明,Pr改性SnO2/Ti电极具有更好的电催化性能.