Microstructure and properties of cutting magnesium-brass containing no lead

1 INTRODUCTIONLead-brass has excellent cutting ability , me-chanical and physical properties and is one of themost widely used copper alloys . The occupationratio of brass tube to all kinds of tubes reaches90 % in developed countries . The cutting lead-brass is a dual-phase brass and fine lead particlesdistribute dispersivelyin grains and on grain boun-ries . Theleadin wasted brass can easily beleachedand dissolvedinto soil .If the wasted lead-brass isburned in air ,the lead will become p…     

黄铜中纳米级微裂纹的形核与钝化

黄铜薄膜试样在透射电镜中原位拉伸观察表明，在平衡条件下加载裂发出的位错纯化成无位错区，它是一个应变很高的异常弹性区。当缺口足够锐，外加载荷足够大时，这个非线弹性区中的应力有可能达到原子键合力，从而使纳米级微裂纹在无位错区中不连续形核，或从钝化的原裂纹顶端形核。这个微裂纹一昊形核，即使保持恒位移，也将钝化成空洞或缺口。     

浅析胶料与镀铜钢丝帘线粘合的影响因素

采用正交设计法和对比试验法，考察了硫黄、氧化锌、促进剂、炭黑以及某些工艺条件对胶料与镀铜钢丝帘线粘合力的影响。结果表明，硫黄品种对粘合力的影响不大；氧化锌用量增大，粘合力增大；用１．０份促进剂ＣＺ时的粘合力大于用１．３份促进剂ＤＺ；使用高结构炭黑可增大粘合力；胶料的混炼方法和硫化时间对粘合力的影响较大。     

Electrochemical anticorrosion performance evaluation of Al2O3 coatings deposited by MOCVD on an industrial brass substrate

Alumina (Al₂O₃) coatings of different thickness were deposited on OT59 brass substrate (BS) using the metal organic chemical vapour deposition (MOCVD) technique to evaluate the corrosion performance by EIS measurements. The used precursor was dimethyl-aluminium-isopropoxide. Electrochemical characterizations of the deposited films were performed in a standard very aggressive acidic solution (aerated 1N H₂SO₄ at 25 °C up to 168 h of immersion time) by means of direct current method (Tafel curves) and electrochemical impedance spectroscopy (EIS). The Rutherford backscattering spectroscopy (RBS) indicated that the films are very pure with the correct Al₂O₃ stoichiometry, while the IR absorption spectra showed that the films did not contain any OH groups. The surface film morphology was investigated by atomic force microscopy (AFM) and displayed a globular texture. The films were very smooth, with a maximum root mean square roughness, for example, of 14 nm for a 0.96 μm thick coating. The EIS data confirmed, as expected, that a 2.40 μm Al₂O₃ layer ensures the best corrosion protection after 168 h of immersion in the very acidic environment used.     

稀土硼锆在HPb59-1黄铜中的细化变质效果

研究了微量稀土、硼、锆对HPb59-1合金的细化变质作用.结果表明:0.0001%～0.001%的硼具有显著细化变质效果;0.03%～0.05%稀土也能消除铸态柱状晶,但细化晶粒能力远小于微量硼;微量锆细化变质效果不明显.高温(680℃×40min)组织显示,稀土、锆及过量硼的添加,均提高合金α→β转变温度,从而影响热加工性能.     

微量硼在HPb59-1黄铜中的细化变质作用

研究了微量硼对HPb59-1合金的细化变质作用。结果表明:0.0001%￣0.0010%的硼具有显著细化变质效果,使发达的柱状晶转化为30￣50μm的等轴晶;高温(680℃×40min)组织显示,微量硼的铸态细化变质组织在高温有较好的热稳定性,对α→β转变影响较小。但过量硼的添加,将减缓α→β转变,提高转变温度,从而影响热加工性能,为此,硼添加量应小于0.001%。     

黄铜热变形流动应力的实验研究

采用恒变形率凸轮压缩试验机对５个黄铜品种的热变形流动应力进行了实验研究，分析了变形温度，变形速率，变形程度对流动应力的影响，同时对不同的数学模型结构形式进行了非线性回归，通过分析比较提出了拟合精度较高的流动应力数学模型．     

冷变形管材残余应力测试与分析

用电阻应变片法测试了变形锡黄铜ＨＳｎ７０－１管材表面的残余应力，分析了拉拔管材变形参数对管材表面残余应力及其他性能指标的影响规律，结果表明，增大管材的减壁变形，可以显著地减小管材表面的拉伸残余应力，当减壁比ｔ０／ｔ１大于１．２时，拉拔管材的残余应力较小，经成品退火后管材晶粒组织细小，采用不同型变形方法生产的管材，其表面残余应力也遵循这一规律，２辊冷轧管材有很大的减壁变形，其表面产生了很大的压应力，     

冷拔无铅含Bi易切削黄铜的研究

研究用连铸-挤压-冷拔的组合工艺生产一种含Bi的易切削黄铜棒，并用光学显微镜和X射线研究了该黄铜的显微组织，用拉伸试验机测定了该黄铜的抗拉强度和塑性。研究发现，该黄铜主要由α（Cu0.64Zn0.36）、β（CnZn）两相组成，Bi以单质的形式分布在晶界和相界上。冷拔使该黄铜强度增加（大于600MPa），塑性下降5％～9％。该黄铜完全可以取代现行的HPb59-1黄铜。     

熔铸-扩散法制备黄铜/钨铜功能梯度材料的研究

对用熔铸-扩散法制备的黄铜，钨铜功能梯度材料进行了研究，对界面区域的元素成分分布和微观组织结构进行了分析，对界面区域的电导率、结合强度及抗脉冲大电流损伤性能进行了测试。结果表明：用该法制备的黄铜，钨铜功能梯度材料，界面区域由成分和组织渐变的三层结构组成；电导率在界面区域呈渐变分布趋势，没有出现电导率突变现象；这种结构缓解了因热性能不匹配而造成的热应力，提高了黄铜与钨铜合金的结合强度；界面的抗脉冲大电流损伤性能良好。