Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

A cheating immune (k, n) visual cryptography scheme by using the rotation of shares

Multimedia Tools and Applications - Since Noar and Shamir introduced visual cryptography scheme (VCS), the cheating problem of VCS has absorbed much attention of scholars. The current researches on...     

The effect of alkali metal oxide on the properties of borosilicate fireproof glass: Structure,thermal properties,viscosity, chemical stability

The purpose of the current work was to research the effect of alkali metal oxide on the structure, thermal properties, viscosity and chemical stability in the glass system (R₂O–CaO–B₂O₃–SiO₂) systematically. Because the glass would emulsify when Li₂O was added to the glass batch, this article did not discuss Li₂O. The results showed that when the amount of Na₂O was less than 4 mol.%, there was a higher interconnectivity of borate and silicate sub-networks in glass, as more mixed Si–O–B bonds were present in glass. The glass samples exhibited excellent thermal properties and chemical stabilities. As the amount of Na₂O exceeded 4 mol.%, the interconnectivity of borate and silicate sub-networks was weakened. The thermal properties and chemical stabilities of the glass samples were reduced. The connectivity of the silicate sub-network was weakened slightly as the Na/K ratio varied, and the coefficient of thermal expansion (CTE) of the glass samples gradually increased, and the resistance to thermal shock (RTS) value gradually decreased. Moreover, the viscosity of the glass samples decreased with the ratio of Na/Si and Na/K increased.     

Facile synthesis of MgO–Mg2SiO4 composite ceramics with high strength and low thermal conductivity

The recycling of solid waste is a win-win solution for humans and nature. For this purpose, magnesite tailings and silicon kerf waste were employed to prepare MgO–Mg₂SiO₄ composite ceramics by solid-state reaction synthesis in the present work. Then, effects of sintering temperature and raw material ratio on as-prepared ceramics were systematically studied. As-prepared ceramics showed improvement in their relative density (from 47.55%–68.12% to 90.96%–95.25%) and cold compressive strength (from 7.34–118.66 MPa to 303.39–546.65 MPa) with the increase in sintering temperature from 1300 to 1600 °C. In addition, it was found that Si promoted synthesis process of Mg₂SiO₄ phase through transient liquid phase sintering and Fe₂O₃ accelerated sintering process through activation sintering. Consequently, the presence of Mg₂SiO₄ phase effectively improved the density and strength of MgO–Mg₂SiO₄ composite ceramic, while reducing its thermal conductivity. This work provides a potential reutilization strategy for magnesite tailings, and as-prepared products are expected to be applied in fields of construction, metallurgy, and chemical industry.     

多孔SiO2分子巢制备多功能涤纶纤维试验研究

针对传统PET材料不具备抗菌、不耐洗等问题,以煎煮法为基础,以草珊瑚、艾叶和薄荷为原料,制备含植物活性成分的溶液,其具有抗菌、杀菌的作用;以溶胶-凝胶法为多孔材料制备方法,用十六烷基三甲基溴化铵、十二烷基苯磺酸钠表面活性剂为模板剂,正硅酸乙酯为有机硅源,氨水为催化剂,乙醇和乙醚为助溶剂,在水-乙醇-乙醚体系中合成多孔二氧化硅微球;然后,多孔二氧化硅微球与提取液混合制备含植物活性成分的多孔二氧化硅分子巢;最后以制备的多孔二氧化硅分子巢与普通的聚酯切片用熔融纺丝工艺进行造粒、纺丝,得到具有抗菌、杀菌和耐洗的多功能涤纶纤维.通过SEM微观观察和力学性能测试、抗菌试验、耐洗性测试,对上述制备的多功能涤纶纤维性能进行验证.结果表明:在模板剂总浓度为0.029 mol·L-1、V醇:V醚=20:20、两种表面活性剂比为4:1时,得到的多孔SiO2微球排列规整;当多孔二氧化硅分子巢掺量(质量分数)在0.5％～1％时,通过熔融共混纺丝得到的新型多功能涤纶纤维力学性能表现最优;当多孔二氧化硅分子巢掺量(质量分数)在1％时,得到的新型多功能涤纶纤维的抗菌性能达到87.9％.而二氧化硅分子巢掺量越高,纤维材料越耐洗.以上结果说明本试验制备涤纶纤维的方案可行.     

Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.     

Feasibility study of large-scale mass customization 3D printing framework system with a case study on Nanjing Happy Valley East Gate

At present, the development and implementation of digital transformation are the keys to promoting high-quality industry development. The new digital fabrication method of robotic 3D printing is a research area being studied by many to tackle the issue of the declining productivity of traditional construction methods. Although many studies have been done, most of the current 3D printing projects are facing limitations in terms of scale. In order to bridge the gap, this article proposed a mass customization 3D printing framework system for large-scale projects. This article discusses how mass customization is made possible through the joint operation of the FUROBOT software and 3D printing hardware. By taking the east gate of Nanjing Happy Valley Plaza as a case study, the article demonstrates and studies the feasibility of the large-scale mass customization 3D printing framework system.     

Rheological phase reaction synthesis and electrochemical performance of LiFe2/3Mn1/3PO4/C cathode for lithium-ion batteries

LiFe_2/3Mn_1/3PO₄/C composite was prepared by the rheological phase reaction using LiH₂PO₄, Li₂CO₃, FePO₄, Mn(Ac)₂·4H₂O and ascorbic acid as starting materials. The crystal structure and morphology of as-synthesized sample were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The analysis of XRD results showed that the obtained sample was single-phase with orthorhombic olivine-type structure (Pnma space group). SEM micrographs revealed that the sample was aggregates, with an irregular morphology. The initial discharge capacity was 166.9, 149.1, 139.6, 112.8, 82.93 mAh g^??1 at the rate of 0.1, 0.5, 1, 2, and 10 C, respectively. And when the rate was 0.1, 0.5, 1, 2, and 10 C, the capacity retention was 92.2%, 90%, 92.9%, 97.6%, 91.5% after 50, 100, 200, 200, 500 cycles, respectively.