VO2/GaAs异质结的制备及其光电特性研究

采用直流磁控溅射和后退火氧化工艺在p型GaAs单晶衬底上成功制备了n-VO_2/pGaAs异质结,研究了不同退火温度和退火时间对VO_2/GaAs异质结性能的影响,并分析其结晶取向、化学组分、膜层质量以及光电特性。结果表明,在退火时间2 h和退火温度693 K下能得到相变性能最佳的VO_2薄膜,相变前后电阻变化约2个数量级。VO_2/GaAs异质结在308 K、318 K和328 K温度下具有较好的整流特性,对应温度下的阈值跳变电压分别为6.9 V、6.6 V和6.2 V,该结果为基于VO_2相变特性的异质结光电器件的设计与应用提供了可行性。     

Effects of high-pressure-modified soy 11S globulin on the gel properties and water-holding capacity of pork batter

The effects of high-pressure-modified soy 11S globulin (0.1, 200, and 400 MPa) on the gel properties, water-holding capacity, and water mobility of pork batter were investigated. The high-pressure-modified soy 11S globulin significantly increased (P < 0.05) the emulsion stability, cooking yield, hardness, springiness, chewiness, resilience, cohesiveness, the a^* and b^* values, and the G′ and G′′ values of pork batter at 80 °C, compared with those of 0.1 MPa-modified globulin. In contrast, the centrifugal loss and initial relaxation time of T_2b, T₂₁, and T₂₂ significantly decreased (P < 0.05). Meanwhile, the microstructure was denser, and the voids were smaller and more uniform compared with those of 0.1 MPa-modified globulin. In addition, the sample with 11S globulin modified at 400 MPa had the best water-holding capacity, gel structure, and gel properties among the samples. Overall, the use of high-pressure-modified soy 11S globulin improved the gel properties and water-holding capacity of pork batter, especially under 400 MPa.     

Facile preparation and strong adhesive strength of honeycomb polyurethane films with small pore diameter

With the continuous development of bionics, such as, geckos and virginia creeper with both superhydrophobic and super-adhesive, the surface wetting and super-adhesive properties of various porous materials have attracted extensive attention of the scientific and medical communities. Here, the honeycomb polyurethane (PU) porous films with strong adhesion were successfully prepared by microphase separation method and the effects of growth parameters on their microstructure and adhesive strength to ice were investigated. It was found that a high relative humidity (e.g., 100%) and a low solution concentration (e.g., 2%) facilitated the formation of ordered honeycomb PU porous films, and as-prepared PU pores with average pore diameter as small as 5 μm are better ordered and more uniform than these in related documents. Although the contact angle of water droplets on the surface of PU porous films increased from the premodification value of 85–130° to more than 160° after surface modification with polydopamine (PDA), the corresponding rolling angle remained approximately constant (180°), indicating that the surface of PU porous films has strong adhesion similar to geckos and virginia creeper. Furthermore, at lower temperature, the PU porous films exhibited the high adhesive strength of 142.13 kPa on ice, which was strongly dependent on the porous microstructures and surface compositions. The improved adhesive behavior to ice of honeycomb PU porous films modified with PDA provides new strategies for surface modification of materials and potential applications in medical domain.     

Centimeter-scale low-damage micromachining on single-crystal 4H–SiC substrates using a femtosecond laser with square-shaped Flat-Top focus spots

Femtosecond (fs) lasers have been proved to be reliable tools for high-precision and high-quality micromachining of ceramic materials. Nevertheless, fs laser processing using a single-mode beam with a Gaussian intensity distribution is difficult to obtain large-area flat and uniform processed surfaces. In this study, we utilize a customized diffractive optical element (DOE) to redistribute the laser pulse energy from Gaussian to square-shaped Flat-Top profile to realize centimeter-scale low-damage micromachining on single-crystal 4H–SiC substrates. We systematically investigated the effects of processing parameters on the changes in surface morphology and composition, and an optimal processing strategy was provided. Mechanisms of the formation of surface nanoparticles and the removal of surface micro-burrs were discussed. We also examined the distribution of subsurface defects caused by fs laser processing by removing a thin surface layer with a certain depth through chemical mechanical polishing (CMP). Our results show that laser-induced periodic surface structures (LIPSSs) covered by fine SiO₂ nanoparticles form on the fs laser-processed areas. Under optimal parameters, the redeposition of SiO₂ nanoparticles can be minimized, and the surface roughness Sa of processed areas reaches 120 ± 8 nm after the removal of a 10 μm thick surface layer. After the laser processing, micro-burrs on original surfaces are effectively removed, and thus the average profile roughness Rz of 2 mm long surface profiles decreases from 920 ± 120 nm to 286 ± 90 nm. No visible micro-pits can be found after removing ~1 μm thick surface layer from the laser-processed substrates.     

