Effect of Rare Earth Element Cerium on Mechanical Properties and Morphology of TiN Coating Prepared by Arc Ion Plating

TiN coatings were deposited on polished substrates of W18Cr4V high speed steel by means of vacuum arc ion plating. The effect of cerium on adhesion between TiN coating and substrate was studied. The microstructures and composition of TiN coatings were also investigated by means of scanning electron microscope (SEM), Auger electron spectroscopy (AES), and X-ray diffraction (XRD) technique. It was found that cerium is an effective modifying agent and the addition of suitable amount of cerium to TiN coatings can produce relatively excellent properties such as micro-hardness, wear resistance, oxidation resistance and porosity. The experimental results show that the added cerium in TiN coatings makesa contribution to form the preferred direction along with a (111 ) or (222) close packed face, which may be one of the reasons that improves some properties mentioned above.     

用于强流离子注入的气体—金属弧离子注入机

本文介绍了新型的TITAN离子注入系统的结构、特点及工作原理。TITAN源设计思想新颖,是DENNING源与MEVVA源的有机结合,它能给出气体离子,也能给出金属和气体的混合离子,在金属材料改性方面具有潜在的应用前景。笔者对该系统的技术特性及优缺点进行了评述。     

离子束辅助沉积对TiAlSiN薄膜性能的影响

分别利用真空电弧沉积技术与等离子体辅助真空电弧沉积技术在不锈钢片、高速钢片和单晶硅片上沉积TiAlSiN多元薄膜，通过X射线衍射和扫描电镜对采用两种方法制备的薄膜物相及表面形貌进行了分析比较，测定了高速钢片上薄膜的显微硬度，进行了耐磨性实验。结果表明，采用离子束辅助沉积制备的薄膜，有（200）面的择优取向，薄膜的表面形貌得到改善，硬度和耐磨性提高。     

用不同锰源高温固相法制备LiMnPO4/C

以MnO2、Mn(Ac)2和MnCO3为锰源,通过高温固相法制备纯相LiMnPO4/C正极材料,进行XRD、SEM分析和充放电、循环伏安测试。采用不同锰源制备的样品,XRD衍射峰均与LiMnPO4的标准图谱一致,无其他杂质峰;但颗粒形貌存在较大的差别。以Mn(Ac)2为锰源的材料具有较好的循环稳定性和相对较高的可逆容量,以0.2C在2.7~4.5 V充放电,首次充、放电比容量分别为113.1 mAh/g和95.7 mAh/g,库仑效率为84.6%,第25次循环的放电比容量为108.9 mAh/g。     

碳改性SnSbCu_(0.5)/M-MCMB/C负极材料

对中间相炭微球(MCMB)进行改性,以改性MCMB(M-MCMB)为基体、柠檬酸为碳源,由化学还原法、球磨法及热裂解工艺制得Sn Sb Cu0.5/M-MCMB/C复合材料。用XRD、SEM及恒流充放电等方法研究样品、纯Sn Sb Cu0.5合金和Sn Sb Cu0.5/M-MCMB负极材料。Sn Sb Cu0.5/M-MCMB/C复合材料可缓解纯Sn Sb Cu0.5合金的体积膨胀效应,提高循环稳定性。以100 m A/g在0.01~2.00 V循环,首次放电比容量为648.51 m Ah/g,库仑效率为74.55%,第80次循环的容量保持率为80.26%。     

Li_(1+x)Ni_(0.166)Co_(0.166)Mn_(0.667)O_(2.175+x/2)正极材料的喷雾干燥法合成及电化学性能

采用喷雾干燥法制备锂离子电池用层状富锂锰基正极材料Li(1+x)Ni0.166Co0.166Mn0.667O(2.175+x/2)(x=0.3,0.4,0.5,0.6),通过X射线衍射(XRD)、扫描电子显微镜(SEM)、等离子体发射光谱(ICP)、热重-差热分析(TG-DSC)、比表面积、粒度分布和恒流充放电等测试手段对材料的结构、形貌及电化学性能进行表征。结果表明:所制得的富锂锰基正极材料为三方层状结构(mR3)的LiNi1/3Mn1/3Co1/3O2和单斜层状结构(C2/m)的Li2MnO3组成的固溶体,且具有多孔球形形貌。当x=0.4时,材料具有最优的电化学性能。在2.0~4.8 V电压范围内,25 mA/g电流密度下材料的首次放电比容量高达277.5 mA·h/g,20周循环后容量保持率达95.3%,500 mA/g电流密度下放电比容量仍达192.5 mA·h/g。     

真空退火对Sn负极材料结构与循环性能的影响

用SEM、XRD、ICP、恒电流充放电方法对真空退火前后磁控溅射制备的锂离子电池用Sn负极薄膜材料的形貌、结构及循环性能进行研究.结果表明,经过200 ℃×8 h真空退火后,薄膜颗粒细化且均匀分布,薄膜中还出现了Cu6Sn5和Cu3Sn合金相的特征峰,改善了膜基结合力.相对于纯Sn电极,热处理后样品的首次放电容量和首次库仑效率均略有下降,分别为709 mAh/g和67%;从第2次到30次循环的容量保持率为87%,库仑效率维持在94% ～99%,均优于纯Sn电极.     

气体爆炸喷涂技术及其应用

气体爆炸喷涂是热喷涂领域的先进技术。世界上主要是美国和前苏联发展有成熟的爆炸喷涂设备和并已实际用于生产。本文论述了爆炸涂设备的组成，爆炸喷涂过程，爆炸喷涂技术特点以及广泛的应用领域。