Comparison of activities in selective catalytic reduction of NOx by C3H8 over Co/MFI, Fe/MFI, and H/MFI zeolite catalysts

The Co/MFI(SiO₂/Al₂O₃ = 30) were prepared by a precipitation method with NaOCl in alkali solutions exhibited high activities to N₂ at 250 °C for the selective catalytic reduction (SCR) of NO_x. These catalysts showed two UV–vis bands at 700 and 400 nm, indicating the presence of octahedral Co(III) as well as tetrahedral Co(II). The high SCR activity over such Co(III, II)/MFI(30) seems to come from Co(III)---O moieties. The Co(II)MFI(30) catalysts prepared from Co(II)Cl₂ exhibited low SCR activities due to the presence of tetrahedral Co(II) ions in MFI. Less CO formation occurred over Co/MFI catalysts. The Fe/MFI(30) catalyst exhibited high activity due to the presence of some Fe---O species in MFI but more amount of CO were produced during SCR. H/MFI(30) catalyst exhibited a good SCR activity. However, more amount of carbonaceous deposits were produced on it. The correlation between acid concentration and SCR activity was discussed over H/MFIs.     

Prediction of spectral reflectance factor distribution of automotive paint finishes

It is necessary to determine the accurate reflectance of painted surfaces for the review of paint finishes by computer graphics (CG) before actual painting of the exterior color of automobiles, and for quality control during production and inspection processes. We have optimized a method for measuring reflectance by using a statistical technique. We have found that the reflectance of a painted surface is best measured at an incident angle of 60° and at five aspecular angles of 10°, 18°, 28°, 40°, and 90°. Our method makes it possible to accurately reproduce reflection characteristics of paint finishes containing special flake pigments, such as pearl mica. Also it was proved that our method can apply not only to solid and metallic coatings but to all painted surfaces. © 2005 Wiley Periodicals, Inc. Col Res Appl, 30, 275–282, 2005; Published online in Wiley InterScience (www.interscience.wiley.com). DOI 10.1002/col.20125     

New approach to environmentally benign epoxidation: the solid-phase-system using urea–H2O2 and recyclable dodecatungstate on apatite

On the basis of new concept using a solid disperse phase we have developed an efficient catalytic solid-phase-system for epoxidations of alkenes using urea–hydrogen peroxide (urea–H₂O₂) complex and cetylpyridinium dodecatungstate ((CetylPy)₁₀[H₂W₁₂O₄₂]) catalyst on fluorapatite (FAp). The recovered solid catalyst phase was reused to keep the catalytic activity after several times. In the conceptual idea it is a key point that in situ solid-phase-activation of the catalyst with urea–H₂O₂ proceeds to form microcrystals of the active species dispersed on the solid phase. The dispersion of the catalyst on FAp in the case of tungstic acid (H₂WO₄) was suggested by EPMA analysis. We proposed the peroxo type of species keeping the parent polyoxometalate framework as novel active species from FT-IR spectroscopic studies. FAp phase plays important roles of dispersing the active species on its surface to have high catalytic activity and of stabilizing the active species to lead to high reusability.     

Phenol novolac/poly(4- hydroxyphenylmaleimide) blend hardeners for DGEBA-type epoxy resin

Phenol novolac/poly (4-hydroxyphenylmaleimide) (PHPMI) blends were used as an epoxy resin hardener. The curing behavior of the above system and the thermal and mechanical properties of the cured epoxy resin were studied. It was not necessary to use a curing accelerator for this system, because PHPMI caused acceleration of the curing reaction. The curing mechanism of this system was investigated by using model compounds. Test pieces from the neat resins and the glass fiber reinforced resins were evaluated in terms of thermal and mechanical properties, respectively. It was found that heat resistance and mechanical properties were improved by increasing the amount of PHPMI in the hardener.     