Fabrication and joining mechanism of Nano-Cu/Si3N4 ceramic substrates

A novel method for fabricating a nano-Cu/Si₃N₄ ceramic substrate is proposed. The nano-Cu/Si₃N₄ ceramic substrate is first fabricated using spark plasma sintering (SPS) with the addition of nanoscale multilayer films (Ti/TiN/Ti/TiN/Ti) as transition layers. The microstructures of the nano-Cu metal layer and the interface between Cu and Si₃N₄ are investigated. The results show that a higher SPS temperature increases the grain size of the nano-Cu metal layer and affects the hardness. The microstructure of the transition layer evolves significantly after SPS. Ti in the transition layer can react with Si₃N₄ and with nano-Cu to form interfacial reaction layers of TiN and Ti–Cu, respectively; these ensure stronger bonding between nano-Cu and Si₃N₄. Higher SPS temperatures improve the diffusion ability of Ti and Cu, inducing the formation of Ti₃Cu₃O compounds in the nano-Cu metal layer and Ti₂Cu in the transition layer. This study provides an important strategy for designing and constructing a new type of ceramic substrate.     

提升我国电磁安全能力的战略思考

阐述电磁安全的战略背景,分析电磁兼容到电磁安全的演化过程,剖析"自扰、互扰、敌扰"等现实迫切问题,阐明电磁干扰、电磁兼容等基本概念和相互关系,提出新需求、新技术、新趋势引发电磁兼容与电磁安全的"六大技术挑战",指出只有在认识和思维上系统性地实现"三个转变",才能实现电磁安全整体能力的提升,最后提出"电磁强国"的"五维布局"建议.     

Theoretical study on a kind of cyclization mechanism of boron trichloride and hexamethyldisilazane to form the borazine ring for SiBCN ceramics precursor

Borazine rings act as a pivotal part in siliconboroncarbonitride ceramics (SiBCN) for high-temperature stability and great resistance to crystallization. A detailed investigation of the ring formation mechanism will guide the design and synthesis of SiBCN to meet application requirements under extreme conditions. Boron trichloride (BCl₃) and hexamethyldisilazane (HN(SiMe₃)₂) are common raw materials for the synthesis of precursors for SiBCN. In this paper, quantum chemical calculation was used to study the cyclization reaction mechanism between BCl₃ and HN(SiMe₃)₂ to form trichloroborazine (TCBZ) at the MP2/6-31G (d,p) level of theory. We discussed the structure properties, reaction pathways, energy barriers, reaction rates, and other aspects in detail. The results show that BCl₃ and HN(SiMe₃)₂ alternately participate in the reaction process, accompanied by the release of trimethylchlorosilane (TMCS), and that the entire reaction shows an absolute advantage in terms of energy. In the Step by step reaction, lower reaction barriers are formed due to the introduction of BCl₃ with more heat released compared to that for the introduction of HN(SiMe₃)₂. The final single-molecule cyclization and TMCS elimination steps are found to be faster compared to all previous bimolecular reactions.     

Display illumination with modulated directional backlight

Illumination is essential for modern life as colorful world is perceived by human visionary system. Display technology has been developing rapidly in recent decades, and the basic principle is related to the way that the image is illuminated and light is emanated. Traditional illumination is provided by different types of light sources, and the display image is visible in large viewing space until the emanating light decays to zero. This work proposes and demonstrates a novel illumination scheme for a display in which the displaying images are visible only in specific spatial regions. The directional backlight ensures the image propagating to specific direction while imaging visibility can be controlled to terminate abruptly at certain distance from the display screen while exerting no influence to nearby regions. The working principle for such an illumination scheme is the use of the modulated coherent directional backlight through an axicon lens. It is shown that the illumination scheme can robustly deliver carried image information to the designated viewing region. This new illumination scheme has many advantages over conventional illumination, including its usage for personal display, very lower energy consumption, as well as minimizing light hazard pollution.     

In situ characterization of LiY(WO4)2 nanotubes for electrochemical energy storage

Here, LiY(WO₄)₂ nanotubes are prepared via a feasible electrospinning technique. This new anode material shows excellent electrochemical properties. The capacity loss of LiY(WO₄)₂ nanotubes is as low as 6.9% after 156 cycles, while bulk LiY(WO₄)₂ presents the capacity loss higher than 55.0%. Even after 600 long-life cycles, the capacity loss of the nanotubes is only 9%. It can be seen that the hollow structure with a rough surface and a porous morphology contributes to the improvement of electrochemical performance. Furthermore, online X-ray diffraction (XRD) method is firstly applied to understand the lithium ions insertion/extraction mechanism of LiY(WO₄)₂ nanotubes. It can be concluded that it is an asymmetrical two-phase reaction. A phase transformation from LiY(WO₄)₂ to Li₃Y(WO₄)₂ can be obviously seen from the in situ XRD during discharge process. While Li₂Y(WO₄)₂ appears as an intermediate phase with a reverse charge reaction. In addition, in situ XRD also demonstrates that LiY(WO₄)₂ nanotubes have surprised electrochemical reversibility. All the above results indicate that LiY(WO₄)₂ nanotubes can be expected to be anode candidate for rechargeable lithium ion batteries (LIBs).