In the course of the cryoplant modernization, a control network will be set up in order to facilitate the control, the supervision, the centralized data acquisition and the alarm handling of the cryogenic system for HT-TU tokamak. The paper introduces the preliminary design of control network based on the Controller Link Network for HT-7U tokamak cryogenic system. The multi-layer structure mentioned in the paper is the mainstream of automatic control. The control philosophy, the structure of the network and the components for control are also presented.     

ZrO_2含量对镁锆不烧砖性能的影响

以w(MgO)=97%的电熔镁砂和w(ZrO2)=14.33%的预合成电熔镁锆料为原料,以酚醛树脂为结合荆,用400 t摩擦压砖机机压成型制备了w(ZrO2)分别为0、2%、4%、6%和8%的镁锆不烧砖,研究了ZrO2含量对镁锆不烧砖的常温性能、高温强度、抗热震性的影响,同时还重点研究了其抗渣性能(采用回转抗渣法,渣为碱度3.6的精炼炉渣,侵蚀温度1 650℃),并借助SEM和EDAX分析了部分抗渣后试样的显微结构.结果表明:(1)随着引入的ZrO2含量提高,镁锆不烧砖的常温力学性能总体呈上升趋势,w(zrO2)由0增加到8%时,1 600℃3 h处理后镁锆不烧砖的高温抗折强度(1 500℃下)从0.5 MPa提高到2 MPa.(2)引入的ZrO2改善了不烧砖的抗热震性,w(ZrO2)由0增加到8%时,试样经1 000℃风冷1次后的抗折强度保持率由20%提高至70%以上.(3)ZrO2的引入可以改善镁质材料的抗渣渗透性,尤其是电熔钱锆合成料以细粉形式引入时效果更佳;但ZrO2的引入又对抗渣侵蚀性有所不利,尤其是引入w(ZrO2)达6%～8%时,会造成主晶相方镁石和c-ZrO2,的热膨胀不匹配效应加剧,使材料产生较大裂纹甚至剥落,导致抗渣渗透性随之恶化.当引入的w(ZrO2,)≤4%时,材料以侵蚀损毁为主,蚀损深度约12 mm;而w(ZrO2)>4%时,以渗透和剥落损毁为主,最高蚀损深度达到30 mm左右.因此,综合考虑,镁锆不烧砖中ZrO2,含量以4%(质量分数)为宜.     

Preliminary Design of Control Network for HT-7U Tokamak Cryogenic System

In the course of the cryoplant modernization,a control network will be set up inorder to facilitate the control,the supervision,the centralized data acquisition and the alarmhandling of the cryogenic system for HT-7U tokamak.The paper introduces the preliminarydesign of control network based on the Controller Link Network for HT-7U tokamak cryogenic