Sug-Woo Jung Suk-Joong L. Kang Sunghak Lee Eun-Pyokim Joon-Woong Noh Woon-Hyung Baek 《Metallurgical and Materials Transactions A》2002,33(4):1213-1219
A carburization technique using a Cr powder layer has been developed to control the diffusion depth of carbon in W-Ni-Fe heavy
alloys. The aged heavy alloy samples were covered with a Cr powder layer of about 1-mm thickness and then packed with carbon
black powder. The packed samples were heat-treated at 1150 °C for 10 minutes in H2 and then for 50 minutes in N2. The carburization treatment resulted in the formation of Cr7C3 and Fe3W3C around the tungsten grains from the sample surface with a thickness of 40 to 50 μm. This carburized layer was much thinner than that formed without a Cr powder layer under the same experimental conditions.
With the surface carburization, the surface hardness increased by ∼75 pct, from 508 to 888 VHN, and the impact energy decreased
by ∼31 pct, from 123 to 85 J. After the carburization treatment, the main fracture behavior in a dynamic torsional test changed
from smearing of the matrix to cleavage of the tungsten grains. A high-speed impact test showed that the surface carburization
of penetrators induced the formation of many cracks around the penetrator surface, enhanced the self-sharpening, and improved
the penetration performance. It appears that the developed technique provides an easy method of carburization without serious
deterioration of the toughness of the material. 相似文献