Peroxide crosslinking of rigid poly(vinyl chloride)

Peroxide crosslinking of unplasticized poly(vinyl chloride) with trimethylolpropane trimethacrylate was investigated. Formulations used in this work contained a nontoxic lead‐free stabilizer and showed good color and heat stability. The samples were examined by differential scanning calorimetry, and their tensile properties were measured at room temperature and at 130°C. Gel content or tetrahydrofuran‐insoluble material was measured as an indication of crosslinking. It was shown that premature crosslinking could be avoided during processing and that 190°C was the optimum processing temperature for maximum gel content. The residual unsaturation was monitored by using FTIR spectroscopy. J. VINYL ADDIT. TECHNOL., 2008. © 2008 Society of Plastics Engineers     

Polymer aqueous solutions as quenching media. II. Ethylene oxide–propylene oxide copolymers

The cooling power of aqueous solutions of ethylene oxide-propylene oxide copolymers are studied with a silver standard sample by using two apparatuses quench with injection and quench with agitation. For temperature T>400°C, the viscosity plays the predominant role; for T<400°C, the cooling is controlled by the polymer precipitation and the cooling rate decreases by lowering the cloud point of the polymer solution. This work demonstrates the possibility of adjusting the cooling curves by taking into account the thermodynamical properties of the polymer.     

Homopolymer Nanolithography

Future progress in nanoscience and nanotechnology necessitates further development of versatile, labor‐, and cost‐efficient surface patterning strategies. A new approach to nanopatterning is reported, which utilizes surface segregation of a smooth layer of an end‐grafted homopolymer in a poor solvent. The variation in polymer grafting density yields a range of surface nanostructures, including randomly organized pinned spherical micelles, worm‐like structures, networks, and porous films. The capability to use the polymer patterns for site‐specific deposition of small molecules, polymers, or nanoparticles is shown. This versatile strategy enables patterning of curved surfaces with direct access to the substrate and no need in changing polymer composition to realize different surface patterns.