纳米TiO2的光催化作用及其应用研究进展

纳米TiO2 是一种宽禁带半导体光催化剂 ,可用于污水处理、空气净化、灭菌消毒、医疗、化学合成、贵金属提取冶金、能源材料等多个领域 ,未来的研究发展重点应是实用化纳米TiO2 光催化剂的开发及高效光反应器的研制。     

Laboratory study of property-modified prebaked carbon anode and application in large aluminum electrolysis cells

A kind of complex additive mainly containing Al, Mg, F, and O was prepared. The synthetical performances of the property-modified prebaked anodes containing additives were tested in laboratory. On the basis of ideal testing results obtained, a large number of industrial prebaked property-modified anodes are prepared in a large-scale aluminum company. Further more, they are all used in 160 kA prebaked anode aluminum electrolysis cells. The statistic result show that, compared with common anodes, the property-modified ones enhance current by 11.6 kg per ton aluminum averagely.     

碳纤维表面处理对铝电解用硼化钛阴极涂层性能的影响

硼化钛阴极涂层是铝电解用可润湿性阴极材料中的一种，具有优良的抗钠渗透性和对铝液润湿性，可以有效地延长铝电解槽寿命。碳纤维是硼化钛涂层材料的增强剂之一．对硼化钛阴极涂层的性能影响很大。本文研究了不同工艺的液相碳纤维表面氧化处理法对硼化钛阴极涂层抗拉强度和粘接强度的影响。采用PTIR检测碳纤维处理后表面含氧基团的变化，寻找影响硼化钛阴极涂层性能的原因，从而达到最有效地提高TiB2阴极涂层抗拉强度和粘接强度的目的。结果表明，采用工艺(1)(10％HNO3，80℃、恒温5min．超声波、5min)对碳纤维进行表面处理最合理，处理后碳纤维表面含氧基团的含量最高．用其制备硼化钛阴极涂层的抗拉强度、粘接强度最大。     

Effect of electrolysis superheat degree on anticorrosion performance of 5 Cu/（10NiO-NiFe2O4） cermet inert anode

5Cu/(10NiO-NiFe2O4) cermet inert anodes were prepared by cold-pressing and sintering process, and the effect of superheat degree of melting K3AlF6-Na3AlF6-AlF3 on their anticorrosion performance was studied under electrolysis conditions. The results show that, the fluctuation of cell becomes small with increasing of superheat degree, which is helpful to inhibit the formation of cathodic encrustation; the concentration of impurities from inert anode in bath goes up to certain degree, but it is far smaller than those in traditional high-temperature bath. Increasing the superheat degree of melting K3AlF6-Na3AlF6-AlF3 has unconspicuous effect on the contents of impurities in cathodic aluminum. The total mass fractions of Fe, Ni and Cu in aluminum are 15.38% and 15.09% respectively under superheat degree of 95 and 195 ℃. From micro-topography of anode used view, increasing the superheat degree can aggravate corrosion of metal Cu in inert anode, and has negative influence on electrical conductivity of electrode to some extent.     

铝电解用TiB_2阴极涂层固化、炭化的升温制度

采用DTG ,DDTA等热分析手段 ,研究了高温固化、炭化过程中 ,铝电解用TiB2 阴极涂层糊料的质量和能量的变化速率 ,制定了涂层的变速固化、炭化升温制度 ;在此基础上 ,研究了升温制度对TiB2 阴极涂层性能的影响。结果表明 :变速升温制度优于匀速升温制度 ,采用变速固化、炭化升温制度所制备的涂层形变小、无裂纹 ,其抗拉强度达 3.13MPa,电阻率为 2 3.2 μΩ·m ;而采用升温速度为 10 .3℃ /h的匀速固化、炭化升温制度制备的涂层形变大、裂纹多 ,抗拉强度小 (2 .6 9MPa) ,电阻率大 (2 8.6 μΩ·m)。     

