钛合金裂纹激光修复工艺研究

采用CO2激光器对TC2钛合金板材进行焊接,通过显微组织、显微硬度对比,优化工艺参数,获得了焊缝外形平整、组织细密、变形小的焊接接头,实现了TC2钛合金的激光精密焊接.激光焊焊缝区的组织较均匀,为典型网篮组织,热影响区较窄,为等轴晶.晶粒度在热影响区较高,从焊缝到基材呈先升后降趋势.焊缝中心显微硬度可达HV420,高于基体约HV80,热影响区的硬度最低,约为HV300～330.     

激光熔覆制备钛基耐磨功能梯度材料

以Ti, 陶瓷粉末和镍基自熔合金粉末按一定比例配置的混合粉末作为预置合金涂层，采用CO2气体激光进行多层熔覆，在Ti600合金表面制备出摩擦磨损性能沿厚度方向呈梯度变化的钛基功能梯度材料(FGM)。利用扫描电镜(SEM)及X射线能谱仪(EDX)分析了材料的微观组织和成份。结果表明，采用合适的合金粉末成份和激光熔覆工艺参数，可以获得原位自生TiC增强颗粒弥散分布且其含量呈梯度变化的钛基功能梯度材料。熔覆层组织均匀细密，各熔覆层之间无明显界限，且与基体呈良好冶金结合。     

TC4合金基体上激光熔敷钛、铝、二氧化硅碳粉末的显微组织

Laser cladding experiment of Ti + Al + SiO2 + C was carried out on Ti6Al4V alloy substrate, thenthe microstructure of the clad layer was analyzed with SEM and its Anti - oxidation function was discussed.Analyses microstructure show that the clad coating can be divided into three zones along the depth direction:clad, binding and heat - affected zones. Ti5Si3 in the clad zone exists in the form of fine dendrites, TiAl matrix filling among Ti5Si3 dendrites plays a role of connecting the Ti5Si3 with the TiAl3 and transferring load,so the clad coating has been strengthened obviously.     

合金基体上激光熔覆Ti+Al粉末的显微组织分析

在合金表面进行了Ti Al的激光熔覆试验研究,利用SEM分析手段对Ti Al熔覆层的显微组织进行了分析,阐述了熔覆层强化相的形成机制,显微组织分析表明,Ti-6Al-4V合金表面Ti Al激光熔覆层的显微组织沿层深方向可分为熔覆区、结合区和热影响区3个区域,在3个区域呈现出不同的组织形态,对基体和熔覆层进行的硬度测试表明,由基体向熔覆层的硬度变化呈上升趋势,在结合区和最外层区域有所下降.     

钛合金激光熔覆(Ti+Al/Ni)/(Cr2O3+CeO2)

为改进钛合金(Ti6Al4V)的耐磨性能，应用脉冲Nd:YAG激光进行了钛合金表面熔覆(Ti+Al/Ni)+(Cr2O3+CeO2)复合涂层实验，分析了工艺参数对熔覆层高度、熔深、稀释率的影响，观测了熔覆层的组织与性能。结果表明，熔覆层高度和熔深随单脉冲能量的增加而增大。单脉冲能量20 J,脉宽8 ms,频率5 Hz,扫描速度1.1 mm/s时稀释率达到最小，其值为3.95%。熔覆层组织是在细小树枝晶和共晶基体上散布的未熔Cr2O3颗粒和白亮球状液析Cr2O3，并有硬化TiAl陶瓷颗粒增强相存在。显微硬度明显提高，最高可达1150 Hv，平均是基材的3～4倍。熔覆层和基材实现良好冶金结合，白亮熔合区宽度10～20 μm。通过优化工艺参数，获得连续、均匀、无裂纹和气孔的高质量涂层。