Wear resistance of ceramic coating on AZ91 magnesium alloy by micro-arc oxidation

The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation （MAO） was characterized. The results show that the ceramic coating （3.4-23 μm in thickness）on the surface ofAZ91 alloy was attained under different micro-arc oxidation treatment conditions, which consist mainly of MgO, Mg2SiO4 and MgSiO3 phases. Nano-hardness in a cross-sectional specimen was determined by nano-indentation experiment. The MAO coatings exhibit higher hardness than the substrate. Dry sliding wear tests for the MAO coatings and AZ91 alloy were also carded out using an oscillating friction and wear tester in a ball-on-disc contact configuration. The wear resistance of the MAO coatings is improved respectively under different treatment time as a result of different structures of ceramic coatings formed on AZ91 alloy.     

语义Web模糊规则的互换与实现

针对模糊规则语言f-SW-if-then-unless-RL不能与f-RIF框架中的模糊规则语言互换规则的问题,构建f-SW-if-then-unless-RL和 f-RIF之间的规则映射,设计并实现一个能够自动处理f-SW-if-then-unless-RL规则和在这2种语言间互换模糊规则的原型系统,命名为规则交换系统。实现的原型系统成为f-RIF互换框架的重要组成部分。     

大跨度桥梁风致竖向抖振控制研究

以鄂东长江大桥(主跨为926m的斜拉桥)为工程背景,建立该桥梁无控、有间断型TMD和连续型TMD的ANSYS模型,对比分析控制器对桥梁风致竖向抖振的减振效果。间断型TMD是在桥梁结构合适的位置布置一段或几段TMD;连续型TMD是在主跨或全桥上连续布置TMD,两者的控制效果均优于单个TMD。ANSYS计算结果表明,间断型TMD和连续型TMD对桥梁风致竖向抖振的减振效果明显。最后,根据相似比制作桥梁模型,进行无控和安装了连续型TMD的桥梁模型风洞试验,结果表明,连续型TMD对桥梁的风致竖向抖振能起到很好的控制效果。     

基于维基百科的冬奥会概念下的低频词条双语迭代扩展

随着2022年北京冬奥会的临近,有必要构建一个与冬奥会相关的垂直领域知识图谱,但目前网络上没有较完整的冬奥会相关术语集,因此,需要用集合扩展的方法对冬奥会术语集进行补充.近年来,集合扩展的方法主要基于Word2Vec进行研究,但扩展平均词频较低的冬奥会中文领域时效果并不理想.该文提出了中英文双语迭代扩展的方法,利用数量...     

优酷VR从内容开始

2016年5月11日晚,优酷在上海举办主题为“2016优酷奇妙夜”的VR战略发布会,宣布将通过与全球顶级制作公司、顶级明星展开合制或版权合作,与产业链最强硬件合作伙伴联盟,以及投入VR基金等全方位举措,打造最强VR平台,全力推进VR产业前行.活动发布了与数字王国合作的《麦兜》、与Reload Studios合作的《Raven》、与狮门影业合作的《分歧者2》、《饥饿游戏3》 VR版,和数字王国、易星传媒合作的国内首个VR短片《黑童话》以及倍受欢迎的综艺节目《极限挑战》、《火星情报局》的VR部分.如此众多的顶级VR内容发布在国内尚属首次.     

无机富锌漆中锌粉形状对涂层重防腐蚀性能的影响

为了进一步研究无机富锌底漆中锌粉形状对涂层及其复合涂层防腐蚀性能的影响,分别选用球状和片状锌粉制备了无机富锌底漆,并与H702环氧云铁中间漆、H703灰环氧面漆一起构成了重防腐蚀复合涂层体系。通过盐雾腐蚀和电化学交流阻抗谱技术研究了无机富锌底漆涂层及其复合涂层的防腐蚀性能。结果表明:片状无机富锌底漆涂层的耐蚀性能更强,经过长时间的盐雾腐蚀没有出现明显的腐蚀产物;复合涂层交流阻抗谱的Bode中低频阻抗模值在较长时间内稳定在107Ω·cm2左右,Nyquist谱中的容抗弧半径明显增大,片状复合涂层的防腐蚀性能优于球状复合底漆涂层。     

占空比对Fe-Ni-Cr合金镀层成分及耐蚀性的影响

采用脉冲电沉积方法在黄铜基体上制备出纳米晶Fe-Ni-Cr合金镀层,并研究了占空比对其成分及耐蚀性的影响。结果表明:当占空比为50%时,制备的Fe-Ni-Cr合金镀层成分稳定,其中Cr的质量分数达到37.4%;晶粒尺寸约为12.6nm;在3.5%的NaCl溶液中的自腐蚀电位约为-200mV,自腐蚀电流密度约为0.27μA/cm2,电荷转移电阻约为12 000Ω/cm2,耐蚀性最好。     

单峰过载对2205双相不锈钢疲劳裂纹扩展速率的影响

采用电液伺服疲劳试验机对2205双相不锈钢进行不同过载比(1.0,1.5,2.5,3.5)下的疲劳裂纹扩展试验,研究了单峰过载对疲劳裂纹扩展速率的影响。结果表明:过载比越大,2205双相不锈钢裂纹扩展停滞的时间越长,疲劳裂纹扩展速率下降的幅度越大;当过载比小于3.5时,单峰过载引起裂纹尖端发生钝化或闭合,疲劳裂纹扩展速率明显下降甚至暂时停滞;当过载比为3.5时,裂纹尖端发生偏折及分叉,疲劳裂纹扩展完全停止。     

Sm(Co_(bal)Ni_(0.18)Fe_(0.1)Zr_(0.04))_x的永磁薄膜性能的研究

稀土永磁合金薄膜在微机电系统(MEMS)、磁记录介质、自旋电子元件和医疗科学领域有着重要的应用。Sm Co基永磁薄膜,其内禀居里温度高于其他永磁薄膜,高温条件下有更高的稳定性,因而在MEMS中具有潜在的应用前景。采用复合靶和纯钐靶共溅射制备出Sm Co基永磁薄膜样品,研究了薄膜合金中Sm含量以及退火温度等对Sm(CobalNi0.18Fe0.1Zr0.04)x相结构、微观形貌以及磁性能的影响,得出以下结论:退火温度对薄膜织构也有明显影响。随着退火温度提高,薄膜织构增强,矫顽力提高。随着Sm含量的提高,薄膜中Sm Co相析出增多,组织更加均匀,矫顽力明显提高。     

柴北缘马北地区下干柴沟组储层特征

运用岩心、铸体薄片、扫描电镜和化验资料等,系统研究了柴达木盆地北缘地区下干柴沟组储层孔隙结构特征,并对储层发育的控制因素进行了分析。结果表明,下干柴沟组储集空间以原生粒间孔为主,其次为溶蚀孔和少量裂缝。储层综合评价为中孔-细喉道-中渗型储层。沉积相带是储层储集性能的主要控制因素,该区发育的辫状河河床亚相的砂砾岩是主要储集岩。成岩作用对储集性能也有影响,其中压实作用和胶结作用降低孔隙度,溶蚀作用增加次生孔隙。