Preparation and electrochemical characterization of activated carbons by chemical-physical activation

A process was proposed based on the combination of chemical and physical activation for the production of activated carbons used as the electrode material for electric double layer capacitor (EDLC). By material characterization and electrochemical methods, the influences of the activitation process on the specific surface area, pore structure and electrochemical properties of the activated carbons were investigated. The results show that specific surface area, the mesopore volume, and the specific capacitance increase with the increase of the mass ratio of KOH to char (m(KOH)/m(char)) and the activation time, respectively. When m(KOH)/m(char) is 4.0, the specific surface area and the mesopore volume reach the maximum values, i.e. 1 960 m²/g and 0.308 4 cm³/g, and the specific capacitance is 120.7 F/g synchronously. Compared with the chemical activation, the activated carbons prepared by chemical-physical activation show a larger mesopore volume, a higher ratio of mesopore and a larger specific capacitance. Foundation item: Project(2007BAE12B01) supported by the National Key Technology Research and Development Program of China     

铝电解用NiFe2O4-Cu金属陶瓷阳极的初步研究

采用粉末冶金技术制备了NiFe2O4-Cu金属陶瓷惰性阳极,并对其导电性能和腐蚀行为进行了初步研究.研究发现,金属Cu与NiFe2O4陶瓷润湿性差,难以实现致密化,在升温过程中,过低的表观密度能导致金属铜氧化,降低导电性能.在电解过程中,金属铜的耐蚀性好,但存在聚结现象,可能会导致电流分布不均匀,同时陶瓷基体发生非协同溶解.     

Synthesis and electrochemical characterization of layered Li[Ni1/3CO1/3 Mn1/3]O2 cathode material for Li-ion batteries

1 INTRODUCTIONDue to the high cost of LiCoO2,a commonlyused cathode material in commercial rechargeablelithium-ion batteries , much efforts have been madeto develop cheaper cathode materials than LiCoO2,Li Ni O2and Li MnO2have been studied extensivelyas possible alternatives to LiCoO2[1 4 ]. Stoichio-metric Li Ni O2is knownto be difficult to synthesizeandits multi-phase reaction during electrochemicalcyclingleads to structural degradation,andlayeredLi MnO2has a significant drawback…     

电沉积法制备CuInSe2薄膜的组成与形貌

采电沉积法制备了CuInSe2薄膜材料，研究了制备工艺条件对材料组成、结构与性能的影响。研究结果表明：最佳的沉积电位范围为-0．6～0．8V（vsSCE）；硒化退火是获得高质量CuInSe，薄膜的必要过程，硒化退火温度应控制在440～610℃范围内；在不同沉积电位和不同电解质浓度组成溶液中，通过电沉积并在500℃下硒化退火均可获得黄铜矿结构CuInSe2多晶薄膜；沉积电位的负移会使膜层中CuInSe2的相对含量增加，晶型完善，且杂相减少；随着电解质浓度的增加，电沉积CuInSe2退火后结晶程度变好，颗粒变得粗壮，致密性也有所改善；电沉积并硒化退火后薄膜中的铜铟摩尔比受沉积电位和电解质浓度影响较大，当沉积电位为-0．7和-0．8V时，铜铟摩尔比约为1较为理想，且铜铟摩尔比的变化与电解液中CuCl2和InCl3的摩尔比变化一致。     

AlF3添加剂和焙烧温度对铝电解炭阳极过电位的影响

在实验室制备各类AlF3掺杂试验阳极，在测试其基本物理化学性能的基础上，采用“改进断电流法”进行阳极过电位测试，研究AlF3添加剂和阳极焙烧温度对阳极过电位的影响。结果表明：在一定条件下，阳极中添加AlF3既可降低阳极的空气／CO2反应活性，也可降低阳极过电位；受高温脱S等因素的影响，阳极的电化学活性及其空气／CO2反应活性并未随着焙烧温度的提高相应降低。