本文将完全互补码(Complete Complementary Code, CCC)应用于多输入多输出(Multiple Input Multiple Output, MIMO)雷达目标探测中，针对具有非零多普勒的多目标检测问题，提出一种基于广义普洛黑-修-莫尔斯(Generalized Prouhet-Thue-Morse, GPTM)序列和二项式系数加权的信号处理方法。该方法分别在发射端和接收端进行处理，在发射端采用GPTM序列设计方法调整脉冲的发射顺序，以降低由多普勒引起的距离旁瓣；在接收端通过二项式设计(Binomial Design, BD)方法为各接收脉冲加上不同权重，扩大目标多普勒附近的清洁区。为综合上述两次处理的优势，将两次处理得到的距离多普勒谱进行逐点最小化处理，得到最终的距离多普勒谱，然后进行有序恒虚警检测。仿真结果表明，本文所提的信号处理方法具有良好的旁瓣抑制效果和多普勒分辨率，能够有效检测出非零多普勒目标。     

Characteristic tryptic peptides and gelling properties of porcine skin gelatin affected by thermal action

Thermal action in extraction process had effects on characteristic tryptic peptides identification and gelling properties of porcine gelatin. SDS-PAGE, HPLC-LTQ/Orbitrap high-resolution mass spectrometry, texture analyser and rheometer were used to evaluate collagen depolymerisation degree, characteristic tryptic peptides and gelling properties of gelatins prepared in various thermal actions. Results showed that with increasing temperature and time, depolymerisation degree enlarged, while gel strength, gelling and melting temperature decreased. Mass spectra showed that 47 and 49 common characteristic tryptic peptides were identified in gelatins extracted at 50 °C and 100 °C with various times, respectively. Moreover, 34 common characteristic tryptic peptides were identified in all gelatin samples. Further comparison between this work and our previous investigations yielded 20 common characteristic tryptic peptides, which stably exist in various thermal actions. These common characteristic tryptic peptides may be very helpful for the accurate authentication of porcine gelatin.     

Enhanced thermal conductivity and stability of boron nitride/phenyl silicone rubber composites via surface modification and grain alignment

Journal of Materials Science - With the extensive use of high-power electronic appliances, polymer-based thermal insulation composites with excellent thermal properties are utilized in the field of...     

Synthesis of Ionic Ultramicroporous Polymers for Selective Separation of Acetylene from Ethylene

The design of highly stable and efficient porous materials is essential for developing breakthrough hydrocarbon separation methods based on physisorption to replace currently used energy-intensive distillation/absorption technologies. Efforts to develop advanced porous materials such as zeolites, coordination frameworks, and organic polymers have met with limited success. Here, a new class of ionic ultramicroporous polymers (IUPs) with high-density inorganic anions and narrowly distributed ultramicroporosity is reported, which are synthesized by a facile free-radical polymerization using branched and amphiphilic ionic compounds as reactive monomers. A covalent and ionic dual-crosslinking strategy is proposed to manipulate the pore structure of amorphous polymers at the ultramicroporous scale. The IUPs exhibit exceptional selectivity (286.1–474.4) for separating acetylene from ethylene along with high thermal and water stability, collaboratively demonstrated by gas adsorption isotherms and experimental breakthrough curves. Modeling studies unveil the specific binding sites for acetylene capture as well as the interconnected ultramicroporosity for size sieving. The porosity-engineering protocol used in this work can also be extended to the design of other ultramicroporous materials for the challenging separation of other key gas constituents.     

125I粒子条联合胆道支架植入治疗恶性梗阻性黄疸22例疗效分析

【摘要】　 　目的 研究和探讨125I粒子条联合胆道支架植入治疗恶性梗阻性黄疸的临床疗效。方法 2011年6月—2013年9月收治恶性梗阻性黄疸患者40例。行胆道支架植入术治疗患者18例，为对照组；采用125I粒子条联合胆道支架植入患者22例，为观察组。两组均采用经皮肝穿刺胆道引流（PTCD）并胆道支架植入。结果 观察组与对照组的平均胆道开通时间分别为（8.7 ± 0.7）和（6.2 ± 0.4）个月，两组比较差异有统计学意义（P < 0.05）。观察组与对照组术后平均生存时间分别为（11.4 ± 0.8）和（8.7 ± 0.5）个月，生存时间的差异有统计学意义（P < 0.05）。术后近期疗效及并发症两组之间的比较无明显差异（P > 0.05），但是远期疗效有显著差异（P < 0.05）。结论 与对照组相比，观察组的术后生存时间及胆道开通时间明显延长，对于125I粒子条联合支架治疗恶性梗阻性黄疸值得进一步临床研究。
     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.     

Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

A first-principles investigation on mechanical and metallic properties of titanium carbides under pressure

The titanium carbides are potential candidates to achieve both high hardness and refractory property. We carried out a structural search for titanium carbides at three pressures of 0 GPa, 30 GPa and 50 GPa. A phase diagram of the Ti-C system at 0 K was obtained by elucidating formation enthalpies as a function of compositions, and their mechanical and metallic properties of titanium carbides were investigated systematically. We also discussed the relation of titanium concentration to the both mechanical and metallic properties of titanium carbides. It has been found that the average valence electron density and tractility improved at higher concentrations of titanium, while the degree of covalent bonding directionality decreased. To this effect, the hardness of titanium carbide decreases as the content of titanium increases. Our results indicated that the titanium content significantly affected the metallic properties of the Ti-C system.