Reusable Polyacrylonitrile-Sulfur Extractor of Heavy Metal Ions from Wastewater

Mercury, lead, and cadmium are among the most toxic and carcinogenic heavy metal ions (HMIs), posing serious threats to the sustainability of aquatic ecosystems and public health. There is an urgent need to remove these ions from water by a cheap but green process. Traditional methods have insufficient removal efficiency and reusability. Structurally robust, large surface-area adsorbents functionalized with high-selectivity affinity to HMIs are attractive filter materials. Here, an adsorbent prepared by vulcanization of polyacrylonitrile (PAN), a nitrogen-rich polymer, is reported, giving rise to PAN-S nanoparticles with cyclic π-conjugated backbone and electronic conductivity. PAN-S can be coated on ultra-robust melamine (ML) foam by simple dipping and drying. In agreement with hard/soft acid/base theory, N- and S-containing soft Lewis bases have strong binding to Hg²⁺, Pb²⁺, Cu²⁺, and Cd²⁺, with extraordinary capture efficiency and performance stability. Furthermore, the used filters, when collected and electrochemically biased in a recycling bath, can release the HMIs into the bath and electrodeposit on the counter-electrode as metallic Hg⁰, Pb⁰, Cu⁰, and Cd⁰, and the PAN-S@ML filter can then be reused at least 6 times as new. The electronically conductive PAN-S@ML filter can be fabricated cheaply and holds promise for scale-up applications.     

Effect of MoS2/PTFE coatings on performance of Si3N4/TiC ceramics in dry sliding against WC/Co

To enhance the tribological performance of Si₃N₄/TiC ceramics, MoS₂/PTFE composite coatings were deposited on the ceramic substrate through spraying method. The micrographs and basic properties of the MoS₂/PTFE coated samples were investigated. Dry sliding friction experiments against WC/Co ball were performed with the coated ceramics and traditional ones. These results showed that the composite coatings could significantly reduce the friction coefficient of ceramics, and protect the substrate from adhesion wear. The primary tribological mechanisms of the coated ceramics were abrasive wear, coating spalling and delamination, and the tribological property was transited from slight wear to serious wear with the increase of load because of the lower surface hardness and shear strength. The possible mechanisms for the effects of MoS₂/PTFE composite coatings on the friction performance of ceramics were discussed.     

Theoretical study on a kind of cyclization mechanism of boron trichloride and hexamethyldisilazane to form the borazine ring for SiBCN ceramics precursor

Borazine rings act as a pivotal part in siliconboroncarbonitride ceramics (SiBCN) for high-temperature stability and great resistance to crystallization. A detailed investigation of the ring formation mechanism will guide the design and synthesis of SiBCN to meet application requirements under extreme conditions. Boron trichloride (BCl₃) and hexamethyldisilazane (HN(SiMe₃)₂) are common raw materials for the synthesis of precursors for SiBCN. In this paper, quantum chemical calculation was used to study the cyclization reaction mechanism between BCl₃ and HN(SiMe₃)₂ to form trichloroborazine (TCBZ) at the MP2/6-31G (d,p) level of theory. We discussed the structure properties, reaction pathways, energy barriers, reaction rates, and other aspects in detail. The results show that BCl₃ and HN(SiMe₃)₂ alternately participate in the reaction process, accompanied by the release of trimethylchlorosilane (TMCS), and that the entire reaction shows an absolute advantage in terms of energy. In the Step by step reaction, lower reaction barriers are formed due to the introduction of BCl₃ with more heat released compared to that for the introduction of HN(SiMe₃)₂. The final single-molecule cyclization and TMCS elimination steps are found to be faster compared to all previous bimolecular reactions.     

Nanomaterials for radiotherapeutics-based multimodal synergistic cancer therapy

Over the past decade, numerous studies have attempted to enhance the effectiveness of radiotherapy (external beam radiotherapy and internal radioisotope therapy) for cancer treatment. However, the low radiation absorption coefficient and radiation resistance of tumors remain major critical challenges for radiotherapy in the clinic. With the development of nanomedicine, nanomaterials in combination with radiotherapy offer the possibility to improve the efficiency of radiotherapy in tumors. Nanomaterials act not only as radiosensitizers to enhance radiation energy, but also as nanocarriers to deliver therapeutic units in combating radiation resistance. In this review, we discuss opportunities for a synergistic cancer therapy by combining radiotherapy based on nanomaterials designed for chemotherapy, photodynamic therapy, photothermal therapy, gas therapy, genetic therapy, and immunotherapy. We highlight how nanomaterials can be utilized to amplify antitumor radiation responses and describe cooperative enhancement interactions among these synergistic therapies. Moreover, the potential challenges and future prospects of radio-based nanomedicine to maximize their synergistic efficiency for cancer treatment are identified.

