塔河油田奥陶系油气藏是大型碳酸盐岩溶洞型油气藏，其储渗空间主要为大小不同的溶洞、裂缝带、溶蚀孔隙等组成，该油气藏具有极强的非均质性，单纯用静态资料来认识这类油气藏是非常困难。文章提出利用生产动态资料和信息进行该类型油气藏研究的新思路，利用人工神经网络技术在处理非线性相关参数预测方面的优势，并以渗流理论为基础，结合试井成果，选用已知油井的产量、油嘴、油压、含水率、气油比、原油密度等6个开发动态参数作为样品输入数据，推导出影响油气藏开发的重要参数（地层系数）与生产信息的关系，建立了人工神经网络预测储层参数的结构模型。通过塔里木盆地塔河油气田实例研究，说明了利用动态信息评价油气藏技术在碳酸盐岩缝洞型油气藏储层预测和非均质性分析等方面具有较高的实用价值。     

Effects of Rare Earths on Toughness of 31Mn2SiRE Wear-Resistance Cast Steel

The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and network ferrite are eliminated, the dislocation density and the quantity of dislocated martensite are increased remarkably, and the shape and distribution of inclusions are improved by the addition of RE. Therefore, the mechanical properties of the modified steel can be greatly increased, especially the toughness (αK) by 44%, yield strength (σs) by 10%, and elongation (δ5) by 42%.     

Fast Positive Feedback Between the Adrenocortical Stress Response and a Brain Mechanism Involved in Aggressive Behavior.

Aggressive behavior induces an adrenocortical stress response, and sudden stressors often precipitate violent behavior. Experiments in rats revealed a fast, mutual, positive feedback between the adrenocortical stress response and a brain mechanism controlling aggression. Stimulation of the aggressive area in the hypothalamus rapidly activated the adrenocortical response, even in the absence of an opponent and fighting. Hypothalamic aggression, in turn, was rapidly facilitated by a corticosterone injection in rats in which the natural adrenocortical stress response was prevented by adrenalectomy. The rapidity of both effects points to a fast, mutual, positive feedback of the controlling mechanisms within the time frame of a single conflict. Such a mutual facilitation may contribute to the precipitation and escalation of violent behavior under stressful conditions. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

miPP/ziPP共混体系的流动性能

首次对茂金属聚丙烯(miPP)／齐格勒-纳塔聚丙烯(ziPP)共混体系的流动性进行了系统的研究。研究发现，在miPP／ziPP共混体系中，miPP含量的变化改变了共混体系的相结构，这种相结构会随着温度和剪切速率的变化而产生明显的变化，从而改变了体系的流动性能，且该共混体系在不同剪切速率下的流动曲线可以分别通过两个模型进行模拟。     

行政行为的概念及构成要素

行政法学的研究应该尽量放宽视角,适应将来法治建设的需要。我们必须把行政行为的概念放到整个法治体系中甚至整个社会的发展中去研究。     

Mechanical properties of polyethylene mixtures crystallized under high pressure

The mechanical properties of a medium molecular weight polyethylene (MMW‐PE) and an ultrahigh molecular weight PE (UHMW‐PE) binary mixture with different weight fractions crystallized from the melt at 0.1 and 450 MPa were studied. The tensile modulus, yield stress, and strain were obtained as a function of the weight fractions in the PE mixtures at 25 and 85°C. The tensile modulus in the sample crystallized at 0.1 MPa decreased from 1.5 GPa of pure MMW‐PE to about 0.4 GPa of pure UHMW‐PE with the UHMW‐PE content but it did not decrease with the UHMW‐PE in the sample crystallized at 450 MPa in testing at 25°C. A decreasing rate of the storage modulus E′ of UHMW‐PE in a dynamic measurement for the sample crystallized at 0.1 MPa with the temperature is larger than that of the sample crystallized at 450 MPa. These experimental facts are interpreted in relation to the molecular motion and crystallinity of the sample. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1962–1968, 2003     

机械合金化Fe-Ni粉末的相结构

使用XRD和Moessbauer等方法，研究了在Ar气氛下机械合金化Fe—Ni粉末相结构的变化．结果表明，在机械合金化Fe64-Ni36粉末过程中，fcc相的数量随着球磨时间的增加先增加然后减少，与加乙醇球磨Fe64-Ni36的情形相同．当Ni的含量(原子分数)大于50％时，有fcc相、顺磁相和FeNi3形成，当Ni的含量低于50％时，bcc相的数量随着Ni含量减少而增加．Moessbauer谱的结果表明，因球磨时间或Fe、Ni比例的不同，Fe—Ni球磨粉末固溶体具有不同结构的原子配比。     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

具有阻力特性材料的σ_f－σ关系及一种新的阻力曲线测定方法

通过对相变增韧陶瓷及一种可切削玻璃－陶瓷动态疲劳（恒应力速率）试验中高应力速率区断裂应力下降现象的理论分析，发现这种现象与材料的阻力特性（Ｒ－ｃｕｒｖｅ）密切相关。确立的σ_ｆ－σ理论关系能够很好地描述整个应力速率区间内的动态疲劳试验结果。高应力速率区σ_ｆ－σ在双对数坐标下为负斜率直线，直线斜率为（ｍ为阻力曲线ＫＲ＝ｋ（△ａ）~ｍ的指数），断裂主要由材料阻力行为控制；低应力速率区，σ_ｆ－σ在双对数坐标下为正斜率直线，直线斜率为　（ｎ为应力腐蚀指数），断裂主要由材料应力腐蚀行为控制。建立了测定材料阻力特性的一种新方法，分别用这种方法及压痕／弯曲方法对一种可切削玻璃－陶瓷的阻力特性进行了实验测定，两种方法所得结果有很好的一致性。     

Processing of Yttria-Alumina Coated Silicon Nitride Slips by Slip Casting

Si₃N₄powders coated with 6 wt% Y₂O₃and 4 wt% Al₂O₃were prepared by coprecipitation. The resulting powders were dispersed in water at different pH values and with addition of various amounts of ammonium polyacrylate (NH₄PA) to produce 32 vol% slips. The influence of the amount of NH₄PA solution added and pH on the rheological properties of 32 vol% coated Si₃N₄slips were studied. In addition, the sintered density of cast samples was determined and related to the degree of slip dispersion. The adsorption of the NH₄PA on the coated particle surface was rather high and the surface became saturated near 0.86 mg/m²at pH 9.2. High NH₄PA concentrations (1.7–3 wt%) were necessary to obtain well dispersed 32 vol% coated Si₃N₄slips at pH 9.2. The best stabilization was obtained with the addition of 2.3 wt% NH₄PA; in this condition, the viscosity reached a minimum value of 35 mPa.s at 100 s^–1. The slip viscosity increased with increasing pH from 9.2 to 10.2. Slips with low viscosities gave a more dense packing of cast samples and consequently higher sintered density values.