Progressive NO2 Sensors with Rapid Alarm and Persistent Memory-Type Responses for Wide-Range Sensing Using Antimony Triselenide Nanoflakes

Antimony triselenide (Sb₂Se₃) nanoflake-based nitrogen dioxide (NO₂) sensors exhibit a progressive bifunctional gas-sensing performance, with a rapid alarm for hazardous highly concentrated gases, and an advanced memory-type function for low-concentration (<1 ppm) monitoring repeated under potentially fatal exposure. Rectangular and cuboid shaped Sb₂Se₃ nanoflakes, comprising van der Waals planes with large surface areas and covalent bond planes with small areas, can rapidly detect a wide range of NO₂ gas concentrations from 0.1 to 100 ppm. These Sb₂Se₃ nanoflakes are found to be suitable for physisorption-based gas sensing owing to their anisotropic quasi-2D crystal structure with extremely enlarged van der Waals planes, where they are humidity-insensitive and consequently exhibit an extremely stable baseline current. The Sb₂Se₃ nanoflake sensor exhibits a room-temperature/low-voltage operation, which is noticeable owing to its low energy consumption and rapid response even under a NO₂ gas flow of only 1 ppm. As a result, the Sb₂Se₃ nanoflake sensor is suitable for the development of a rapid alarm system. Furthermore, the persistent gas-sensing conductivity of the sensor with a slow decaying current can enable the development of a progressive memory-type sensor that retains the previous signal under irregular gas injection at low concentrations.     

Multiply Charged Conjugated Polyelectrolytes as a Multifunctional Interlayer for Efficient and Scalable Perovskite Solar Cells

A series of anionic conjugated polyelectrolytes (CPEs) is synthesized based on poly(fluorene-co-phenylene) by varying the side-chain ionic density from two to six per repeat units (MPS2-TMA, MPS4-TMA, and MPS6-TMA). The effect of MPS2, 4, 6-TMA as interlayers on top of a hole-extraction layer of poly(bis(4-phenyl)-2,4,6-trimethylphenylamine (PTAA) is investigated in inverted perovskite solar cells (PeSCs). Owing to the improved wettability of perovskites on hydrophobic PTAA with the CPEs, the PeSCs with CPE interlayers demonstrate a significantly enhanced device performance, with negligible device-to-device dependence relative to the reference PeSC without CPEs. By increasing the ionic density in the MPS-TMA interlayers, the wetting, interfacial defect passivation, and crystal growth of the perovskites are significantly improved without increasing the series resistance of the PeSCs. In particular, the open-circuit voltage increases from 1.06 V for the PeSC with MPS2-TMA to 1.11 V for the PeSC with MPS6-TMA. The trap densities of the PeSCs with MPS2,4,6-TMA are further analyzed using frequency-dependent capacitance measurements. Finally, a large-area (1 cm²) PeSC is successfully fabricated with MPS6-TMA, showing a power conversion efficiency of 18.38% with negligible hysteresis and a stable power output under light soaking for 60 s.     

Properties and applications of β‐glycosidase from Bacteroides thetaiotaomicron that specifically hydrolyses isoflavone glycosides

To modify the glycan part of glycosides, the gene encoding β‐glycosidase was cloned from Bacteroides thetaiotaomicron VPI‐5482. The cloned gene, bt_1780, was expressed in Escherichia coli MC1061 and the expressed enzyme was purified using Ni‐NTA affinity chromatography. The purified enzyme, BTBG, showed optimal activity at 50 °C and pH 5.5. Interestingly, this enzyme did not have any hydrolysing activity on ordinary β‐linkage–containing substrates such as xylobiose, lactose and cello‐oligosaccharide, but specifically hydrolysed isoflavone glycosides such as daidzin, genistin and glycitin. Compared to a commercial beta glucosidase, BTBG selectively hydrolysed isoflavone glycosides in soybean extract mixture solution. These results suggest that BTBG may be a specialized enzyme for the hydrolysis of glycosides and that the substrate specificity of BTBG is applicable for the bioconversion of isoflavone glycosides in the food industry.     

A robust control of robot manipulators for physical interaction: stability analysis for the interaction with unknown environments

Intelligent Service Robotics - A robust control designed for multiple degrees-of-freedom (DOF) robot manipulators performing complex tasks requiring frequent physical interaction with unknown...     

Recording of volume hologram using a beam pattern from taperedoptical fiber

A photorefractive volume hologram was recorded and probed using light diffracted from a tapered optical fiber as a reference beam. A single-mode fiber (SMF) was chemically etched and tapered to give a complicated beam pattern, and it is shown that the tapered optical fiber can be utilized to increase the storage density of the volume hologram. Spatial selectivity of the volume hologram with this method was increased by two times compared to the normal SMF referencing, which is due to the fact that the complicated beam pattern has little correlation with its shifted version     

Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Strength of Al-Zn-Mg-Cu matrix composite reinforced with SiC particles

The AA7075 alloys reinforced with SiC and without SiC particles were fabricated by a pressureless infiltration method, and then, their tensile properties and microstructures were analyzed. The spontaneous infiltration of molten metal at 800 °C for 1 hour under a nitrogen atmosphere made it possible to fabricate 7075 Al matrix composite reinforced with SiC, as well as a control 7075 Al without SiC. A significant strengthening even in the control alloy occurred due to the formation of in-situ AlN particle even without an addition of SiC particles. Composite reinforced with SiC particles exhibited higher strength values than the control alloy in all aging conditions (underaged (UA), peak-aged (PA), and overaged (OA)), as well as a solution treated condition. Spontaneous infiltration was further prompted owing to the combined effect of both Mg and Zn. This may lead to an enhancement of wetting between the molten alloy and the reinforcement. Consequently, strength improvement in a composite may be attributed to good bond strength via enhancement of wetting. The grain size of the control alloy is greatly decreased to about 2.5 μm compared to 10 μm for the commercial alloy. In addition, the grain size in the composite is further decreased to about 2 μm. These grain refinements contributed to strengthening of the control alloy and the composite.