Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Fabrication and laser performances of Yb:Sc2O3 transparent ceramics from different combination of vacuum sintering and hot isostatic pressing conditions

In this paper we report on the preparation and laser performance of transparent 3at.% Yb:Sc₂O₃ ceramics by reactive sintering of commercially available powders under vacuum followed by hot isostatic pressing (HIP). Combinations of different vacuum sintering temperatures (1650 °C and 1750 °C) and different HIP treatments (1700 °C and 1800 °C at 200 MPa) were tested in order to understand how these steps influence the microstructure and thus the optical and lasing properties of the ceramic samples. All the samples showed a good optical quality. The microstructure analysis and the laser tests showed that the vacuum pre-sintering temperature is the key factor determining the quality of the samples and the laser performances. The best values of slope efficiency i.e. η_L = 50 % and output power i.e. P_out = 6.62 W were obtained for the sample pre-sintered under vacuum at 1650 °C and hot isostatically pressed at 1800 °C.     

Microstructure and mechanical properties of hot-pressed SiC nanofiber reinforced SiC composites

This study reports on the preparation and mechanical properties of a novel SiC_nf/SiC composite. The single crystal SiC nanofiber(SiC_nf) reinforced SiC ceramic matrix composites (CMC) were successfully fabricated by hot pressing the mixture of β-SiC powders, SiC_nf and Al–B–C powder. The effects of SiC_nf mass fraction as well as the hot-pressing temperature on the microstructure and mechanical properties of SiC_nf/SiC CMC were systematically investigated. The results demonstrated that the 15 wt% SiC_nf/SiC CMC obtained by hot pressing (HP) at 1850 °C with 30 MPa for 60 min possessed the maximum flexural strength and fracture toughness of 678.2 MPa and 8.33 MPa m^1/2, respectively. The nanofibers pull out, nanofibers bridging and cracks deflection were found by scanning electron microscopy, which are believed can strengthen and toughen the SiC_nf/SiC CMC via consuming plenty of the fracture energy. Besides, although the relative density of the prepared SiC_nf/SiC CMC further increased with the sintering temperature rose to 1900 °C, the further coarsend composites grains results in the deterioration of the mechanical properties for the obtained composites compared to 1850 °C.     

Microstructures and mechanical properties of B4C-TiB2-SiC composites fabricated by ball milling and hot pressing

B₄C-TiB₂-SiC composites were fabricated via hot pressing using ball milled B₄C, TiB₂, and SiC powder mixtures as the starting materials. The impact of ball milling on the densification behaviors, mechanical properties, and microstructures of the ceramic composites were investigated. The results showed that the refinement of the powder mixtures and the removal of the oxide impurities played an important role in the improvement of densification and properties. Moreover, the formation of the liquid phases during the sintering was deemed beneficial for densification. The typical values of relative density, hardness, bending strength, and fracture toughness of the composites reached 99.20%, 32.84?GPa, 858?MPa and 8.21?MPa?m^1/2, respectively. Crack deflection, crack bridging, crack branching, and microcracking were considered to be the potential toughening mechanisms in the composites. Furthermore, numerous nano-sized intergranular/intragranular phases and twin structures were observed in the B₄C-TiB₂-SiC composite.     

街面水电站混凝土面板堆石坝主要技术问题探讨

街面水电站拦河坝为混凝土面板堆石坝,在面板止水结构型式、面板防裂措施、上游面的施工方法、趾板开挖处理及趾板灌浆等方面,根据工程实际情况,结合国内外的新技术新工艺进行了探讨。     

压电超声微电机混合结构定子的固有频率特性分析

压电超声微电机是依靠定子振动变换能的功率器件，定子性能将直接关系到微电机能否实现，本文采用Ｒａｙｌｅｉｇｈ－Ｒｉｔｚ方法来分析机械中经常采用的多层膜结构（混合结构）定子的固有振动特性，推导中考虑了平面应力和弯曲应力对固有频率的影响，模拟计算和实验结果符合得较好，此外还讨论了定子有关参数对固有频率的影响。     

Ф16mm、Ф18mm钼棒的研制

采用等静压制法，压制钼圆棒坯，经中频高温烧结，制得尺寸适合、用户满意的钼电极棒。     

炸药压装爆炸事故剖析

文中依据压爆事故的实例，对其产生的原因做了剖析，在剖析的基础上对压爆机理做了简要的阐述并提出了相应的预防措施。     

Recovery retardation in equal channel angular pressed Al–Zr alloy during friction stir welding

The effect of Zr on reduction of hardness and microstructure in an FS weld of equal channel angular-pressed Al alloy was investigated. Zr addition to Al suppressed dynamic recovery in the thermomechanically affected zone and enabled retention of the high hardness of the ECA-pressed material throughout the weld.     