Preparation of a Near-Infrared Ray Absorption Film from N-Phenylthiocarbamoyl Chitosan Derivative

We recently observed that the decanoylation of N-phenylthiocarbamoyl chitosan (2) with a mixture of decanoic anhydride and pyridine at 60 °C for 24 h afforded N,N-(decanoyl)phenythiocarbamoyl-/2-isothiocynato chitosan decanoate (3b) rather than the expected product N,N-(decanoyl)phenylthiocarbamoyl chitosan decanoate (3a). This result suggested that some of the N,N-(decanoyl)phenylthiocarmbamoyl groups had been converted to isothiocyanate groups during the decanoylation process. The subsequent reaction of compound 3b with aniline gave N,N-(decanoyl)phenylthiocarbamoyl/N-phenylthiocarbamoyl chitosan decanoate (4) in high yield. A solution of compound 4 in CHCl₃ was then added to a solution of copper decanoate (5) in the same solvent, and the resulting mixture was cast onto a glass plate to give a cast film. The film was annealed at 200 °C in an oven to give a greenish film, which showed good near-infrared absorption characteristic in the range of 800–2200 nm.     

Vapor absorption by LiBr aqueous solution in vertical smooth tubes

Heat and mass transfer in a falling film vertical in-tube absorber was studied experimentally with LiBr aqueous solution. The presented results include the effect of solution flow rate, solution subcooling and cooling water temperature on the absorption in a smooth copper tube 16.05 mm I.D. and 400 mm long. The experimental data in the previous report for a 1200-mm-long tube was also re-examined and compared. It was demonstrated by the observation of the flow in the tube that the break down of the liquid film into rivulets leads to deterioration of heat and mass transfer at lower film Reynolds number or in longer tubes. An attempt to evaluate physically acceptable heat and mass transfer coefficients that are defined with estimated temperature and concentration at the vapor–liquid interface was also presented.     

Glycoconjugated polymer 6. Synthesis of poly[styrene-<Emphasis Type="Italic">block</Emphasis>-(styrene-<Emphasis Type="Italic">graft</Emphasis>-amylose)] via potato phosphorylase-catalyzed polymerization

Summary The potato phosphorylase-catalyzed polymerization of α-D-glucose-1-phosphate (G-1-P) onto poly[styrene-block-(4-vinylbenzyl maltohexaoside)] (1) was performed at the molar ratios of [G-l-P]₀ and [maltohexaose]₀ of 35, 80, and 250. The product was found to be soluble in dimethyl sulfoxide, which was a good solvent for amylose, and showed the complex-formation with iodine, indicating that the product was assignable to poly[styrene-block-(styrene-graft-amylose)] (2). The quantitative analysis of the liberated phosphoric acid gave the average degree of polymerization o f the glucose unit (n) as 27, 5 1, and 180 for 2-I, 2-II, and 2-III, respectively. Received: 29 November 2002/Accepted: 22 December 2002 Correspondence to Toyoji Kakuchi     

Relation between encoder and syndrome former variables and symbol reliability estimation using a syndrome trellis

We derive a linear correspondence between the variables of an encoder and those of a corresponding syndrome former. Using the derived correspondence, we show that the log-likelihood ratio of an information bit conditioned on a received sequence can be equally calculated using the syndrome trellis. It is shown that the proposed method also applies to recursive systematic convolutional codes which are typical constituent codes for turbo codes. Moreover, we show that soft-in syndrome decoding considering a priori probabilities of information bits is possible in the same way as for Viterbi decoding based on the code trellis. Hence, the proposed method can be applied to iterative decoding such as turbo decoding. We also show that the proposed method is effective for high-rate codes by making use of trellis modification.     

Changes in the gaseous H2S barrier properties of damaged silicate coated nylon 6 films

The damage imposed on SiO _x deposited nylon 6 films as a result of abrasion with a cotton cloth and Gelboflex testing was examined by evaluating the rate at which copper plates, which were enveloped by the damaged films, were corroded by H₂S. Abrasion with a cotton cloth caused some micro-cracking of the SiO _x layer and the permeation rate of H₂S approached that of the uncoated nylon 6 film. Damage to the SiO _x layer by twisting and crushing progressed gradually with the number of Gelboflex test cycles and correspondingly the corrosion rate of the copper plates increased. Comparison of the corrosion rates of the copper plates kept in the pouches made of various commercial films with those obtained for the damaged SiO _x deposited nylon 6 films showed a clear relationship between the H₂ permeation rate of the films and the corrosion rate of the copper plates by H₂S.     

Gap modulation in MCu[Q1−xQ′x]F (M=Ba, Sr; Q, Q′=S, Se, Te) and related materials

BaCuQF (Q=S, Se, Te) materials exhibit band gaps that allow transmission of much of the visible spectrum. BaCuSF is transparent in thin-film form with a band gap of 3.1 eV. Band gap estimates for powders of the solid solution series BaCuS_1−xSe_xF were obtained from wavelength-dependent diffuse-reflectance measurements using an integrating sphere. The band gap can be tuned by the substitution of Se for S to 2.9 eV for BaCuSeF. The decrease scales almost linearly with the increase in the volume of the tetragonal unit cell, which is determined primarily by the expansion of the a lattice parameter; the overall volume increase is 7.0% from x=0 to 1. Further reduction of the band gap is observed in BaCuSe_1−xTe_xF solid solutions, where a unit cell volume increase of 5.5% produces a band gap of 2.7 eV in BaCuSe_0.5Te_0.5F. Powders and films of BaCuSF exhibit strong red luminescence under ultraviolet excitation, which is suppressed by K doping. Additional tuning of band gap and electrical properties (the materials are p-type conductors) can be achieved by replacing Ba with Sr.     

Breakdown characteristics of oil and paper insulation for a very fast transient voltage

This paper describes the dielectric breakdown characteristics of oil and oil‐impregnated paper for very fast transient (VFT) voltages. Blumlein circuits generate VFT voltages of 60 and 300 ns in a pulse width that simulates disconnecting switching surges in gas‐insulated switch gears. We measured the breakdown voltages of needle‐to‐plane, plane‐to‐plane oil gaps and several pieces of paper between plane electrodes for VFT and lightning impulse voltages. The measured data were formulated in V‐t characteristics and Weibull probability distributions. The inclination n of V‐t characteristics of insulating paper is 150, which is less than n = 13.7 of the plane‐to‐plane oil gap in the VFT time range. The shape parameters of Weibull distribution obtained in this study show that the scattering of breakdown voltages of paper is much less than that of oil. © 2002 Wiley Periodicals, Inc. Electr Eng Jpn, 141(4): 16–24, 2002; Published online in Wiley InterScience ( www.interscience.wiley.com ). DOI 10.1002/eej.10043