     

Polyethylene oxide-polypropylene oxide -polyethylene oxide derived porous carbon materials with different molecular weights as ORR catalyst in alkaline electrolytes

Polyethylene oxide (PEO)-polypropylene oxide (PPO)-polyethylene oxide block copolymer having different molecular weights are used as precursors of carbon materials to prepare Hollow -Derivatives carbon material as an electrocatalyst through block copolymer self-assembly. The composition and microstructure of the prepared catalysts are shown by Raman spectroscopy, X-ray diffraction (XRD), Test of nitrogen adsorption and desorption curves, High resolution transmission electron microscopy (HR-TEM) and scanning electron microscopy (HR-SEM). Oxygen was passed into alkaline electrolyte solution until the solution reached saturation state. With molecular weight increasing, the obtained sample gradually changed from block to hollow and spherical. When the molecular weight was 12600 g mol^?1, the evenly hollow carbon nanocages was acquired (C-12600). In O₂ saturated alkaline electrolyte (0.1 M KOH solution), C-12600's limited current density，half-wave potential and initial potential are 5.23 mA cm^?2@0.4 V, 0.72 V and 0.81 V, respectively. And most important is that half-wave potential and onset potential have barely change after 2000 cycles of cyclic voltammetry. As a result, the porous carbon materials exhibited excellent electrocatalytic activity while maintaining high stability in alkaline KOH solution.     

Design of novel urogenital pharmabiotic formulations containing lactobacilli,salivaricin CRL 1328 and non-microbial compounds with different functionalities

Context: The administration of pharmabiotics is a promising alternative to antimicrobial drugs for the treatment and/or prevention of female urogenital infections.

Objective: To design pharmabiotic formulations including bioactive ingredients of microbial origin combined with non-microbial substances and then to evaluate the stability of the combinations during freeze-drying and storage.

Materials and methods: Different formulations including Lactobacillus gasseri CRL 1263, Lactobacillus salivarius CRL 1328, salivaricin CRL 1328 (a bacteriocin) and non-microbial compounds (lactose, inulin and ascorbic acid) were assayed, and the ingredients were freeze-dried together or separately. The formulations were stored in gelatin capsules at 4?°C for 360?d.

Results: The viability of lactobacilli was affected to different extents depending on the strains and on the formulations assayed. L. salivarius and ascorbic acid were successfully combined only after the freeze-drying process. Salivaricin activity was not detected in formulations containing L. gasseri. However, when combined with ascorbic acid, lactose, inulin or L. salivarius, the bacteriocin maintained its activity for 360?d. The selected microorganisms proved to be compatible for their inclusion in multi-strain formulations together with lactose, inulin and ascorbic acid. Salivaricin could be included only in a L. salivarius CRL 1328 single-strain formulation together with non-microbial substances.

Conclusions: This study provides new insights into the design of urogenital pharmabiotics combining beneficial lactobacilli, salivaricin CRL 1328 and compounds with different functionalities.     

Photopolymerization synthesis of polyacrylic acid dispersant with methoxysilicon end groups and its application in a nano‐SiO2 aqueous system

In order to improve the dispersity and stability of the nano‐SiO₂ aqueous system with high solid content, a kind of polyacrylic acid dispersant with methoxysilicon end groups (KH590‐PAA) was synthesized by photopolymerization of acrylic acid (AA) initiated with (3‐mercaptopropyl)trimethoxysilane (KH590). After adding KH590‐PAA into the nano‐SiO₂ aqueous dispersion system (20 wt% solid content), the viscosity and the curing time of the system were measured with a rotational viscometer and the inverted bottle method. Moreover, the dispersion mechanism of KH590‐PAA for the nano‐SiO₂ aqueous system was researched by measuring the adsorption capacity, the particle size and the zeta potential of the nanoparticles with a conductivity meter, dynamic light scattering, SEM and TEM, respectively. The results showed that the methoxysilicon groups in KH590‐PAA could react with hydroxyl groups on the surface of nano‐SiO₂ in the process of stirring, which enhanced the adsorption capacity of the dispersant and then increased the surface charge of the particles. Therefore, electrostatic repulsion and steric hindrance effects between the SiO₂ nanoparticles could be further enhanced by adding the KH590‐PAA dispersant, and then the nano‐SiO₂ aqueous system exhibited better dispersity and stability. Besides, the dispersion properties of SiO₂ nanoparticles in water were closely related to the addition amount and the molecular weight of the KH590‐PAA dispersant. © 2018 Society of Chemical Industry     

A new perspective of co-doping and Nd segregation effect on proton stability and transportation in Y and Nd co-doped BaCeO3

Bulk and surface properties of proton stability and transportation in Y and Nd co-doped BaCeO₃ (BCYN), especially the effect of Nd segregation, were investigated by first-principles calculations. Since the structure of doped BaCeO₃ at the operating temperature of proton-conducting has been unclear for a long time, we have summarized the latest experimental results and calculated the structure of the asymmetric BCYN for the first time. The results show that compared with Y, Nd doping promotes oxygen vacancy formation, however reduces proton stability. Our calculation can also provide a possible explanation for the formation of space charge layer at the grain boundary of doped BaCeO₃ in experiment. Unlike the stable Y in BCYN, Nd is calculated to be easily segregated, which can facilitate both proton hydration and proton transportation near the surface. Moreover, Nd segregation at the grain boundary is predicted to be beneficial for proton transportation between grains.