Sintering studies of nano-crystalline zinc oxide

Sintering and grain growth of nano-crystalline undoped ZnO has been studied in detail over a wide range of temperature and holding time. Below 800 °C, sintering of over 70% theoretical density is not observed, irrespective of particle size. At 900 °C for 6 h, the nano-crystalline sample sinters to 99% of theoretical density whereas the density for as received sample is 93% of theoretical density. However, at 1300 °C or higher, the densification is found to be much faster and after a few hours becomes independent of holding time. Grain growth studies reveal a similar feature of attaining saturation over holding time. The average saturated grain size is found to be ∼1.5 and ∼2.2 μm at 800 and 900 °C, respectively, while at 1300 °C or higher, it is in between 12 and 13 μm.     

Cardiorespiratory effects of conventional and high frequency ventilation in rabbits with bilateral pneumothoraces and surfactant depleted lungs

We compared high frequency ventilation (HFV) to conventional mechanical ventilation (CMV) under normoxic and normocapnic condition in surfactant depleted rabbits with bilateral pneumothoraces. We hypothesized that lower airway pressures would be required with HFV under these conditions. We applied CMV and HFV in 8 anaesthetized rabbits with a prototype ventilator at frequencies of 30, 100, 200, and 300 cycles/min. A positive end-expiratory pressure (PEEP) just below the pressure sufficient to open the air leak from the pneumothoraces was applied at all frequencies. Airway pressures, gas exchange, heart rate, and mean arterial pressure were recorded. Peak airway pressure decreased significantly from 2.50 to 2.10 kPa when the frequency of ventilation was increased from 30 to 300 cycles/min. There were no significant changes in mean airway pressure, PaO2, arterial pH, heart rate, and mean arterial pressure when HFV was compared to CMV. In conclusion, during HFV peak airway pressures measured at the mouth were decreased. Our ability to maintain adequate gas exchange in the face of ongoing pulmonary air leaks may reflect lower alveolar pressures.     

Anhydrous esterification of myristic acid with propylene: Ion exchange resin and acid-treated clay as catalysts

Anhydrous esterification of myristic acid with propylene was carried out in the temperature range of 110–145°C and pressure from 190–195 psig in the presence of Amberlyst-15 (cation exchange resin) and Filtrol-24 (acid-treated clay) as catalysts. The product ester, isopropyl myristate finds use in cosmetic and topical medicinal preparations where good absorption through the skin is desired. Filtrol-24 is the catalyst of choice, and the recommended operating temperature is 130°C with a pressure of 190 psig.