DP980+Z烘烤硬化值与退火温度的关系

摘要：为了研究退火温度对镀锌DP980+Z烘烤硬化值的影响，退火温度控制在760～820℃之间，系统分析退火温度对烘烤硬化值的影响。通过准静态拉伸试验机测量烘烤硬化值及抗拉强度，采用lepara试剂对组织中的马氏体进行着色，利用金相显微镜及图像处理软件测量马氏体的体积分数；采用扫描电镜观察DP980+Z的双相组织特点，并且将组织图片通过CAD转化成有限元图进行网格划分，建立代表性体积单元（RVE），通过有限元分析铁素体、马氏体强度对烘烤硬化值的影响。在同样的变形量情况下，DP980+Z的原始屈服强度越高，烘烤硬化值越高。     

In situ formation of multi scale reinforcing phases to improve performance of Al2O3-SiC C castables

In order to improve the physical properties and slag corrosion resistance of refractory materials for hot metal pretreatment, different contents of composite metal powders (CMP) were introduced into Al2O3-SiC-C refractory castables. The effect of CMP on the microstructure, physical properties and slag corrosion resistance of Al2O3-SiC-C refractory castables were studied. The results show that the multi scale reinforcing phases including flake crystals, rod shaped fibers, filamentous fibers and whiskers are in situ formed in the samples with addition of CMP, which result to the improvement of the cold modulus of rupture and cold crushing strength. When the addition of CMP is 6 wt.%, the high temperature modulus of rupture increases by 231%, the thermal shock resistance increases by 77% after thermal shock by water cooling 5 times and the percentage of the slag resistant area reduces by 37.2%.     

Research and application of automatic control system of argon blowing at ladle shroud

Argon blowing at the ladle shroud requires the best flow control strategy to effectively avoid the secondary oxidation of molten steel, slag entrapment and heat loss during the casting of the tundish, and at the same time, give full play to the role of bubbles to remove inclusions. Therefore, an automatic control system for argon blowing at the ladle shroud was proposed. The data collected by S7-300PLC and software programming were used to adjust the argon blowing flow online in real time according to factors such as pouring and continuous pouring. On this basis, PID control algorithm and closed loop control mechanism were used for real time adjustment. The flow control valve ensures theminimum deviation between the actual value of the flow and the set value. The production data of this system in the first quarter of 2021 in a special steel plant show that the proportion of furnaces with an acid soluble aluminum (Als) loss percentage of less than 10% of each steel grade has increased by 5.52%, and the proportion of furnaces with an Als loss percentage of more than 60% has increased from 1% decrease to 0. The actual application results show that the use of the system improves the surface quality of the continuous casting slab and the performance of the final product.     

Effect of partitioning on microstructure and properties of a medium carbon Ti Mo bearing high strength Q&P steel

In order to investigate the effect of partitioning procedures on microstructure and properties of a medium carbon Ti Mo bearing steel, the salt bath experiment, field emission SEM, TEM and tensile tests as well as wear tests were utilized to clarify the microstructural evolution and property changes treated by different partitioning parameters. The results show that the microstructures consist of tempered lath martensite, cementite and (Ti, Mo)C particles. With prolonging partitioning time or increasing partitioning temperature, the amount of laths martensite decreases and thicker martensite plates with blunt boundaries appear. In addition, with increasing partitioning temperature from 310℃ to 400℃, the tensile strength, hardness and low temperature toughness are simultaneously decreased, and the reduction reaches up to about 300MPa, 100HV and 20J, respectively. Finally, the wear performance of the samples partitioned below Ms is obviously better than that of samples partitioned above Ms. The morphology of worn surface of samples partitioned below Ms is characterized by plastic fatigue morphology, while the worn surfaces of samples partitioned above Ms are mainly dominated by grooves.     

