1.
采用氧-乙炔火焰喷熔工艺,制备了碳化钨颗粒增强镍基合金喷熔层(NiCrBSi/WC),研究了它在腐蚀介质条件下的摩擦磨损行为与机理,并考察了载荷、滑动速度对其摩擦磨损性能的影响规律。研究结果表明:NiCrBSi/WC具有良好的耐腐蚀磨损性能,且当WC含量为20%时,腐蚀磨损率最低;WC含量超过20%后,由于喷熔层存在“腐蚀原电池”效应,其腐蚀磨损率增大。NiCrBSi/WC的腐蚀磨损率随载荷增加而变大,随速度增大而减小。载荷的增加使喷熔层的犁削磨损加剧,导致摩擦系数和磨损率增大;速度的增大造成摩擦界面温度上升,可生成摩擦转移膜,从而降低了喷熔层的磨损率。 相似文献
2.
一台刚大修过的TY-120推土机在作业过程中,前两个小时机励运行基本正常,但在以后的作业中,无记尉进组后运,边机都有自动问6侧胞德的现象,打目此现象随着作业时间的后长而加重,最后导致推工作业无力,不能再继续使用。履带式推土机跑编的主要原因是:敢侧转向高合器国遵片充油污或挪n外露,使摩擦系数降培,转向日台器不能有效地输出初刀;滚测活问慕台器库源广磨损失效或压紧弹奏弹刀降境,凛凛片不能被压紧,使转回高吕器不能合效地输出动力;挺倒转向日合器操纵针没合自由百程式操纵村自愿胶缓冲望同有杂物,造成库门口吕器的分日… 相似文献
3.
玻璃孔加工的试验研究 总被引:3,自引:0,他引:3
研究了电镀金刚石工具结构和加工参数对玻璃孔加工质量和加工效率的影响。试验结果表明,在电镀金刚石工具端部开槽,可获得小的玻璃爆边直径和高的材料去除率。冷却方式影响玻璃孔的加工质量,主轴转速和配重载荷影响玻璃孔的加工效率。 相似文献
4.
为提高石墨/CaF2/TiC/镍基合金(GCTN)复合涂层的力学性能和摩擦学性能,运用等离子喷涂技术在45钢表面制备了Y2O3改性GCTN复合涂层,研究了Y2O3对复合涂层的微观组织、显微硬度、断裂韧性和摩擦磨损性能的影响。结果表明:Y2O3改性GCTN复合涂层主要由γ-Ni、CrB、Cr7C3、TiC、CaF2和石墨等物相组成。Y2O3在等离子火焰加热作用下与C元素反应生成活性元素Y,Y净化了复合涂层的微观组织,并细化了CrB、Cr3C7等硬质相晶粒,提高了其致密性。当Y2O3质量分数为0.5%时,复合涂层的显微硬度和断裂韧性分别为593.3MPa和6.82MPa·m1/2,比不含Y2O3的复合涂层分别增大了8%和22%,其机理主要是Y2O3细化了CrB、Cr3C7等硬质相晶粒,起到了细化强化作用。由于GCTN-0.5Y2O3复合涂层的显微硬度和断裂韧性显著提高,减少了其黏着磨损和微观断裂磨损,因而GCTN-0.5Y2O3复合涂层的摩擦因数和磨损率最小,分别为0.085和0.39×10-3mm3/m。 相似文献
5.
运用等离子喷涂技术在7005铝合金表面制备了WC和CeO2颗粒协同增强镍基合金复合涂层,研究了该复合涂层的微观结构和摩擦学性能。结果表明:加入CeO2颗粒细化了复合涂层的显微组织,使WC增强颗粒从圆形变为不规则多边形,并降低了其脱碳分解程度。不同PV值摩擦条件下,WC-CeO2/镍基合金复合涂层的摩擦系数和磨损失重均低于WC/镍基合金复合涂层和镍基合金涂层。PV值小于3.36 N·m/s时,复合涂层磨损表面的最大接触应力低于其弹性极限接触应力,主要发生微观切削磨损和疲劳磨损;PV值大于3.36N·m/s后,磨损表面的最大接触应力超过其弹性极限接触应力,接触温度也急剧上升至648℃,磨损表面出现明显的塑性变形和脱落,其磨损机制变为多次塑变磨损、磨粒磨损和粘着磨损,并伴有氧化磨损。 相似文献
6.
7.
根据军用机械化桥梁在线监测技术指标要求,提出了在线监测的无线传输网络结构方案,进行了主控单元、电源模块、信号采集模块、无线传输模块等硬件设计.应用实例表明,开发的在线监测系统实现了适应野外作业条件下对军用机械化桥梁工作状态的在线监测以及故障的实时监控、定位和报警. 相似文献
8.
The property parameters and machining output parameters were selected for machinability evaluation of machinable ceramics. Based on fuzzy evaluation theory, two-stage fuzzy evaluation approach was applied to consider these parameters. Two-stage fuzzy comprehensive evaluation model was proposed to evaluate machinability of machinable ceramic materials. Ce-ZrO2/CePO4 composites were fabricated and machined for evaluation of machinable ceramics. Material removal rates and specific normal grinding forces were measured. The parameters concerned with machinability were selected as alternative set. Five grades were chosen for the machinability evaluation of machnable ceramics. Machinability grades of machinable ceramics were determined through fuzzy operation. Ductile marks are observed on Ce-ZrO2/CePO4 machined surface. Five prepared Ce-ZrO2/CePO4 composites are classified as three machinability grades according to the fuzzy comprehensive evaluation results. The machinability grades of Ce-ZrO2/CePO4 composites are concerned with CePO4 content. 相似文献
9.
运用共价官能化技术,实现纳米SiO_2表面接枝3-氨丙基三乙氧基硅烷(APTES)改性(T-SiO_2),并制备功能化纳米SiO_2改性环氧树脂复合材料(T-SiO_2/EP),分析改性后纳米SiO_2表面官能团和化学元素的变化规律,测试T-SiO_2/EP的主要力学性能,研究其在干摩擦条件下的摩擦磨损行为与机制。结果表明:功能化纳米SiO_2的引入,有效改善了环氧树脂的力学与摩擦学性能,且当功能化纳米SiO_2含量为2%时(质量分数,下同),环氧复合材料(2%T-SiO_2/EP)的显微硬度和断裂韧度均达到最大值(70.2HD和1.02MPa·m~(1/2)),并具有优异的减摩耐磨性能。干摩擦条件下,2%T-SiO_2/EP复合材料的摩擦因数和磨损失重分别为0.49和1.7mg,较纯环氧树脂分别降低了31.9%和34.6%,较未改性纳米SiO_2增强的环氧树脂复合材料(U-SiO_2/EP)分别降低了14%和10.5%,并对相应的磨损机理进行了分析。 相似文献
10.
根据电解成形理论设计阴极,用于金属结合剂成形金刚石砂轮的电解修整。应用有限元法求解电场中的拉普拉斯方程几何反问题,计算出阴极曲线形状。假定初始阴极形状,施加阳极边界条件,从砂轮阳极表面开始逐层计算电位分布,求得修整间隙区域的等电位线,从而得到修整阴极工具曲线族。通过设计阴极与砂轮廓形的对比,分析了成形砂轮轮廓形状,修整电压和电解液电导率对设计阴极形状的影响。研究结果表明:设计阴极与成形砂轮的廓形并不一致。随着成形砂轮廓形曲率,修整电压和电导率的增加,设计阴极与砂轮廓形的偏差加大。为了修整出精确的砂轮廓形,成形砂轮的修整参数应保持稳定。 相似文献