Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Controlled Secure Direct Communication Protocol via the Three-Qubit Partially Entangled Set of States

In this paper, we first re-examine the previous protocol of controlled quantum secure direct communication of Zhang et al.’s scheme, which was found insecure under two kinds of attacks, fake entangled particles attack and disentanglement attack. Then, by changing the party of the preparation of cluster states and using unitary operations, we present an improved protocol which can avoid these two kinds of attacks. Moreover, the protocol is proposed using the three-qubit partially entangled set of states. It is more efficient by only using three particles rather than four or even more to transmit one bit secret information. Given our using state is much easier to prepare for multiqubit states and our protocol needs less measurement resource, it makes this protocol more convenient from an applied point of view.     

A facile method for preparation of PGS@ZB‐N and gas‐sol alternating synergistic effect for fire resistance of EVA

Through the simple precipitation of palygorskite (PGS) by zinc borate (ZB) (to make PGS@ZB) and the decoration of PGS@ZB by dodecylamine (N), a novel organic‐inorganic@inorganic hybrid flame retardant of PGS@ZB‐N was prepared and was incorporated with ethylene vinyl acetate copolymer (EVA) to improve its flame retardance. The structure and morphology of PGS@ZB‐N were characterized by Fourier transform infrared (FTIR) spectroscopy, X‐ray diffraction (XRD), and scanning electron microscopy (SEM), and it was confirmed that the PGS@ZB‐N hybrid had been successfully prepared. The flame retardancy and burning behavior of EVA/PGS@ZB‐N/EG (EG = expandable graphite) composite were studied through thermogravimetric analysis (TGA), limiting oxygen index (LOI), UL‐94 (by the vertical burning test), and cone calorimeter test (CCT) characterizations. The prepared EVA/PGS@ZB‐N/EG composite obtained an LOI value of 41.2% with the addition of 30 wt% PGS@ZB‐N/EG. It was found that EVA/PGS@ZB‐N/EG was protected through a gas phase and condensed phase alternating synergistic effect mechanism.     

Zinc doped Fe2O3 for boosting Electrocatalytic Nitrogen Fixation to ammonia under mild conditions

Artificial nitrogen fixation is emerging as a promising approach for synthesis of ammonia at mild conditions. Inspired by biological nitrogen fixation based on bacteria containing iron, zinc doped Fe₂O₃ nanoparticles are proposed as an efficient and earth abundant electrocatalyst for converting N₂ to NH₃. In neutral media, it achieves a maximum Faradaic efficiency (FE) of 10.4% and a large NH₃ yield rate of 15.1 μg h^?1 mg^?1_cat. at ?0.5 V vs. reversible hydrogen electrode. This catalyst also exhibits excellent selectivity and stability. Theoretical calculations suggest the reaction follows the associative enzymatic mechanism and it has a barrier of as low as 0.68 eV.     

营尔凹陷下白垩统油气勘探应避开高压水层

营尔凹陷下白垩统(K₁₎存在下沟组和赤金堡组2套源岩，目前它们已到成熟阶段。凹陷东侧长沙岭构造在下白垩统下沟组和赤金堡组储层中也发现油藏，但主要分布在高压水层的顶部及下部，而高压水层段存在良好的储层，并未发现油气。文章根据高压水层段的储层荧光特征，通过储层烃与源岩的对比，分析了下白垩统高压水层对油气运移的影响。研究结果表明：高压水层段，储层荧光弱，储层抽提物特征既不同于赤赤金堡组源岩，也不同于下构组源岩，为就近捕获的产物；高压水层未发生大规模的油气运移，其形成时间早于油气运移的时间。建议该区油气勘探目标的选择应避开高压水层，选择凹陷附近的圈闭、高压水层以下的层位。     

炼油厂碱性污水生物催化氧化预处理工艺研究

在对炼油厂碱性污水水质分析的基础上,提出采用生物催化氧化工艺对碱性污水进行预处理。试验结果表明,在水力停留时间为4 h,曝气量(标准状态)为8 m3／h的条件下,碱性污水的硫化物去除率可达90％以上,出水中的硫化物平均值为15．2 mg/L,CODCR、酚和油的去除率分别为47．5％,44．1％,50．8％,其中CODCR体积负荷为3．85 kg／(m3·d),是传统生化处理的10倍, 达到了污水预处理的目的。