Preparation and photoconduction of rapidly quenched films in the Bi2O31bM2O5 system (M=V,Nb and Ta)

The Bi₂O₃1bM₂O₅ films (M=V, Nb and Ta) were prepared by a rapid quenching technique using a twin-roller type equipment. Quenched film of pure Bi₂O₃ partially precipitated a tetragonal phase which differs from well-known β-Bi₂O₃ in structure. In every (Bi₂O₃)_0.975 (M₂O₅)_0.025 composition (2.5% M₂O₅), the tetragonal phase was obtained as single phase, and the tetragonality became greater than that of the pure Bi₂O₃. Beyond this composition, the tetragonality decreased to form δ-phase with a fcc structure with increasing the M₂O₅ content. The lowest V₂O₅ content forming a δ-phase was 5%, while a slight tetragonality still remained in the samples containing 10% Nb₂O₅ and 10% Ta₂O₅, respectively. From the measurement of the photoconductivities of the quenched films, it was proved that a photoconduction appeared in the tetragonal phase while no photoconductivity was observed in the cubic phase. The characteristic of the photoconduction was that a remarkable decrease in the resistivity was observed when a light of ca. 500 nm in wave length was irradiated on the films.     

Crystallographic Texture Development in Bismuth Sodium Titanate Prepared by Reactive-Templated Grain Growth Method

Bi_0.5Na_0.5TiO₃ (BNT) and 0.94Bi_0.5Na_0.5TiO₃·0.06BaTiO₃ (BNT–BT) bulk ceramics with extensive 〈100〉 texture were prepared by the reactive-templated grain growth method, using platelike Bi₄Ti₃O₁₂ (BIT) particles as templates for BNT. Calcined compacts were composed of matrix grains with random orientation and 〈100〉-oriented grains transformed from aligned BIT particles, and the texture developed by the growth of oriented grains during sintering. Ceramics with extensive texture were obtained by using the starting mixture containing the maximum concentration of platelike BIT to form the maximum volume fraction of oriented grains.     

Microstructures of functionally graded materials fabricated by centrifugal solid-particle andin-situ methods

Functionally graded materials (FGMs) belong to a relatively new class of inhomogeneous composite materials, in which the composition and/or microstructure undergo a gradual change along some directions. In this review article, the microstructures and composition gradients in Al/SiC, Al/Shirasu (volcanic eruptions commonly found in south Kyushu in Japan), Al/Al₃Ti, Al/Al₃Ni, Al/Al₂Cu FGMs have been investigated. The Al/SiC, Al/Shirasu and Al/Al₃Ti FGMs are fabricated by the centrifugal solid particle method where the distribution particles of SiC, Shirasu and Al₃Ti are solids in the melts. On the other hand, Al/Al₃Ni and Al/Al₂Cu FGMs are fabricated by the centrifugalin-situ method where Al/Al₃Ni and Al/Al₂Cu systems have lower liquidus temperatures than the processing temperatures. The feature of Al/(Al₃Ti−Al₃Ni) hydrid FGM, which is fabricated by a method combining both the centrifugal solid-particle andin-situ methods, is also shown.     

Three dimensional virtual crack closure-integral method (VCCM) with skewed and non-symmetric mesh arrangement at the crack front

In this paper, an extension of virtual crack closure-integral method (VCCM) for three dimensional linear fracture mechanics analysis using hexahedron finite elements is presented. In conventional three dimensional VCCM, there are some inherent requirements on the finite element model. They are (i) the faces of finite elements across the crack front have the same areas and (ii) they must be arranged symmetrically across the crack front. In present study, we developed a three dimensional VCCM without such requirements by considering work required to open one element face area whose shape is arbitrary. Though we assume the use of an ordinary 20 node serendipity element, present approach can be applied to other types of hexahedron elements.     

Some Notes on Stability Problems of Probabilistic Automata

Abstract

The behavior of a probabilistic automaton is essentially characterized by products of matrices selected from a given finite set of stochastic matrices. It is of interest to know under what conditions these matrix products are stable against perturbations of the entries in the matrices.     

Cerebral Hyperperfusion after Revascularization Inhibits Development of Cerebral Ischemic Lesions Due to Artery-to-Artery Emboli during Carotid Exposure in Endarterectomy for Patients with Preoperative Cerebral Hemodynamic Insufficiency: Revisiting the “Impaired Clearance of Emboli” Concept

