Effects of solvent and temperature on the coupling agent/epoxy resin interface

Increased wetting of the coupling agent/epoxy resin interface was observed when γ-glycidoxypropyltrimethoxysilane, polyfunctional aminosilane and γ-aminopropyltriethoxysilane were applied respectively from methyllethylketone, dimethylformamide and water on woven glass cloths which had been cleaned at 300°C. However, when factory-applied coupling agents were burnt off the woven cloths and fresh coupling agents re-applied, it was found that the nature of the factory-applied coupling agent influenced subsequent wetting. Thinner glass fibres showed a greater improvement in wetting rate than thicker fibres in those solvents identified to be good for improved wettability, irrespective of the heat-cleaning temperature.     

JOINING MECHANISMS OF β''''-Al2O3 CERAMIC AND PYREX GLASS TO Al MATRIX COMPOSITE

The bonding of β'-Al2O3 and pyrex glass to Al matrix composites by anodic bonding process is achieved. The microstructure of the bonded interface and the joining mechanisms are analyzed with scanning electron microscope (SEM), energy dispersive X-ray fluorescence spectrometer (EDX). It is observed that the bonding region across the interface consists of the metal layer, oxide transitional layer and the ceramic layer, with the transitional layer composed of surface region and sub-surface region. The bonding process can mainly be categorized into anodic bonding process and solid state diffusing process. The pile-up of the ions and its drift in the interface area are the main reasons for anode oxidation and joining of the interface. The temperature, voltage and the drift ions in the ceramic or glass during the bonding process are the essential conditions to solid state diffusing and oxide bonding at the interface. The voltages, temperature, pressure as well as the surface state are the main factors that influence the anodic bonding.     

Fluorine analysis of nuclear waste glasses

A method for analyzing the fluorine content of glass using a microwave oven to digest the glass is presented. Analysis time and secondary waste generation are reduced using this method, without sacrificing accuracy.     

Dynamics of hydrated iron(II) cations in nafion polymer membranes

Mössbauer studies of Fe²⁺ in water-soaked nafion polymer membranes in the temperature range between 90 K and 250 K have been performed. Above a critical temperature (～ 180 K) the spectra exhibit both elastic narrow absorption lines and quasielastic broad lines. These spectra are typical of bounded diffusion phenomena observed by Mössbauer spectroscopy in macromolecular systems like haemoglobin, myoglobin and ferritin. Similar spectral shapes have been observed by quasielastic neutron scattering from water in nafion membranes. Within 50 K above the critical temperature the total Mössbauer absorption area decreases by an order of magnitude whereas the narrow absorption line decreases by two orders of magnitude. The results are interpreted in terms of bounded diffusive motion of the iron. Using a model based on overdamped harmonically bound Brownian motion, the essential parameters of the iron motion can be derived as a function of temperature. The iron motion most probably reflects the motion of a large Fe²⁺ complex, e.g. Fe(H₂O)²⁺₆, which is attached to the polymer side chains via the sulphonic group.     

改性玻纤增强尼龙610,1010塑料

研究了采用(准)中粘度级尼龙做基体树脂,加入成核剂改善尼龙的结晶过程,提高结晶速率和初始熔融温度;添加光、热氧稳定剂,防止尼龙在成型加工和使用过程中产生降解与老化,提高塑料制品的质量和减少性能的分散性;采用合理的工艺条件,确保添加剂的均匀分散与减少玻纤的磨损,得到适于军工、航空和机电等领域需要的高性能的受力结构工程塑料。     

锆钡镧铝氟化物玻璃的分相研究

本文综述了氟化物玻璃中的分相研究。在前人研究基础上应用透射电镜，X射线能谱，电子能量损失谱及X射线衍射，差热分析等研究了锆钡镧铝氟化物玻璃中的液-液分相，发现此种现象普遍存在于该类玻璃之中。对玻璃成分与分相形貌及微观结构之间的关系、对析出晶相种类及分相与析晶的相互影响进行了研究。提出欲降低氟化物玻璃的光损耗，分相与析晶一样是不容忽视的因素。     

Role of Specimen Geometry in the Effect of Fiber Orientation on the Thermal Conductivity of a Uniaxial Carbon-Fiber-Reinforced Aluminoborosilicate Glass-Matrix Composite

A study concerning the effect of fiber orientation on the thermal conductivity of a uniaxial carbon-fiber-reinforced borosilicate glass was conducted. For thin specimens, and thick specimens with specimen sides cut parallel to the fiber direction, the dependence of thermal conductivity on fiber orientation showed excellent agreement with theoretical behavior predicted for a composite infinite in extent. In contrast, the thermal conductivity data for rectangular thick specimens fell well below the data for the thin and angled specimens. For fiber orientation of 45° and higher, at which the heat was directed toward the side of the specimen rather than across, the thermal conductivity values showed excellent agreement with theoretical behavior predicted for a finite composite strip with insulated sides.     

Microstructural investigation of long-term degradation mechanisms in GFRP dowel bars for jointed concrete pavement

Steel dowel bar is used to transfer loads in concrete pavement slab. However, once the steel dowel bar corrodes, it may cause faults, such as joint freezing in concrete pavement, level differences resulting from spalling or decreased efficiency of load transfer, etc., which are the same problems experienced by typical reinforcing steel. This study evaluated the applicability of glass fiber-reinforced polymer (GFRP) dowel bar as a substitute for steel dowel bar. A microstructural analysis was conducted to examine the decrease in durability of GFRP dowel bar exposed to deterioration environments. To analyze the deterioration mechanism of GFRP dowel bar, scanning electron microscopy was employed and the porosity was measured by the gas absorption method. It was concluded that the longer the GFRP dowel bar was exposed to deterioration environments, the more the interlaminar shear stress decreased. This result was validated by the microstructural analysis. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008