Preparation and photoconduction of rapidly quenched films in the Bi2O31bM2O5 system (M=V,Nb and Ta)

The Bi₂O₃1bM₂O₅ films (M=V, Nb and Ta) were prepared by a rapid quenching technique using a twin-roller type equipment. Quenched film of pure Bi₂O₃ partially precipitated a tetragonal phase which differs from well-known β-Bi₂O₃ in structure. In every (Bi₂O₃)_0.975 (M₂O₅)_0.025 composition (2.5% M₂O₅), the tetragonal phase was obtained as single phase, and the tetragonality became greater than that of the pure Bi₂O₃. Beyond this composition, the tetragonality decreased to form δ-phase with a fcc structure with increasing the M₂O₅ content. The lowest V₂O₅ content forming a δ-phase was 5%, while a slight tetragonality still remained in the samples containing 10% Nb₂O₅ and 10% Ta₂O₅, respectively. From the measurement of the photoconductivities of the quenched films, it was proved that a photoconduction appeared in the tetragonal phase while no photoconductivity was observed in the cubic phase. The characteristic of the photoconduction was that a remarkable decrease in the resistivity was observed when a light of ca. 500 nm in wave length was irradiated on the films.     

Gel chromism and anomalous luminescence in poly(3-alkylthiophene)

The absorption spectrum of poly(3-alkylthiophene) gel changes drastically in association with a volume instability upon changing the solvent composition and also the temperature. In the expanded state in chloroform and at high temperature, the photoluminescence is much enhanced compared with the shrunken state in ethanol and at low temperature. This gel chromism and anomalous luminescence are discussed in terms of the change of effective conjugation length induced by the steric hindrance and the dynamics of the photoexcited species.     

The oxidation properties of fourth generation single-crystal nickel-based superalloys

The fourth-generation nickel-based single-crystal superalloys, which contain large amounts of refractory metals for strengthening and platinum group metals for topologically close-packed phase prevention, show excellent high-temperature strength. However, these alloying elements seem to decrease high-temperature oxidation resistance. In this study, nickel-based superalloys with various amounts of tantalum, rhenium, and ruthenium were examined in isothermal and cyclic exposures at 1,100°C to investigate the effect on the oxide growth rate and resistance to scale spallation. Ruthenium and rhenium were found to degrade the oxidation resistance by the vaporization of their oxide. Tantalum-rich oxide in the spinel layer acts to stabilize ruthenium and rhenium oxide in the scale. The addition of hafnium and yttrium is effective in improving the oxidation resistance of ruthenium-containing nickel-based superalloys.     

Some experimental findings in compression-after-impact (CAI) tests of CF/PEEK (APC-2) and conventional CF/epoxy flat plates

Compression-after-impact (CAI) tests have been conducted for quasi-isotropic thick plates with 48 plies by using the NASA method and on plates with 32 plies by using the SACMA method. Specimens are made of CF/PEEK (APC-2) and conventional CF/epoxy for the NASA plates and CF/epoxy for the SACMA plates. In the NASA CAI tests, the sequence of delamination buckling and its propagation is clearly revealed through various experimental techniques. One major technique is moiré topography, and the other is thermo-mechanical stress analysis with a high-accuracy infrared sensor. The arrest of delamination propagation just before catastrophic failure due to high fracture toughness is clearly captured by the moiré camera. This behavior provides good CAI values of CF/PEEK. The initial buckling properties of the delaminated region by the impact are then extensively discussed. Numerical predictions of initial buckling stress have been obtained by modelled geometry of the delaminated region simplified from its precise structure clarified by ultrasonic C-scanning. They agree fairly well with the experimental results. The in-plane stress distribution in the delaminated region before initial buckling is measured by an infrared stress graphic system. This compared favorably with finite element predictions. Two types of symmetric buckling modes with respect to the central plate surface, twin and single peak ones, are experimentally captured.     

An investigation of induced voltages to an underground gas pipeline from an overhead transmission line

This paper investigates induced voltage characteristics from an overhead transmission line by applying a method of modeling of induced voltages proposed by the authors. EMTP simulation results obtained by the modeling method agree with analytical results obtained from a well‐known formula. The induced voltages are significantly dependent on the configuration of the overhead line. A horizontal line induces the largest voltage in a gas pipeline, and the voltage induced by a vertical twin‐circuit line is about 20% smaller than that induced by a vertical single‐circuit line. The method is applied to a real pipeline system and the simulation results show reasonable agreement with field test results. © 2008 Wiley Periodicals, Inc. Electr Eng Jpn, 164(1): 43–51, 2008; Published online in Wiley InterScience ( www.interscience.wiley.com ). DOI 10.1002/eej.20465