储氢合金表面处理的研究

用快淬法制得晶粒尺寸为20～50 nm的富铈稀土储氢合金,其0.4C放电比容量达到310 mAh/g.经表面改性处理后,合金的活化性能、循环性能、大电流放电性能和1.2 V放电电压平台等电化学性能都得到提高.经4 h表面改性处理后,在1C放电条件下,合金只需2次活化,就能达到最大比容量300.2 mAh/g;经18次循环后,合金的放电比容量仍保持在297 mAh/g,其放电效率达到93.80%.1C,2C和3C放电能力分别达到97.84%,93.27%和92.40%.     

Research on preparation of layered LiNi_(0.5)Mn_(0.5)O_2

1IntroductionLithium secondary batteries have been rapidly developed because of their well performances such ashigh voltage,high specific energy,high capacity and light weight since appeared at last century.It waspromising to be the main power source of electric vehicles and electric tools.The more practical interestcathode materialsincluded mainlylithiumcobalt oxide,lithiumnickel oxide andlithium manganese oxideetal.At present,lithiumcobalt oxygen was the most widely usedin comerical,andits s…     

无镨钕La1-x Cex(NiCoMnAlCuSnFeB)5.1贮氢合金的电化学特性

采用真空电弧熔炼-热处理制备了一系列无镨钕稀土基AB5型贮氢合金,研究了Ce掺杂量对贮氢合金La1-xCex(NiCoMnAlCuSnFeB)5.1的相结构、吸放氢PCT曲线和电化学性能的影响.XRD分析结果表明,该系列贮氢合金均为CaCu5型六方结构,晶胞体积随Ce含量的增加而减小.由合金的吸放氢PCT曲线可知,随Ce含量的增加,合金的吸氢平台压升高而吸氢量减少.对合金的电化学性能测试结果表明,随Ce含量的增加,合金的电化学容量减小而电化学稳定性则有所改善.在La1-xCex (NiCoMnAlCuSnFeB)5.1贮氢合金中,当Ce含量(原子分数)为0.15～0.23时,合金在0.2C的放电比容量为349.5～333.1mA·h/g,高倍率放电性能HRD7C为75.53,～73.21,,当合金电极的容量保持率Sn为80,时,合金电极的充放电循环次数为269～365次.     

纳米晶稀土贮氢合金的研究

用双辊快淬工艺制备了纳米晶AB5型富镧稀土贮氢合金。对热处理后的合金进行X射线衍射和扫描电镜SEM分析，并测试合金的吸放氢等温平衡曲线PCT。结果表明，处理的合金晶粒尺寸〈50nm，该合金具有良好的吸放氢动力学性能。     

锂离子电池阴极材料LiCoO2制备方法的研究进展

详述了固相合成法和液相合成法制备LiCoO2的工艺,并指出了这两类方法各自存在的问题;在分析影响材料电化学性能因素的基础上,提出今后的研究方向.     

氮化钒形成机制中热动力学及活化能研究

研究以钒酸铵和碳粉为原料,经过混料、研磨、压制成型后放入反应炉中还原氮化制备氮化钒。对还原氮化的过程进行热动力学分析,得到氮化钒形成机制中物料的比表面积和温度、压强等外部条件对反应过程的反应速率及活化能的影响。并建立反应速率常数与温度之间的数学模型。     

靶材用氧化铌粉体的制备及表征北大核心

采用酸洗除杂、氢氟酸溶解、氨水沉淀、水洗过滤、喷雾干燥,然后在氢气气氛中高温煅烧的还原脱氧工艺,制备出可用于制备靶材的铌氧化物粉体,通过差热分析、XRD、TEM、粒度分布测试等方法对产物脱水、脱氧情况,物相、颗粒大小及微观形貌进行研究,同时对粉体纯度、振实密度及氧含量进行测试。结果表明:产品颗粒呈球形,流动性好,纯度达到99.96%(质量分数)以上,振实密度1.88 g/cm^3,失氧量为粉末中总氧含量(质量)的3.3%,达到靶材原料质量要求,证明了该工艺的可行性。     

Study on LiCoO_2 cathode materials with well performance for lithium ion batteries

1IntroductionLiCoO2is one of key commercial cathode materials usedfor lithiumsecondary batteries at present.It isal most synthesized by traditional high temperature solid-state reaction method.Due to not only requiringgrinding and blending for a longer ti me,but also demanding higher caclination temperature and longerti mes,it is difficult to control the compositions,structure and partical size distribution of the resultingpowder during the preparation process,so theidentity of electrochemica…     

3～5GHz超宽带并联负反馈低噪声放大器的设计

设计了一种用于3～5GHz MB-OFDM超宽带接收机射频前端的CMOS低噪声放大器(LNA).分析了RC电阻反馈式低噪声放大器的结构,针对其存在的噪声大、增益低等问题,提出一种改进电路结构;增加了一个源极电感,以克服上述电路的不足,采用TSMC 0.18μm RFCMOS工艺,进行设计和仿真.仿真结果表明:改进结构在...     

纳米晶稀土贮氢合金的热处理研究

用快淬法制备的纳米晶稀土贮氢合金活化速度快,比容量高,但充放电循环稳定性差。通过TG—DSC分析,确定了合金热处理条件,经950℃退火2h,再在800℃退火1h两阶段热处理后,合金的充放电循环稳定性明显改善.用2C充放电300次循环后,其比容量由初始的305.1mA·h/g下降至269.9mA·h/g,比容量下降了11.5％。X射线衍射分析结果表明,热处理后合金晶粒尺寸由40nm增大至50nm。该技术指标已达到电池生产厂家对合金粉的技术要求。