直升机发动机超转实验系统的测频设计

本文采用FPGA技术测量直升机发动机转速,介绍了双通道等精度测频的原理,设计了信号调理电路,并在FPGA上设计了Verilog代码,在实际应用中测量直升机发动机转速表现了良好的系统实时性能。     

计算机数据安全存储技术及应用

数据安全是计算机安全问题的核心,对于很多具有高度保密要求的单位,安全地存储重要数据,并且在不需要这些数据时作彻底销毁不被他人恢复是至关重要的。本文详细介绍了数据安全存储技术的发展现状,并结合典型的企业信息安全防护体系设计进一步阐述了如何为具有一定保密要求的部门建立可靠的数据安全防护系统。此外,本文从数据存储和销毁的原理上进行了详细分析,并给出了应用软件及案例的测试说明,提出了安全销毁数据的详细解决方法。     

物联网智能家居系统的研究与设计

智能家居有广阔的应用前景.针对传统家居控制上的缺陷,采用B/S架构设计了智能家居管理系统,采用ZigBee无线网络实现对各类家居设备的信息采集和指令控制.用SQL Server 2005数据库管理系统与家庭网关,进行数据的传递与接收.通过Web浏览器,用户可以实现对智能家居系统的管理.     

焦粉粒度对烧结混合料制粒的影响

摘要：研究了焦粉粒度对烧结混合料制粒的影响,包括焦粉在制粒小球中的分布规律与混合料制粒效果。结果表明：粒度小于0.5mm焦粉主要起黏附粉作用,较为均匀地黏附到各粒级制粒小球中;粒度在0.5~1mm的焦粉作为核颗粒,分布在0.5~1mm、1~3mm制粒小球中的占比总和为81.3%,部分以共核形式存在于3~5mm及以上粒级的制粒小球中;粒度在1~3mm及以上粒级焦粉作为核颗粒分布于相同粒级与大一粒级的制粒小球中;粒度在1~3mm及以上粒级焦粉对烧结混合料制粒无明显影响,粒度小于1mm的焦粉会提高制粒后混合料中小粒径制粒小球的含量,不利于混合料制粒,应尽可能减少焦粉中粒度在05~1mm的含量,将焦粉中粒度小于0.5mm的质量分数控制在20%~30%。     

球团链箅机回转窑工艺中氯和硫元素迁移规律

摘要：对链箅机回转窑工艺中各段球团样品进行实验分析,研究了氯元素和硫元素在链箅机回转窑工艺中的迁移规律,明晰了烟气中HCl的生成机制。结果表明,球团原料中的氯元素主要是以NaCl的形式存在,氯元素有一部分在链箅机抽风干燥段会转变成HCl气体并进入烟气,一部分在链箅机预热Ⅱ段之后以NaCl的形式汽化进入烟气,剩余的氯元素仍以NaCl的形式存在于成品球团矿中。烟气中的HCl气体是在抽风干燥段,由富含SO2的烟气与含水球团料层中的NaCl发生反应生成的,烟气中SO2转变成Na2SO4重新固定于料层中。在预热Ⅰ段和预热Ⅱ段,烟气中的SO2与原料中碳酸钙分解生成的游离CaO反应生成CaSO4,也会重新固定烟气中的SO2。     

旋转电极电渣重熔过程电极熔速的理论解析

摘要：旋转电极电渣重熔通过改变结晶器内熔体的流动和传热规律,增强了渣池与电极间的对流换热,在提高电极熔化速率和生产效率方面具有巨大潜力。提出了电渣重熔过程电极熔化速率的求解方法,并考虑了电极旋转时的强制对流,基于多物理场耦合模型预测了电极直径、转速对电极熔化速率的影响规律。结果表明,随着转速提高,金属液滴由从电极中心滴落向电极边缘滴落转变,高温区由渣池外侧向渣池中心移动。当转速从0增大至90r/min,55mm直径电极的熔化速率从7.90g/s增大至9.68g/s,对比固定电极,转速为90r/min时,生产效率最多提高了22.5%;进一步增大转速,电极熔化速率反而减小。存在一个最佳转速可使熔化速率达到最大,且该最佳转速随着电极直径的增大而减小。