吸湿凉爽机织物的结构设计与性能

为研究织物组织结构与复合纱线线密度对织物凉爽性能的影响,将线密度为7.4和9.8 tex涤纶分别与线密度为7.8 tex锦纶反向加捻、并线后作为纬纱,以8.3 tex涤纶/竹浆纤维50/50混纺纱作经纱,设计平纹、二上一下斜纹和透孔组织织物.测试织物的瞬间接触凉感、热湿舒适性能及织物干、湿态升温曲线,并采用凉爽温度指数对织物的综合凉爽性能进行评价.研究结果表明:6种设计织物的瞬间接触凉感均高于标准,且平纹织物最好,纬纱粗细对瞬间接触凉感影响不显著;透孔织物透气性最好,且在人体出汗的状态下具有较好的导湿散热性能.平纹织物凉爽温度指数最高,最大凉爽温度为2.8℃,综合凉爽性能最好.     

三维石墨烯-碳纳米管/水泥净浆的压敏性能

为了探索三维石墨烯-碳纳米管(G-CNTs)/水泥净浆的压敏性能,采用四电极法研究了荷载作用下GCNTs/水泥净浆的电阻率变化,并分析不同G-CNTs掺量、加载幅度、加载速度以及恒定荷载对电阻率变化的影响。研究表明:随着G-CNTs掺量的增加,电阻率呈先减小后稳定的变化趋势,在G-CNTs掺量由0.2wt%增加至1.6wt%时,电阻率下降51.8%;电阻率与温度呈负相关;G-CNTs掺量高于0.8wt%时可以显著提高水泥净浆的压敏性能,且电阻率变化率与应力应变有明显的对应关系,1.2wt%G-CNTs掺量下试件的应力灵敏系数和应变灵敏系数分别为2.3%/MPa和291;G-CNTs/水泥净浆电阻率变化率幅值随着加载幅度增大而相应增加,其电阻率变化率曲线在不同加载速度以及恒定荷载作用下均与应力-应变曲线一一对应,具有良好的压敏特性。     

Preparation and electrochemical characterization of Ti-based amorphous metallic glass with high strength

Ti-based amorphous metallic glasses have excellent mechanical, physical, and chemical properties, which is an important development direction and research hotspot of metal composite reinforcement. As a stable, simple, efficient, and large-scale preparation technology of metallic powders, the gas atomization process provides an effective way of preparing amorphous metallic glasses. In this study, the controllable fabrication of a Ti-based amorphous powder, with high efficiency, has been realized by using gas atomization. The scanning electron microscope, energy-dispersive spectrometer, and X-ray diffraction are used to analyze surface morphology, element distribution, and phase structure, respectively. A microhardness tester is used to measure the mechanical property. An electrochemical workstation is used to characterize corrosion behavior. The results show that as-prepared microparticles are more uniform and exhibit good amorphous characteristics. The mechanical test shows that the hardness of amorphous powder is significantly increased as compared with that before preparation, which has the prospect of being an important part of engineering reinforced materials. Further electrochemical measurement shows that the corrosion resistance of the as-prepared sample is also significantly improved. This study has laid a solid foundation for expanding applications of Ti-based metallic glasses, especially in heavy-duty and corrosive domains.     

Crystallization,structure, and enhanced mechanical property of ethylene-octene elastomer crosslinked with dicumyl peroxide

Crosslinking of polyolefin elastomer (POE, ENGAGE™ 8480) with Dicumyl Peroxide (DCP) can have effects on its crystallization dynamics, crystal structure, and properties. The POE crosslinked uniformly has significantly lower crystalline ability than the one with only amorphous phase crosslinked, which, in turn, has weaker crystalline ability than neat POE. The crystallinity and melting point depend on how the POE is crosslinked. The neat POE and POE crosslinked in amorphous phase only, are investigated with DSC and in-situ tensile/synchrotron radiation (WAXD/SAXS). In situ tensile/synchrotron X-ray during a uniaxial stretching process indicates that severe crystal fragmentation is observed at a strain around 45%, and with further increase in strain. The stress in the crosslinked POE is significantly larger than neat POE. For both samples, crystal orientation increases sharply within the strain range up to 88% where orientation-induced new crystals aligned in stretching direction are observed. The long period increases more in stretching direction for the crosslinked POE, consistent with larger stress in this sample, and the stress difference is more pronounced at large strains (27.3 vs. 10.9 MPa at a strain 435%). Permanent set of the crosslinked POE is smaller, consistent with less oriented crystals observed after the test for permanent set.     

Simultaneous fractionation of multiple classes of polyphenols from honeybush tea using solid-phase extraction

The structural diversity of polyphenols and the inherent limitations of current extraction techniques pose a challenge to extract polyphenols using a simple and green method. Hence, in this study, a method was developed to simultaneously fractionate multiple classes of polyphenols by only varying ethanol-water solutions. Honeybush tea, which is rich in polyphenols, was selected as a model for this study. Solvent extraction followed by solid-phase extraction (SPE) was developed to obtain a polyphenol-rich fraction from six honeybush samples. Based on a gradient elution programme (10%, 30%, 50%, 70% and 90% (v/v) ethanol-water solution) of SPE, the Strata X cartridge showed a better recovery of most targeted polyphenols under 0.9 mL of the drying volume and 1 mL min⁻¹ of the dispensing speed. The elution programme for fractionating most polyphenols was as follows: single elution with 50% ethanol, followed by twice elution with 70% ethanol. The antioxidant capacity was used to analyse the differences among the polyphenol-rich fractions from six honeybush samples. Principal component analysis (PCA) revealed that unfermented C. genistoides (GG) has the greatest antioxidant capacity among the honeybush species studied. Additionally, mangiferin, isomangiferin and vicenin-2 were the main contributors to the antioxidant capacity in six honeybush fractions according to the correlation study.     

有机二氟化硼配合物的合成及压致变色性能表征

以阿伏苯宗和三氟化硼为原料,经过一步反应,合成阿伏苯宗二氟化硼(BF2AVB),产物的结构经1HNMR谱确证.基于荧光光谱与X射线粉末衍射测试,对BF2AVB的压致发光性能和机理进行研究.本实验原料易得,反应条件温和,实验操作简单,反应收率高.BF2AVB的压致变色现象明显,通过探讨压致变色机理,加深同学对压致变色材料的了解.同时,该实验可以拓展学科知识,激发学生的专业热情和科研兴趣.     

中医学视角下城市物质空间的生命要素探析

通过借鉴中医学整体观和生命观的相关理论,从认识城市有机体的生命属性入手,发现并提炼能够产生和传递城市运营所需各种能量的生命要素:廊道和功能体。阐释了其多层级、多性质和多形态的特点,提出了功能体有动力、廊道成系统、敏感点有活力的疏通策略,旨在促进城市各种能量的有机循环,从而维护城市的健康与安全,提高城市生活的效率与质量。