Achieving Rich and Active Alkaline Hydrogen Evolution Heterostructures via Interface Engineering on 2D 1T‐MoS2 Quantum Sheets

Large‐scale production of hydrogen from water‐alkali electrolyzers is impeded by the sluggish kinetics of hydrogen evolution reaction (HER) electrocatalysts. The hybridization of an acid‐active HER catalyst with a cocatalyst at the nanoscale helps boost HER kinetics in alkaline media. Here, it is demonstrated that 1T–MoS₂ nanosheet edges (instead of basal planes) decorated by metal hydroxides form highly active ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ heterostructures, which significantly enhance HER performance in alkaline media. Featured with rich ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ sites, the fabricated 1T–MoS₂ QS/Ni(OH)₂ hybrid (quantum sized 1T–MoS₂ sheets decorated with Ni(OH)₂ via interface engineering) only requires overpotentials of 57 and 112 mV to drive HER current densities of 10 and 100 mA cm^?2, respectively, and has a low Tafel slope of 30 mV dec^?1 in 1 m KOH. So far, this is the best performance for MoS₂‐based electrocatalysts and the 1T–MoS₂ QS/Ni(OH)₂ hybrid is among the best‐performing non‐Pt alkaline HER electrocatalysts known. The HER process is durable for 100 h at current densities up to 500 mA cm^?2. This work not only provides an active, cost‐effective, and robust alkaline HER electrocatalyst, but also demonstrates a design strategy for preparing high‐performance catalysts based on edge‐rich 2D quantum sheets for other catalytic reactions.     

陕南山地烟田不同植烟年限土壤养分的变化

为给陕南山地烟草生产布局及有针对性的施肥措施提供依据,分析了陕南山地烟田不同植烟年限(0~15年)与土壤养分含量的关系。结果表明:随着植烟年限延长,有机质线性下降,全氮和速效钾显著上升,有效磷先上升后下降;氯、有效铁、有效锰、有效硼和有效铜无显著变化或变化很小,有效锌则在第1年急剧下降,之后保持稳定,10年后再次显著下降。认为陕南山地烟区烟叶生产中应适当增加有机肥的施用而合理控制氮肥、磷肥和钾肥的施用,并要注意锌肥的补充。     

Preparation and electrochromism of pyrochlore-type tungsten oxide film

Pyrochlore-type WO_3 powder was synthesized via hydrothermal method using aqueous sodium tungstate solution and oxalic acid as raw materials. The as-prepared powder was made into a soliquoid,from which films were made by dip coating process with indium-tin oxide(ITO).The obtained films were characterized by thermogravimetric and differential thermal analysis(TG-DTA), X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM), cyclic voltammetry(CV), chronoamperometry(CA) and ultravioletvisible(UV-Vis) absorption. Results show that the crystal of the pyrochlore-type WO_3 powder is perfect. When the calcination temperature rises from room temperature to500 ℃,the pyrochlore-type structure first becomes deformed, then it is destroyed and turns into amorphous phase,finally it will completely convert to WO_3 with a monoclinic structure. Electrochemical and optical tests demonstrate that the film calcined at 300 ℃ exhibits the best electrochromic performance and has a coloration efficiency of up to 68.5 cm~2 C~(-1) at 884 nm.     

埋地管道泄漏内封堵装置设计与研究

针对流体输送埋地管道泄漏问题,设计了一种利用管道机器人携带封堵气囊进行快速应急封堵修复的埋地管道泄漏内封堵装置。采用矩阵变换方法建立了牵引系统驱动轮过弯方程,利用MATLAB软件对过弯方程进行了验证,同时利用ADAMS软件仿真分析过弯路径与驱动轮转角对牵引系统行走速度的影响。研究结果表明:由两个串联封堵器组成的应急封堵系统可满足复杂工况下的管道泄漏封堵要求;牵引系统驱动轮在弯管内部行走时,单轮速度呈周期性变化,但三个驱动轮整体周期运动特性一致;驱动轮转角在25°~40°时,牵引系统行走速度与驱动轮转角成正比,且转角为30°时驱动效果最好。该内封堵装置的结构设计可为管道泄漏应急封堵领域装备的研发提供重要参考。