我国铸造有色合金及其特种铸造技术发展现状

结合我国在铸造有色合金领域的发展概况,从合金发展、应用和有色合金熔体技术以及特种铸造在有色合金中的应用角度,分析了五十年来我国在该领域所取得的成绩和存在的问题,以引起广大科技工作者和生产技术人员对这方面自主创新的重视,不断提高铸造有色合金的技术水平,扩大其应用领域。     

Microstructure and mechanical properties of high strength as—cast Ti—15—3 alloy

The effects of heat treatment and solidification cooling rate on the microstructure and mechanical properties of as-cast Ti-15-3 alloy prepared by induction skull melting method were investigated.Results show that the microstructure of as-cast Ti-15-3 alloy changes from the features of simplified and larger size of beta grains to finer grain size with increasing solidification cooling rate.After solution treatment and different ageing treatment,alpha phase precipitates in grains interior as well as in grain boundaries.Due to the modification of the precipitate phase,the tensile stength and elongation of the alloy are improved simultaneously.A good combination of the values of 1.406GPa of σb and 4.5% of δ was obtained,which will be satisfied the use of this kind of alloy in critical areas.     

冷坩埚熔铸技术的研究及开发现状

综述了冷坩埚技术的原理和特点、目前的研究及开发现状。冷坩埚具有无污染，可熔化高熔点金属，制备的材料组织均匀等优点。冷坩埚技术在以下领域得到广泛的研究和应用：与熔化技术相结合能高纯均匀熔炼活性金属，通过起熔材料能制备陶瓷材料；与连铸技术相结合能进行冷坩埚电磁连铸技术，提高铸锭表面质量，改善内部组织；与定向凝固和连铸技术相结合的冷坩埚定向凝固技术已成功进行钛合金的定向凝固；与多晶硅制备技术相结合能连续制备多晶硅，杂质含量少；与雾化沉积技术相结合的冷坩埚雾化沉积技术具有熔化合金种类多、适用范围广的优点。冷坩埚的自身特点决定了其必将更受重视和广阔发展前景。     

二元合金等轴枝晶生长相场模拟

在传统纯物质相场模型的基础上，对其中的体系自由能进行重新构造，得到一个紧密联系相图且综合考虑了传热、溶质扩散、界面能各向异性和界面动力学各向异性等适用于二元合金枝晶生长的新相场模型，并利用该模型结合一种能显著提高计算效率的“临界面点相场大梯度计算域控制法”，对AJ-7Si合金在初始过冷度分别为35K和50K的过冷熔体中等轴枝晶生长进行了模拟，得到许多与试验观察相符合的结果；同时在枝晶生长过程中跟踪枝晶主轴尖端，获得其尖端半径和尖端速率，发现随着凝固时间的增加，逐渐收敛，直到枝晶达到稳定生长，而且通过简化KGT模型计算的枝晶尖端的生长速率与模拟值相近。另外，就过冷度对等轴枝晶生长的影响进行了分析。     

Equivalent heat transfer coefficient at casting/Cu mould interface and temperature field simulation

1　INTRODUCTIONThesolidifiedmicrostructuresofalloysdependontheirsolidifyingprocesswhoseprimarycharacteristicsarethetemperaturedropofthesuperheatedmeltandthere leaseofthelatentheat.Sothestudyontheheattransferduringthesolidificationprocessistheessentialprobleminthesolidificationtheorystudy .Theresearchersworkingonthenumericalsimulationofthesolidificationprocessallknowthattheinterfacialheattransfercoefficientatthecasting/mouldisavariablechangingwithtime .Thusthedeterminationoftheinterfacialh…     

选区激光熔化Inconel 718合金的熔池形态与组织

通过不同扫描速度和扫描方式的选区激光熔化(SLM)技术制备了Inconel 718合金,研究了工艺参数对熔池的形态、凝固组织、晶粒大小和晶粒取向的影响。结果表明,随着扫描速度增加,熔池的深度与宽度的比值增大,曲率增大;而扫描速度为1 450mm/s时,采用单向扫描比十字交叉扫描时深宽比值更大。在熔池内,凝固组织由熔池底部的胞晶向熔池侧面的胞枝晶转变。晶粒以<001>方向择优生长,其晶粒间的取向差角以小角度(<15°)为主。当十字交叉扫描时,随着扫描速度增加,小角度取向差角的分布分数增加。当速度一定、采用十字交叉扫描时,小角度的取向差角占比为62.57%,而采用单向扫描时为47.69%。     

W对γ-TiAl基合金单向凝固组织的影响

采用电弧熔炼并直接在冷坩埚中凝固,得到了具有单向凝固特征的TiAl合金纽扣锭,以此研究了合金元素W对单向凝固组织的影响.结果表明,W对TiAl合金单向凝固的枝晶组织有细化作用,当W含量为2.5%时,可以将凝固组织的晶粒宽度减小到200 μm,二次枝晶间距减小到50 μm.随着W含量的增加,先凝固形成的β相晶粒内部出现网络分布的富W相,并最终转变为B2相.Ti-46Al合金中加入W元素后,片层团尺寸及片层厚度减小.     

TiAl基合金定向凝固中领先相的确定及影响因素

TiAl基合金因其优异的高温性能及较低的密度成为近年的研究热点,室温塑性是其走向工程化应用最主要的障碍。通过定向凝固技术控制TiAl基合金片层取向与生长方向平行时,可有效提高其综合力学性能,领先相的选择及生长取向的控制是TiAl基合金片层取向控制的关键因素。本文综述了定向凝固TiAl合金领先相的类型及生长取向的几种确定方法,及其生长取向的影响因素,最后总结了领先相生长取向控制的研究方向,对制备定向凝固TiAl基合金叶片具有重要的指导意义。     

铝合金熔体中氢溶解度的计算模型

基于Sieverts定律和多元合金组元活度系数计算模型,建立了一个计算氢在多元合金熔体中的溶解度的计算模型,该模型只需要氢在纯金属熔体中的溶解度参数,为预测多元合金熔体中氢含量提供了有效的途径.以此计算了氢在多种铝合金熔体中的溶解度随温度变化的情况,计算结果与实验值吻合较好.     

电磁铸造移动磁场发生器磁场分布规律及其作用分析

研究了用于电磁铸造的移动磁场发生器上磁场强度变化及其对金属产生的力的作用.结果表明,磁感应强度分量By和Bz的变化趋势相反.By的存在使金属流动充型过程中产生表面凹坑型缺陷,Bz明显提高金属液流动速度,而在提高充型能力的同时,会使金属液流前端截面减小而形成反向充填,引发冷隔缺陷.铁磁性上模可以减弱By、增强Bz,提高表面质量.金属在移动磁场中受到的力与其投影面积有关,而且存在临界投影面积,小于该临界值后,电磁力不足以拉动该金属.