Myelodysplastic syndromes (MDS) are highly heterogeneous myeloid neoplasms, and a large number of patients are difficult to diagnose and classify by blood and bone marrow examination. As a surface marker of granulocyte, studies have shown CD10 can be used to define the degree of granulocyte maturation in MDS patients. However, whether it can be used for differential diagnosis of MDS and other hematological diseases remains inconclusive. To explore the value of CD10 for differential diagnosis of MDS, 60 newly diagnosed MDS, 20 aplastic anemia (AA) patients, and 35 iron-deficient anemia (IDA) patients were selected for this study. Bone marrow (BM) specimens were processed for surface marker analysis and labeled with pre-conjugated monoclonal antibodies. Stained cells were detected by flow cytometry. Our results indicated that CD10-positive granulocytes were significantly decreased in BM of MDS patients than AA and IDA patients, and the level of CD10-positive mature granulocytes was not associated with the clinical stages of malignancy. Receiver operating characteristic (ROC) areas under the curve (AUC) of CD10-positive granulocytes was 0.86 and 0.85, respectively, in MDS patients than the IDA group and AA group with good specificity and sensitivity. Further, CD10-positive granulocytes were increased after effective treatment. In conclusion, we found the decrease in CD10-positive granulocytes has a differential diagnostic value of MDS.     

300M超高强钢在中性盐雾环境中的腐蚀行为及机制

摘要：为了研究300M超高强钢在中性盐雾环境中的腐蚀行为及腐蚀机制，采用失重法，宏观、微观腐蚀形貌分析，三维表面轮廓分析及电化学分析的研究方法，来表征腐蚀实验现象并进行分析。结果表明：300M超高强钢在中性盐雾环境中的腐蚀产物为FeOOH、Fe2O3、Fe(OH)3和Fe3O4；腐蚀速率随着腐蚀时间逐渐降低，腐蚀后期（72h）腐蚀速率降低50%；腐蚀初期以点蚀为主，点蚀坑通过横向扩展，逐渐发展为后期的均匀腐蚀，腐蚀表面形貌呈沟壑状；外腐蚀层对基体的保护能力很弱，Cr元素在锈层靠近基体的一侧偏聚使内腐蚀层具有一定的抗腐蚀性。     

Crystallographic characteristics and microwave dielectric properties of Ni-modified MgTa2O6 ceramics

Ni²⁺ modified MgTa₂O₆ ceramics with a trirutile phase and space group P4₂/mnm were obtained. The correlations between crystallographic characteristics and microwave dielectric performance of MgTa₂O₆ ceramics were systematically studied based on the chemistry bond theory (PVL theory) for the first time. The results indicate that the introduction of Ni²⁺ causes a change in polarizability and the Mg–O bond ionicity, which contributes to the variation of dielectric constant. Moreover, the lattice energy, and packing fraction, full width at half maximum of the Raman peak of Ta–O bond, as the quantitative characterization of crystallographic parameters, regulate the dielectric loss of MgTa₂O₆ ceramics in GHz frequency band. In addition, the study of sintering behavior shows that the densification and micromorphology are the crucial factors affecting the microwave dielectric performance. Typically, Ni²⁺ doping on the A-site of MgTa₂O₆ can effectively promote the Q × f values to 173,000 GHz (at 7.43 GHz), which ensures its applicability in 5G communication technology.     

Investigation of crystal characteristics,Raman spectra,and microwave dielectric properties of Mg1-xZnxTa2O6 ceramics

Mg_(1-x)Zn_xTa₂O₆ (x = 0.00?0.08) dielectric ceramics were synthesized via the traditional solid-state reaction method. We used XRD and Rietveld refinement to demonstrate that a pure Mg_(1-x)Zn_xTa₂O₆ phase with trirutile structure was formed. Zn²⁺ substitution helped to decrease the Raman full width at half width of the A_1g mode at 703 cm^?1, which resulted in an increase in the order and rigidity of the TaO₆ octahedron, this in turn contributed to improving the Q×f values. Additionally, the introduction of Zn²⁺ significantly promoted grain growth and increased the dense, and the molecular polarizability, these factors lead to a higher permittivity. Moreover, enhanced Ta-O bond energy resulted in a more stable TaO₆ octahedron in the Mg_(1?x)Zn_xTa₂O₆ system, which contributed to enhanced τ_f values via substitution of Zn²⁺ doped on the A-site. Correspondingly, the microwave dielectric properties were significantly improved for 0.04-doped samples, obtaining: ε_r = 27, Q × f = 185,000 GHz (at 7.47 GHz), τ_f =32 ppm/°C.     

HFC电缆分配系统的建设与思考

结合沧州市网络的实际情况，主要分析HFC电缆分配系统双向传输改造的建设标准和实施方案。     

晶须取向对SiCw/6061Al复合材料热压缩变形行为的影响

采用SEM 和 Magiscan-2A 图像分析系统研究了晶须取向对SiCw/6061Al复合材料在300℃压缩变形行为的影响.结果表明:晶须取向影响着晶须折断程度和转动角度; 随着晶须取向角的增加,晶须转动和折断行为所导致的软化效果下降.同时晶须取向也影响复合材料的热压缩应力-应变曲线的形状.在热压缩变形过程中,晶须取向角为0°和30°的复合材料表现出明显应变软化现象, 晶须取向角为45°的复合材料无明显软化现象.晶须取向角为90℃的复合材料表现出应变硬化现象.     