The purpose of the present study was to determine whether cerebral hyperperfusion after revascularization inhibits development of cerebral ischemic lesions due to artery-to-artery emboli during exposure of the carotid arteries in carotid endarterectomy (CEA). In patients undergoing CEA for internal carotid artery stenosis (≥70%), cerebral blood flow (CBF) was measured using single-photon emission computed tomography (SPECT) before and immediately after CEA. Microembolic signals (MES) were identified using transcranial Doppler during carotid exposure. Diffusion-weighted magnetic resonance imaging (DWI) was performed within 24 h after surgery. Of 32 patients with a combination of reduced cerebrovascular reactivity to acetazolamide on preoperative brain perfusion SPECT and MES during carotid exposure, 14 (44%) showed cerebral hyperperfusion (defined as postoperative CBF increase ≥100% compared with preoperative values), and 16 (50%) developed DWI-characterized postoperative cerebral ischemic lesions. Postoperative cerebral hyperperfusion was significantly associated with the absence of DWI-characterized postoperative cerebral ischemic lesions (95% confidence interval, 0.001–0.179; p = 0.0009). These data suggest that cerebral hyperperfusion after revascularization inhibits development of cerebral ischemic lesions due to artery-to-artery emboli during carotid exposure in CEA, supporting the “impaired clearance of emboli” concept. Blood pressure elevation following carotid declamping would be effective when embolism not accompanied by cerebral hyperperfusion occurs during CEA.     

Investigation of UV-A light irradiation on tomato fruit injury during storage

We investigated the effect of UV-A light (wavelength 315 to 400 nm) irradiation during storage on tomato fruit injury. Mature green tomato fruit (cv. House Momotaro) were exposed to UV-A at doses of 0.02, 0.5, and 2 mW x cm(-2) throughout storage at 25 degrees C. The physiological disorders, fruit ripening, superoxide dismutase (SOD) activity, and increases in fruit temperature were evaluated. All UV-A-irradiated and nonirradiated tomatoes developed a full red color at the same time (2 weeks). Irradiated fruit ripened normally, and exposure of tomato fruits to UV-A did not lead to the discoloration of ripe tomato fruit at any dosage. The fruit temperature did not increase in response to various UV-A light doses and exposure times, and none of the UV-irradiated fruits showed physiological disorders (dull skin blemish, pitting). The SOD activity of UV-A-irradiated fruit exposed to the various UV-A doses did not significantly (P = 0.05) differ from that of fruit stored in dark conditions. The SOD results imply that UV-A light might not induce reactive oxygen species in UV-A-irradiated fruit.     

Alcohol dehydrogenases that catalyse methyl formate synthesis participate in formaldehyde detoxification in the methylotrophic yeast Candida boidinii

Methyl formate synthesis during growth on methanol by methylotrophic yeasts has been considered to play a role in formaldehyde detoxification. An enzyme that catalyses methyl formate synthesis was purified from methylotrophic yeasts, and was suggested to belong to a family of alcohol dehydrogenases (ADHs). In this study we report the gene cloning and gene disruption analysis of three ADH-encoding genes in the methylotrophic yeast Candida boidinii (CbADH1, CbADH2 and CbADH3) in order to clarify the physiological role of methyl formate synthesis. From the primary structures of these three genes, CbAdh1 was shown to be cytosolic and CbAdh2 and CbAdh3 were mitochondrial enzymes. Gene products of CbADH1, CbADH2 and CbADH3 expressed in Escherichia coli showed both ADH- and methyl formate-synthesizing activities. The results of gene-disruption analyses suggested that methyl formate synthesis was mainly catalysed by a cytosolic ADH (CbAdh1), and this enzyme contributed to formaldehyde detoxification through glutathione-independent formaldehyde oxidation during growth on methanol by methylotrophic yeasts.     

Optical assessment of silicon nanowire arrays fabricated by metal-assisted chemical etching

Silicon nanowire (SiNW) arrays were prepared on silicon substrates by metal-assisted chemical etching and peeled from the substrates, and their optical properties were measured. The absorption coefficient of the SiNW arrays was higher than that for the bulk silicon over the entire region. The absorption coefficient of a SiNW array composed of 10-μm-long nanowires was much higher than the theoretical absorptance of a 10-μm-thick flat Si wafer, suggesting that SiNW arrays exhibit strong optical confinement. To reveal the reason for this strong optical confinement demonstrated by SiNW arrays, angular distribution functions of their transmittance were experimentally determined. The results suggest that Mie-related scattering plays a significant role in the strong optical confinement of SiNW arrays.     

Improvement of carrier diffusion length in silicon nanowire arrays using atomic layer deposition

To achieve a high-efficiency silicon nanowire (SiNW) solar cell, surface passivation technique is very important because a SiNW array has a large surface area. We successfully prepared by atomic layer deposition (ALD) high-quality aluminum oxide (Al₂O₃) film for passivation on the whole surface of the SiNW arrays. The minority carrier lifetime of the Al₂O₃-depositedSiNW arrays with bulk silicon substrate was improved to 27 μs at the optimum annealing condition. To remove the effect of bulk silicon, the effective diffusion length of minority carriers in the SiNW array was estimated by simple equations and a device simulator. As a result, it was revealed that the effective diffusion length in the SiNW arrays increased from 3.25 to 13.5 μm by depositing Al₂O₃ and post-annealing at 400°C. This improvement of the diffusion length is very important for application to solar cells, and Al₂O₃ deposited by ALD is a promising passivation material for a structure with high aspect ratio such as SiNW arrays.