有机-无机压电材料TMCM-MnCl3的研究

有机-无机压电材料是一种分子铁电体，具有柔性、结构灵活、易成膜、全液相合成及环保节能等优点，可满足新一代薄膜器件及可穿戴设备的需求。该文以三甲基卤代甲基铵(TMXM, X=F, Cl, Br)为有机部分，MnCl₂为无机部分，通过溶液蒸发法制备了具有钙钛矿分子结构的有机-无机压电材料三甲基氯三氯化锰(TMCM-MnCl₃)，并对其分子结构组成、压电、热学、声学及铁电性进行表征。结果表明，TMCM-MnCl₃的压电常数为106 pC/N，居里温度为130 ℃，声阻抗值约为16.5 MRayl，低于压电陶瓷PZT-4(大于33 MRayl)，具有广阔的应用前景。     

High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

Eco-friendly and degradable red phosphorus nanoparticles for rapid microbial sterilization under visible light

Pathogens pose a serious challenge to environmental sanitation and a threat to public health.The frequent use of chemicals for sterilization in recent years has not only caused secondary damage to the environment but also increased pathogen resistance to drugs,which further threatens public health.To address this issue,the use of non-chemical antibacterial means has become a new trend for environmental disinfection.In this study,we developed red phosphorus nanoparticles(RPNPs),a safe and degradable photosensitive material with good photocatalytic and photothermal properties.The red phosphorus nanoparticles were prepared using a template method and ultrasonication.Under the irradiation of simulated sunlight for 20 min,the RPNPs exhibited an efficiency of 99.98%in killing Staphylococcus aureus due to their excellent photocatalytic and photothermal abilities.Transmission electron microscopy and ultraviolet–visible spectroscopy revealed that the RPNPs exhibited degradability within eight weeks.Both the RPNPs and their degradation products were nontoxic to fibroblast cells.Therefore,such RPNPs are expected to be used as a new type of low-cost,efficient,degradable,biocompatible,and eco-friendly photosensitive material for environmental disinfection.     

堰筑湖底隧道围护结构选型分析——以竺山湖隧道为例

隧道基坑围护方案的选择是隧道建设中的一个关键环节,文章结合工程实例,根据隧道所处的位置环境、开挖深度以及地质条件等,对几种围护方案的选择进行了分析论述,同时阐述了围护结构构造设计及计算结论,对类似工程的实施具有一定的参考意义.     

掺钪AlN材料特性及HBAR器件性能研究

该文基于掺钪AlN薄膜制备了高次谐波体声波谐振器(HBAR),研究了钪(Sc)掺杂浓度对AlN压电薄膜材料特性及器件性能的影响。研究表明,当掺入Sc的摩尔分数从0增加到25%时,压电应力系数e₃₃增加、刚度 下降,导致Al₁-_xSc_xN压电薄膜的机电耦合系数 从5.6%提升至15.8%,从而使HBAR器件的有效机电耦合系数 提升了3倍。同时,当Sc掺杂摩尔分数达25%时,Al₁-_xSc_xN(x为Sc掺杂摩尔分数)压电薄膜的声速下降13%,声学损耗提高,导致HBAR器件的谐振频率和品质因数降低。     

带热电偶数显温度巡回检测仪校准方法的研究

本文通过对巡检仪进行示值稳定性、重复性的试验,探讨热电偶的选择与巡检仪示值之间的关系,以确定校准方法,指导使其有效溯源.     

生态封场技术在非正规垃圾堆放场治理中的应用

本文通过对各项治理技术比选,提出了生态封场技术在非正规垃圾堆放场治理中的应用,并结合实际案例给出了详细治理方案.     

Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.