Transmission electron microscopy (TEM) is an important analysis technique to visualize (bio)macromolecules and their assemblies, including collagen fibers. Many protocols for TEM sample preparation of collagen involve one or more washing steps to remove excess salts from the dispersion that could hamper analysis when dried on a TEM grid. Such protocols are not standardized and washing times as well as washing solvents vary from procedure to procedure, with each research group typically having their own protocol. Here, we investigate the influence of washing with water, ethanol, but also methanol and 2-propanol, for both mineralized and unmineralized collagen samples via a protocol based on centrifugation. Washing with water maintains the hydrated collagen structure and the characteristic banding pattern can be clearly observed. Conversely, washing with ethanol results in dehydration of the fibrils, often leading to aggregation of the fibers and a less obvious banding pattern, already within 1 min of ethanol exposure. As we show, this process is fully reversible. Similar observations were made for methanol and propanol. Based on these results, a standardized washing protocol for collagenous samples is proposed.     

Linear correlation between pH value of stimulated beef and electrical current intensity

The aim of the present study was to determine mathematical relationships between pH changes in beef 24 h post-slaughter and changes in the intensity of electrical current flowing through bull and heifer carcasses during high-voltage electrical stimulation. The electrical stimulation was applied 40 min postmortem for 120 s. The pH values of m. longissimus thoracis et lumborum were analyzed in the function of electrical current intensity changes and its change during electrical stimulation. Mathematical linear correlations of the y = ax ± b type were demonstrated between pH values at 2, 6, and 24 h postmortem and the initial (I_i) and ultimate (I_u) electrical current intensity values, the difference between them and the initial pH values determined before electrical stimulation. High multiple correlation coefficients (R² = 0.416, α ≤ 0.001) between I_u and pH values 24 h post-slaughter enabled concluding that there is a possibility to predict a pH value of stimulated carcass with high accuracy, and thus also beef quality, based merely on the ultimate electrical current intensity values.     

The influence of volume fraction of amorphous phase on corrosion resistance of Mg67Zn 29Ca 4 alloy

The aim of this study was to investigate the structure and corrosion resistance of amorphous, amorphous‐crystalline, and crystalline Mg₆₇Zn₂₉Ca₄ alloy for biodegradable applications. This paper presents a preparation method and results of the structural characterization and corrosion resistance analysis of the material. Samples were prepared in the form of 3 mm diameter rods. The structure of the alloy was examined with the use of X‐ray diffractometry and scanning electron microscopy. The thermal properties of the samples were examined with differential scanning calorimetry (DSC). Results of DSC analysis were used to determine heat treatment temperatures, allowing to obtain different fractures of crystalline phase in the material. Corrosion resistance of heat‐treated samples was investigated by immersion tests and electrochemical measurements performed in the simulated body fluid. The X‐ray diffraction results confirmed that the prepared Mg₆₇Zn₂₉Ca₄ alloy's structure is fully amorphous. After heat treatment, samples with different fractions of amorphous phase in the structure were obtained. Immersion tests of the samples showed that the structure significantly influenced corrosion resistance in examined materials. It should be pointed out, that certain amounts of crystalline phase in amorphous matrix can greatly improve the corrosion resistance of Mg₆₇Zn₂₉Ca₄ alloy.     

Software assurance practices for mobile applications

Mobile software applications have to cope with a particular environment that involves small size, limited resources, high autonomy requirements, competitive business models and many other challenges. To provide development guidelines that respond to these needs, several practices have been introduced; however, it is not clear how these guidelines may contribute to solve the issues present in the mobile domain. Furthermore, the rapid evolution of the mobile ecosystem challenges many of the premises upon which the proposed practices were designed. In this paper, we present a survey of the literature on software assurance practices for mobile applications, with the objective of describing them and assessing their contribution and success. We identified, organized and reviewed a body of research that spans in three levels: software development processes, software product assurance practices, and software implementation practices. By carrying out this literature survey, we reviewed the different approaches that researchers on Software Engineering have provided to address the needs that raise in the mobile software development arena. Moreover, we review the evolution of these practices, identifying how the constant changes and modernization of the mobile execution environment has impacted the methods proposed in the literature. Finally, we introduced discussion on the application of these practices in a real productive setting, opening an area for further research that may determine if practitioners have followed the proposed assurance paradigms.     

Strength of pure alumina ceramics above 1 GPa

Up to now, commercially available alumina ceramics were claimed to have strength between 400 and 550 MPa. However, our study shows strength ~ 2 times higher for commercially available alumina than commonly believed. The average and characteristic strength, measured on 31 pure alumina ceramic discs by ball on three balls (B3B) test, were 1205 ± 93 MPa and 1257 MPa, respectively, with a Weibull modulus of m = 11.8. Tested specimens were in form of discs with a diameter of 5 mm and thickness 0.5 mm. The grain size distribution of the alumina is bimodal with an average grain size of ~ 850 nm measured at the surface. The fracture reveals a mixed transgranular / intergranular failure mode. To avoid incorporation of additional flaws, the discs were tested as sintered. The characteristic flexural strength measured in B3B was recalculated according to Weibull theory for standard 4-point bending bars of size 3 × 4 × 45 mm as bend 856 MPa. The measured strength of nearly 900 MPa shows the potential of strength for high purity alumina ceramics.     

Intrinsic CFRP-metal-hybrids with rubber interface for the improvement of the damping behaviour

This paper presents an integrated passive damping approach in hybrid metal-CFRP parts for structural applications. In this concept a viscoelastic material is embedded in the joint zone of the hybrid component. To examine the connection strength single-lap-joint specimens were produced and tested and the influence of the used material combinations, different surface structures, and different process parameters i.e. the moment of cross-linking were evaluated. Afterwards, the metal-CFRP hybrids were tested in quasi-static tests to assess their connection strength and failure behaviour. Dynamic cyclic tensile tests with step-wise increased loading conditions were performed to determine the specimens damping behaviour and to estimate their fatigue performance. Finally, these results are compared to a state of the art metal-CFRP hybrid with rivets connecting both materials.     

On stochastic comparisons of finite mixtures for some semiparametric families of distributions

In this paper, we consider the classical finite mixture model, which is an effective tool for modeling lifetime distributions for random samples from heterogeneous populations. We discuss new results on stochastic comparison for two finite mixtures when each of them is drawn from one of the following semiparametric families, i.e., proportional hazards, accelerated lifetime and proportional reversed hazards.