Separation of hematite from banded hematite jasper (BHJ) by magnetic coating

The separation of iron oxide from banded hematite jasper(BHJ) assaying 47.8% Fe, 25.6% Si O2 and 2.30%Al2O3 using selective magnetic coating was studied. Characterization studies of the low grade ore indicate that besides hematite and goethite,jasper, a microcrystalline form of quartzite, is the major impurity associated with this ore. Beneficiation by conventional magnetic separation technique could yield a magnetic concentrate containing 60.8% Fe with 51% Fe recovery. In order to enhance the recovery of the iron oxide minerals, fine magnetite, colloidal magnetite and oleate colloidal magnetite were used as the coating material. When subjected to magnetic separation, the coated ore produces an iron concentrate containing 60.2% Fe with an enhanced recovery of56%. The AFM studies indicate that the coagulation of hematite particles with the oleate colloidal magnetite facilitates the higher recovery of iron particles from the low grade BHJ iron ore under appropriate conditions.     

Al2O3在钒钛烧结矿中的行为研究

针对攀钢钒钛烧结矿Al2O3含量高的情况，在实验室对Al2O3在钒钛烧结矿中的行为进行了试验研究，结果表明，Al2O3含量增加对钒钛烧结矿的产量，质量有不利影响，钒钛烧结矿中的Al2O3主要以固溶体形式贮存于除钙钛矿外的其他矿物相，它对烧结矿的矿物组成和结构有较大的影响。     

某硅线石矿石选别中除铁研究

针对矿石中硅线石微细嵌布，铁矿物嵌布亦较细。且有近二分之一铁在非金属矿物晶格之中，除铁难的特点，通过试验研究对比采用一段磨矿磁选除铁后磁尾浮选富集硅线石．浮选精矿再磨后酸浸再除铁的工艺方法，获得了理想的除铁效果，使硅线石精矿质量达到较高品质。     

Effect of Aminated Chitosan-Coated Fe3O4 Nanoparticles with Applicational Potential in Nanomedicine on DPPG,DSPC, and POPC Langmuir Monolayers as Cell Membrane Models

An adsorption process of magnetite nanoparticles functionalized with aminated chitosan (Fe₃O₄-AChit) showing application potential in nanomedicine into cell membrane models was studied. The cell membrane models were formed using a Langmuir technique from three selected phospholipids with different polar head-groups as well as length and carbon saturation of alkyl chains. The research presented in this work reveals the existence of membrane model composition-dependent regulation of phospholipid-nanoparticle interactions. The influence of the positively charged Fe₃O₄-AChit nanoparticles on a Langmuir film stability, phase state, and textures is much greater in the case of these formed by negatively charged 1,2-dipalmitoyl-sn-glycero-3-phospho-rac-(1-glycerol) (DPPG) than those created by zwitterionic 1,2-distearoyl-sn-glycero-3-phosphocholine (DSPC) and 2-oleoyl-1-palmitoyl-sn-glycero-3-phosphocholine (POPC). The adsorption kinetics recorded during penetration experiments show that this effect is caused by the strongest adsorption of the investigated nanoparticles into the DPPG monolayer driven very likely by the electrostatic attraction. The differences in the adsorption strength of the Fe₃O₄-AChit nanoparticles into the Langmuir films formed by the phosphatidylcholines were also observed. The nanoparticles adsorbed more easily into more loosely packed POPC monolayer.     

Selective leaching of vanadium from V-Ti magnetite concentrates by pellet calcification roasting-H_2SO_4 leaching process

A novel method of pellet calcification roasting-H_2 SO_4 leaching was proposed to efficiently separate and extract vanadium(V) from vanadium-titanium(V-Ti) magnetite concentrates.The leaching rate of V is as high as 88.98%,while the leaching rate of impurity iron is only 1.79%.Moreover,the leached pellets can be used as raw materials for blast furnace ironmaking after secondary roasting.X-ray photoelectron spectroscopy(XPS) and scanning electron microscopy with energy dispersive X-ray spectrometry(SEMEDS) analyses showed that V~(3+) was oxidized to V~(5+) after roasting at 1200℃,and V~(5+) was then leached by H_2 SO_4.X-ray diffraction(XRD) analyses and single factor experiment revealed a minimal amount of dissolved Fe_2 O_3 during H_2 SO_4 leaching.Therefore,a high separation degree of V and iron(Fe) from V-Ti magnetite concentrate was achieved through H_2 SO_4 leaching.Compared with the traditional roastingleaching process,this process can achieve a high selectivity of V and Fe,and has excellent prospects for industrial production.     

米糠-硫酸直接浸锰工艺条件研究

以米糠及湘西软锰矿为原料,对米糠-硫酸直接浸锰制备硫酸锰的工艺条件进行了研究。结果表明,米糠-硫酸法浸锰的最佳工艺条件为:浸锰温度250℃,硫酸质量分数50%,浸锰时间75min,米糠用量为软锰矿粉质量的20%,硫酸用量为其理论用量的110%。按该工艺条件浸锰,锰的浸出率可达95%以上。该工艺具有能耗少、生产成本低、锰的浸出率高等优点,为软锰矿的开发利用开辟了一条新途径。     

二氧化硫浸锰制备高纯碳酸锰

采用湘潭低品位的贫软锰矿为原料，对二氧化硫气体湿法浸锰、浸出液除杂、碳化结晶制备高纯碳酸锰的工艺进行了研究。实验得到二氧化硫浸锰的最佳工艺条件为：浸锰温度150～155℃，液固质量比3：1，二氧化硫体积分数6％～7％、流速1．5～2．0mL／min，浸锰时间3．0～3．5h。按该条件浸锰，锰的浸出率可达95％以上。该工艺为贫软锰矿的开发利用及有色金属冶炼厂二氧化硫废气的综合治理开辟了一条新途径。     

基于遥感和模糊数学的矿山地质环境综合评价研究-以红格钒钛磁铁矿区为例

利用IKONOS影像对红格钒钛磁铁矿区的矿山地质环境进行监测,结合实地调查资料,利用模糊数学综合评价法建立了研究区的评价指标体系,并对研究区矿山地质环境进行了综合评价。以研究区内5个规模较大的矿山为评价单元,得到白草铁矿、潘家田铁矿和小黑箐铁矿的矿山地质环境评价等级为Ⅰ(好),优于阳雀箐铁矿的Ⅱ(一般)和红格铁矿的Ⅲ(较差)。研究成果可为矿山地质环境评价、矿产资源合理开发及矿山生态环境综合整治等工作提供参考。