06NiCuCrMoNb钢高温加热时表层铜的行为

将06NiCuCrMoNb钢试样在不同的加热温度保温不同时间后，观察并分析试样表层的形貌和成分。结果表明，在一定条件下铜会扩散进入表层奥氏体晶界，得到沿奥氏体晶界分布的富铜相，并在热变形加工时导致热脆。试验得到了沿奥氏体晶界分布的富铜相与加热温度和保温时间的关系。     

Inverse Analysis of Axisymmetrical Compression of HSLA Steel

The objective of the present work is to further explore the problem of selection of the flow stress function which will give the best agreement with experiments for a wide range of the Zener‐Hollomon parameter. Analysis of various flow stress functions was performed, with particular emphasis on the Zerilli‐Armstrong model. Inverse analysis was successfully applied to identify the flow stress model for microalloyed steels deformed in ferrite, two‐phase and austenite regions. Inverse method is applied to interpret the results of the axisymmetrical compression tests performed for HSLA steel samples on a Gleeble 3800 and Split Hopkinson Pressure Bar. Sensitivity analysis is performed based on local and global methods. The objective of the sensitivity analysis in the present study is the evaluation to what extent the selected coefficients in the rheological model influence the result of simulations. In the considered tests this result is represented by two dependent variables, the load and the shape of the sample (barrelling). It is confirmed that the Zerilli‐Armstrong equations should be applied at very high strain rates. Physical meaning is an advantage of this model. Difficulties with identification are the main disadvantage.     

不同弛豫时间下低合金高强度钢的组织和拉伸性能

研究了低合金高强度钢在不同弛豫时间下的组织和拉伸性能。结果表明：在适当的弛豫时间下。能进一步提高材料的屈服强度和抗拉强度。     

一种Cr—Mn—Mo—B低碳低合金钢的热变形行为

利用ＴＨＥＲＭＣＭＡＳＴＯＲ－Ｚ热处理机对一种Ｃｒ－Ｍｎ－Ｍｏ－Ｂ钢的热变形行为进行了研究，绘制了真应力－应变曲线，得到了各变形工艺参数之间的定量关系，得出试验用钢的Ｑ值为３７３．７ｋｊ／ｍｏｌ。在此基础上给出了试验用钢的动态再结晶图，试验发现，试验用钢９００℃以上变形后，在奥氏体区冷过程中发生静态再结晶与晶粒长大，相变前晶粒尺寸与变形条件Ｚ的关系：ｄｒｅｃ＝２．８８×１０＾４×Ｚ＾－０．２０５。     

高强度低合金铌钒钢板的失效分析

针对高强度低合金铌钒钢板在拉伸试验后出现分层开裂的现象,采用SEM、EDAX进行微观分析,发现试样内部有大量夹杂物存在,这些夹杂物主要含有钙、氧、硫、锰等元素。带有缺陷的钢板若应用到实际工程中,会影响铁塔的寿命。     

工程机械用800MPa低合金高强度钢焊接接头断裂韧性评价

对调质状态800MPa低合金高强度钢及其焊接接头进行了系列温度的断裂韧性测试,讨论不同焊接方法对焊接接头断裂韧性的影响。发现板材的轧制方向对断裂韧性影响显著,LT方向试件的断裂韧性远超过TL方向试件的断裂韧性。在-60℃以上,母材处于上平台延性断裂范畴。在-80℃,裂纹扩展过程中有延脆断裂模式的转变。焊条电弧焊焊缝的断裂韧性与气体保护焊焊缝的断裂韧性相当。尽管常温下焊缝金属的断裂韧性甚至优于母材,但随着试验温度的降低,焊缝金属的断裂韧性迅速下降。在-20℃已发生断裂模式转变,这在结构服役时要引起重视。本研究为大型工程机械的断裂安全评定奠定了基础。     

Effect of nitrogen and vanadium on austenite grain growth kinetics of a low alloy steel

Austenite grain growth kinetics in a steel containing 0.4% C, 1.8% Cr with different nitrogen contents (in the range 0.0038–0.0412%) and a micralloying addition of 0.078% V were investigated. The investigations were carried out in an austenitising temperature range of 840–1200 °C for 30 min. The results of investigations showed that N promotes the grain growth of austenite. The microalloying addition of vanadium protects the austenite grain growth because of carbonitride V(C,N) precipitation and the grain boundary pinning effect of undissolved particles of V(C,N). Using a thermodynamic model, the carbonitride V(C,N) content, undissolved at the austenitising temperature was calculated. At temperatures when a coarsening and dissolution of carbonitride occurs, the austenite grains start to growth. The effect of nitrogen on the type of chord length distribution of austenite grains was analysed.     

80 t UHP DC EAF-LF-CC工艺生产Q390B低合金高强度钢的实践

杭钢用80 t UHP DC电弧炉-钢包炉(LF)-200 mm×200 mm连铸及700×1/650×3轧机轧制,生产直径75 mm的Q390B低合金高强度圆钢.LF精炼时控制(%)0.16～0.19C,1.35～1.52Mn,0.03～0.05V,≤0.025S,≤0.025P,喂CaSi线并全程吹氩,连铸采用长水口保护浇注.检验结果表明,钢材具有良好的表面质量、低倍组织,夹杂物≤2.0级,钢的σs 380～465 MPa,σb 545～625 MPa,δ 22.0%～28.5%,AK 98～210 J.     

高强度低合金中宽热轧钢带的研制

分析了高强度低合金钢的性能要求,论述了其成分设计基本思路,介绍了工艺流程和产品实物质量,讨论了新产品高强度与高韧性的匹配和焊接性能等问题.     

TEM Investigations of Fine Niobium Precipitates in HSLA Steel

Commercially produced 0.03 % C, 0.08 % Nb, 0.01 % Ti high strength low alloyed (HSLA) steel in the form of 20 mm thick plates was investigated. The steel was thermomechanically processed and the mechanical properties of the steel were evaluated by tensile testing. Using analytical and high resolution transmission electron microscopy the distribution, morphology, composition, crystal structure and particle size of niobium and titanium carbonitrides were observed and identified in these steels. The distribution of the precipitates was found to be nearly random, with occasional occurrence of precipitation free zones. Complex agglomerates with a cubic TiN seed crystal overgrown by a cubic NbC particle were the most commonly observed precipitates. Further TEM analysis in the accelerated cooled and tempered specimens in 1/4 plate thickness did not reveal any evidence that additional precipitation in the ferrite occurred. Precipitation in ferrite was only detected after subsequent cold deformation and tempering of the same samples. By a combination of EFTEM, STEM, HRTEM in addition to EDX spectroscopy, a large population of strain induced NbC precipitates with fcc crystal structure ranging in size down to 2 nm were identified in the ferrite matrix.