磨料有序排布电镀砂轮的制备及其把持力研究

为解决电镀砂轮磨削加工中容屑空间不足的问题，采用点胶微粘接的方法制备了磨料有序排布的电镀砂轮，分析了磨料粘接效果和镀层力学性能。通过SEM分析了磨料/镀层/导电胶的结合界面，并进行了干磨削试验。研究结果表明，直径约为磨料粒径40%的胶点可粘接住磨料，单个胶点上粘接多颗磨料的占比小于6%；双脉冲电镀工艺制备的镀层显微硬度大于500HV，表层残余应力小于100MPa，磨料/镀层/导电胶之间的界面贴合紧密，无明显缺陷；砂轮在磨削时没有出现磨料脱落现象。     

Impact of gypsum on flotation of scheelite and fluorite using sodium oleate as collector

ABSTRACT

In this study, effect of calcium and gypsum on scheelite and fluorite was investigated using sodium oleate as collector. Micro-flotation and contact angle results showed that the adsorption of calcium could inhibit the hydrophobicity of scheelite and fluorite. Moreover, sulfate could enhance the inhibition. FT-IR results showed that calcium could be priori precipitated into calcium oleate and adsorb on mineral surface. The adsorption of calcium could increase the scheelite potential to IEP, while it showed limited effect on fluorite potential. However, the interaction of calcium on scheelite and fluorite in gypsum solution was more complex than that in calcium solution.     

Novel Bi-Doped Amorphous SnOx Nanoshells for Efficient Electrochemical CO2 Reduction into Formate at Low Overpotentials

Engineering novel Sn-based bimetallic materials could provide intriguing catalytic properties to boost the electrochemical CO₂ reduction. Herein, the first synthesis of homogeneous Sn_1−xBi_x alloy nanoparticles (x up to 0.20) with native Bi-doped amorphous SnO_x shells for efficient CO₂ reduction is reported. The Bi-SnO_x nanoshells boost the production of formate with high Faradaic efficiencies (>90%) over a wide potential window (−0.67 to −0.92 V vs RHE) with low overpotentials, outperforming current tin oxide catalysts. The state-of-the-art Bi-SnO_x nanoshells derived from Sn_0.80Bi_0.20 alloy nanoparticles exhibit a great partial current density of 74.6 mA cm⁻² and high Faradaic efficiency of 95.8%. The detailed electrocatalytic analyses and corresponding density functional theory calculations simultaneously reveal that the incorporation of Bi atoms into Sn species facilitates formate production by suppressing the formation of H₂ and CO.     

300M超高强钢在中性盐雾环境中的腐蚀行为及机制

摘要：为了研究300M超高强钢在中性盐雾环境中的腐蚀行为及腐蚀机制，采用失重法，宏观、微观腐蚀形貌分析，三维表面轮廓分析及电化学分析的研究方法，来表征腐蚀实验现象并进行分析。结果表明：300M超高强钢在中性盐雾环境中的腐蚀产物为FeOOH、Fe2O3、Fe(OH)3和Fe3O4；腐蚀速率随着腐蚀时间逐渐降低，腐蚀后期（72h）腐蚀速率降低50%；腐蚀初期以点蚀为主，点蚀坑通过横向扩展，逐渐发展为后期的均匀腐蚀，腐蚀表面形貌呈沟壑状；外腐蚀层对基体的保护能力很弱，Cr元素在锈层靠近基体的一侧偏聚使内腐蚀层具有一定的抗腐蚀性。     

Mineralization of Para-Chlorobenzoic Acid in Water by Cobalt-Incorporated MCM-41 Catalyzed Ozonation

Cobalt-incorporated MCM-41(Co-MCM-41) was used as a heterogeneous catalyst for the ozonation of para-chlorobenzoic acid (p-CBA) in aqueous solution. Cobalt oxide supported on MCM-41(Co/MCM-41) was synthesized for comparison. Their textural properties were elucidated by various characterization techniques to understand the relationship between surface texture and catalytic activity. TOC removal at 60 min reached 91% with Co-MCM-41, 83% with Co/MCM-41 and only 52% with ozone alone, respectively. Observations from diffuse reflection spectroscopy demonstrated that different metal phases were formed in these cobalt-modified molecular sieves samples. Radical scavenger experiments indicated the formation of hydroxyl radicals that were responsible for the effective degradation of p-CBA. An integrated approach to the catalytic mechanism was proposed by considering the variation of pH in the course of ozonation as well as its subsequent influence on the dissociation of targeted compounds and surface charge of the catalyst. In the reusability experiments, the reused Co-MCM-41 was able to regain the same catalytic capability as the fresh one within 5 cycles. X-ray photoelectron spectroscopy results indicated that a part of Co²⁺ was oxidized to Co³⁺ after oxidation reaction.     

微型步进马达线架组自动卷线设备设计

微型步进马达线圈组卷线上下料基本靠手动作业,效率低下,同时因工人技术水平的不同造成产品品质不稳定的问题多发.为此专门设计了微型步进马达线圈组自动卷线及上下料设备.通过结合现阶段的先进工业技术,采用振动盘分离区分进料,多机构并联三菱PLC及威纶人机界面触摸屏研发了此微型步进马达线圈组自动上下料及卷线设备.通过该设备实现了微型步进马达因工人不足导致产能减少和品质多发问题,减少企业成本,提升产品品质.     

Oxygen transport,thermal and electrochemical properties of NdBa0.5Sr0.5Co2O5+δ cathode for SOFCs

In this study, the crystal structure, thermal, oxygen transport, electrical conductivity and electrochemical properties of the perovskite NdBa_0.5Sr_0.5Co₂O_5+δ (NBSC55) are investigated. In the temperature range of 250 °C–350 °C, the weight loss upon heating was due to a partial loss of lattice oxygen and along with a reduction of Co⁴⁺ to Co³⁺. The tend of weight-loss slows down as temperature increased above 350 °C indicating a reduction of Co³⁺ to Co²⁺ during this stage. The oxygen migration is dominated by surface exchange process at high temperature range (650-800 °C); however, the bulk diffusion process prevails at low temperature range (500–600 °C). For long-term testing, the polarization resistance of NBSC55 increases gradually form 3.13 Ω cm² for 2 h to 3.34 Ω cm² for 96 h at 600 °C and an increasing-rate for polarization resistance is around 0.22% h^?1. The power density of the single cell with NBSC55 cathode reached 341 mW cm^?2 at 800 °C.     

用于疏浚工程泥浆密度测量的电阻层析成像技术

江河湖海疏浚工程对于拓展和保障航运安全、促进生态恢复、维护/改善远海岛礁环境具有不可或缺的作用.目前,在绞吸和耙吸疏浚船上,多采用射线密度计及电磁流量计对输泥密度、产量等进行在线计量,并作为实现疏浚系统自动控制的重要参量.由于射线密度计潜在的人员健康、公共安全和环保风险,在一些国家和地区已建立了放射源的有序退出机制.电阻层析成像使用安装于管壁的电极阵列获得管道内流体的电导率分布,进而推导出管道内的泥浆密度,具有无辐射、全场测量及实时可视化的优点.电阻层析成像测量系统经过特殊设计,可适应从内陆淡水到海水的巨大电导率变化.初步测试表明,电阻层析成像测量数据与射线密度计具有良好一致性,具备了作为在线泥浆密度测量的可行性.此外,ERT可提供实时的流动成像,对于提高对疏浚管道监测能力和降低堵管概率具有重要意义.     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.