Facile preparation and strong adhesive strength of honeycomb polyurethane films with small pore diameter

With the continuous development of bionics, such as, geckos and virginia creeper with both superhydrophobic and super-adhesive, the surface wetting and super-adhesive properties of various porous materials have attracted extensive attention of the scientific and medical communities. Here, the honeycomb polyurethane (PU) porous films with strong adhesion were successfully prepared by microphase separation method and the effects of growth parameters on their microstructure and adhesive strength to ice were investigated. It was found that a high relative humidity (e.g., 100%) and a low solution concentration (e.g., 2%) facilitated the formation of ordered honeycomb PU porous films, and as-prepared PU pores with average pore diameter as small as 5 μm are better ordered and more uniform than these in related documents. Although the contact angle of water droplets on the surface of PU porous films increased from the premodification value of 85–130° to more than 160° after surface modification with polydopamine (PDA), the corresponding rolling angle remained approximately constant (180°), indicating that the surface of PU porous films has strong adhesion similar to geckos and virginia creeper. Furthermore, at lower temperature, the PU porous films exhibited the high adhesive strength of 142.13 kPa on ice, which was strongly dependent on the porous microstructures and surface compositions. The improved adhesive behavior to ice of honeycomb PU porous films modified with PDA provides new strategies for surface modification of materials and potential applications in medical domain.     

Polymers dynamics of the nonfluoro,nano-brush repelling agent with self-stratifying property in water-based coatings

While perfluoroalkyl acids (PFAAs), also known as C8s, are used extensively in textile repellent coatings, concerns have arisen for their carcinogenicity and hazardous effects on the environment. In this study, a novel water-based, nonfluoro, and nanobrush textile repelling agent was prepared by conventional sol–gel chemistry using amorphous fumed silica and n-octyltriethoxysilane as the starting materials. Minimal interaction between the designed repelling agent and marketed water-based resins was confirmed using linear viscosity region (LVR) analysis and asymmetric-flow field-flow fractionation (AF4), suggesting the self-stratification potential of the repelling agent. More specifically, the repelling agent exhibited excellent compatibility and self-stratifying ability with a force-emulsified acrylic-based resin, affording a water contact angle of 104.3° when incorporated at 7% solid content. Performance tests carried out on thermoplastic polyurethane (TPU) revealed excellent adhesion (100/100) of a final formulation, and a significant increase in water contact angle from 80.1° to 103.8° after treatment. In addition, the fouling area after the removal of a submerged sample from a mixture of slurry, polymer, and oil decreased from 48 to 1% when the repelling agent was added. Moreover, the sludge-fouling property remained unchanged after 1000 cycles of abrasion. These findings demonstrate the potential of the described nonfluoro, nanobrush repelling agent as an environmentally safe alternative for use with commercial resins, in turn realizing a fully water-based hydrophobic coating. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48003.     

Synthesis and Characterization of Pr0.6-xNdxCa0.4FeO3-δ with Pechini Method

Pr0.6-x NdxCa0.4 FeO3-δ （ x = 0.0, 0.2, 0.3, 0.4, 0.5, 0.6） were synthesized using Pechini method. A number of studies were conducted concerning composition, specific area, crystalline structure and microstructure of the samples by means of FT-IR, BET, XRD TG-DTA and SEM. The results show that all the samples with different doping amounts of Pr^3＋ and Nd^3＋ on A-site are fine dispersed, and mean particle size less than 100 nm. The powders have good sinterability, and the relative density is 95% after sintered at 1200 ℃ for 2 h. It is found that all specimens are entirely single phase solid solutions with orthorhombic perovskite structure, the stable perovskitetype phase is formed completely after calcination at 900 ℃.     

循环伏安法在润滑油检测中的应用

介绍了循环伏安法的产生背景、原理。应用该技术可以快速、方便地对润滑油中抗氧剂、总酸（碱）值进行测定，并且可以对不同厂家润滑油的抗氧剂包进行区别。该技术还可以有效地评价润滑油的使用寿命和设备工作状况。     

溶剂脱沥青组合工艺生产重交通道路沥青

中国石化荆门分公司以江汉-阿曼混合原油和江汉-鲁宁混合原油为原料,分别采用减压蒸馏—丙烷脱沥青和减压蒸馏—添加催化裂化油浆—丙烷脱沥青工艺,生产出符合SH 0522—2000的100号道路沥青。结果表明,江汉-阿曼混合原油减压渣油中掺兑质量分数为30%的催化裂化油浆后,脱油沥青的各项性能均满足AH-70或AH-90重交通道路沥青的要求,而且薄膜烘箱试验表明,试样延度超过标准要求。     

Magnetic effects of direct ion implantation of Mn and Fe into p-GaN

In p-GaN implanted with Mn (3×10¹⁶ cm⁻² at 250 keV), the material after annealing shows ferromagnetic properties below 250 K. Cross-sectional transmission electron microscopy (TEM) revealed the presence of platelet structures with hexagonal symmetry. These regions are most likely Ga_xMn_1−xN, which produce the ferromagnetic contribution to the magnetization. In p-GaN implanted with Fe, the material after annealing showed ferromagnetic properties at temperatures that were dependent on the Fe dose, but were below 200 K in all cases. In these samples, TEM and diffraction analysis did not reveal any secondary phase formation. The results for the Fe implantation are similar to those reported for Fe doping during epitaxial growth of GaN.