纳米AlN粉末的制备与烧结

利用低温燃烧合成前驱物制备出平均粒度为100 nm的AlN陶瓷粉末,比较了该粉末的常压烧结和放电等离子烧结的特性.实验表明:以合成的AlN粉末为原料,添加5%(质量比)Y2O3作为烧结助剂,在常压、流动N2气氛下1600℃保温3 h,制备出平均晶粒尺寸为4～8 μm、密度为3.28 g·cm-3的AlN陶瓷;将同样的粉末不加任何烧结助剂,采用SPS技术在1600℃保温4 min,得到密度为3.26 g·cm-3的AlN陶瓷,晶粒度约为1～2μm.     

Synthesis of amphiphilic magnetic microspheres by dispersion copolymerization of styrene and poly(ethylene oxide) macromonomer

Amphiphilic magnetic microspheres ranging in diameter from 5 to 100 µm were prepared by dispersion copolymerization of styrene and poly(ethylene oxide) vinylbenzyl (PEO‐VB) macromonomer (MPEO) in the presence of Fe₃O₄ magnetic fluid. The effects of various polymerization parameters on the average particle size were systematically investigated. The average particle size was found to increase with increasing styrene concentration and initiator concentration. It also increased with decreasing stabilizer concentration and molecular weight of MPEO. The content of the hydroxyl groups localized in the microspheres ranged from 0.01 to 0.2 mmol g^?1. © 2003 Society of Chemical Industry     

住宅设计的分析与研究

总结了住宅设计的发展,概括了住宅各个功能区的特点。通过设计的实例说明了各不同功能区的设计,成果可供进一步的研究参考。     

电信企业信息化统一模型构建策略

电信企业信息化的实质就是赋予电信企业精细化的企业资源整合能力，本以此认识为出发点，通过定义基本的信息化业务元素，需求参数和基本信息处理机制，构建出带有行业共性的电信企业信息化统一模型，该模型针对目前电信企业信息化中常见的和潜在的问题提供了有效的解决措施。     

连续波雷达测距中的解模糊技术

研究连续波雷达测距中的距离模糊问题，分析几种常用解模糊方法的性能，并讨论参差比的选取对测距范围的影响。     

阴,阳离子聚合物地层内凝胶化改善水驱效果的研究

研究了一杆阴离子聚合物（Ａｃ５３０）和一种阳离子聚合物（Ｍｂ５８１）在水溶液中形成凝胶的条件和过程、凝胶化学结构、形态、稳定性和力学性能。在模拟地层的二维微观模型内观测了两种聚合物驱替渗流、相逼、形成凝胶、凝胶封堵大孔道的机理。在亲水填砂模型内测定了阴、阳离子聚合物凝胶体系降低渗透率的能力。     

多孔板体结构足尺性能分析及材料基本要求

本文就利用诸如蛋白石这样的疏松多孔矿料同灰土构成的混合料，在路面结构中表现出的独特有效的抗冻作用机理作了深入分析，并结合足尺试验数据加以验证。阐述了所谓多孔板体结构的概念、机制和材料组成要求。     

HNO3和有机介质中U（Ⅳ）的稳定性研究

研究了ＨＮＯ＿３和ＴＢＰ－煤油介质中Ｕ（Ⅳ）的稳定性。测定了两种介质中Ｕ（Ⅳ）、ＨＮＯ＿３、ＴＢＰ浓度和气相中氧浓度对Ｕ（Ⅳ）氧化速率的影响。Ｕ（Ⅳ）的氧化速率都随温度提高而明显增加．其表观活化能分别为９１ｋＪ／ｍｏｌ（ＨＮＯ＿３介质）和４２ｋＪ／ｍｏｌ（ＴＢＰ－煤油介质）。对两种介质中Ｕ（Ⅳ）的氧化速率规律进行了比较。     

On the corrosion fatigue crack initiation model and expression of metallic notched elements

In the present study, attempts are made to extend the application of the mechanical model for the fatigue crack initiation (FCI) and the FCI life formula of metallic notched elements in laboratory air to those in the corrosive environment. The test results and analysis of the corrosion FCI (CFCI) life of aluminum alloys and Ti---6A1---4V show that the expression of the CFCI life obtained by modifying the FCI life formula in laboratory air can give a good fit to the test results of the CFCI life. The salt water (3.5% NaCl) environment has no effects on the CFCI resistant coefficient compared with the FCI resistant coefficient in laboratory air. However, 3.5% NaCl environment greatly decreases the CFCI threshold of aluminum alloy, but has little effect on the CFCI threshold of Ti---6A1---4V. The loading frequency ranging from 1 Hz to 10 Hz has no appreciable effect on the CFCI life, and thus, the CFCI threshold of aluminum alloys investigated. Hence, the expression for the CFCI life of metallic notched elements proposed in this study is a better one, which reveals a correlation between the CFCI life and the governing parameters, such as, the geometry of the notched elements, the nominal stress range, the stress ratio, the tensile properties and the CFCI threshold. However, this new expression of the CFCI life needs to be verified by more test results.