聚酯新型催化剂乙二醇锑的工业应用

介绍了国产新型催化剂惭二醇锑在洛阳石油化工总厂聚酯装置上的使用情况，结果表明：乙二醇锑催化剂活性高、易溶解；以乙二醇锑催化剂合成的聚酯产品质量稳定，纺丝时的加工性能明显得到改善。     

EO/EG装置生产过程中有机酸的生成原因分析

分析了环氧乙烷，乙二醇装置工艺系统中有机酸生成的原因．指出在银催化剂作用下，乙烯氧化过程有机酸生成主要成分是甲酸和乙酸，银催化剂不是影响氧化反应器出口醛含量的主要因素；杂质、温度等对反应器出口气中的醛含量有重要影响，也直接影响到装置前系统的有机酸含量；乙二醇后系统中有机酸的增加仅取决于两级吸收及解析工艺的稳定操作。     

Influence of expandable graphite on fire resistance and water resistance of flame-retardant coatings

Expandable graphite (EG) coating and ammonium polyphosphate-pentaerythritol-melamine (APP-PER-MEL) coating were prepared. Thermal degradation and char formation of the coatings were investigated by differential thermal analysis (DTA), thermogravimetry (TG), X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The results have shown that the anti-oxidation and fire-resistant properties of expandable graphite coating containing EG with size of 74 μm are better than those of APP-PER-MEL coating. The static immersion test was applied to study water resistance of the coatings, and the fire protection test and mechanical test were used to analyse heat insulation and mechanical properties of coatings before and after water immersion. The fire-resistant and mechanical properties of APP-PER-MEL coating were severely damaged by water immersion, whereas EG coating containing 8.5% EG with size of 74 μm could retain the good fire resistance even after 500 h water immersion.     

降低湿法MD-240树脂的材料成本

通过调整聚氨酯树脂的生产配方,用乙二醇和/或聚乙二醇取代1,4-丁二醇和己二酸合成的聚酯多元醇,充当聚酯树脂的柔性链段,同时,用乙二醇等相对分子质量低的二元醇取代1,4-丁二醇作扩链剂,从而减少1,4-丁二醇的用量,降低湿法MD-240树脂的材料成本。     

Polymer gel electrolytes prepared from P(EG‐co‐PG) and their nanocomposites using organically modified montmorillonite

Polymer gel electrolytes were prepared by thermal crosslinking reaction of a series of acrylic end‐capped poly(ethylene glycol) and poly(propylene glycol) [P(EG‐co‐PG)] having various geometries and molecular weights. Acrylic end‐capped prepolymers were prepared by the esterification of low molecular weight (M_n: 1900–5000) P(EG‐co‐PG) with acrylic acid. The linear increase in the ionic conductivity of polymer gel electrolyte films was observed with increasing temperature. The increase in the conductivity was also monitored by increasing the molecular weight of precursor polymer. Nanocomposite electrolytes were prepared by the addition of 5 wt % of organically modified layered silicate (montmorillonite) into the gel polymer electrolytes. The enhancement of the ionic conductivity as well as mechanical properties was observed in the nanocomposite systems. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 894–899, 2004     

中国信息服务业空间集聚研究

通过产业集聚的EG指数对中国各省份信息服务业的空间集聚程度进行研究,得出集聚程度比较显著.在此基础上,找到这一服务业的两个相关指标,利用产业集中度CRn判断出信息服务业主要集中于北京、广东等六个地区,然后对两指标数据进行无量纲化处理,加权求和得到新的综合指标,最后对这一新指标进行了系统聚类分析,得知这一产业主要集中在北京和广东两个地区.     

乙二醇和不同相对分子质量聚乙二醇对聚氨酯多孔膜性能的影响

采用乙二醇和不同相对分子质量的聚乙二醇作为聚氨酯多孔膜的致孔剂,通过对聚氨酯多孔膜的电镜图、透湿性、接触角以及拉伸性能的表征与分析,探究乙二醇和不同分子量聚乙二醇的用量对聚氨酯微孔膜结构和性能的影响。结果表明：采用乙二醇,添加量在50％时,透湿量达到2929 g/（m2· d ）;断裂强力与断裂伸长率分别在5．77 M Pa ,451．3％,说明得到的聚氨酯多孔膜具有较高的透湿量、孔隙率以及较强的拉伸性。     

An efficient four points modified explicit group poisson solver

In this paper, wc introduce a four points modified explicit group method for solving a two dimensional Poisson equation with Dirichlet boundary condition. The method is shown to be superior compared to the existing four points–explicit group and explicit decoupled group methods due to D. J. Evans and M. J. Biggins (1982) and A. R. Abdullah (1991), respectively, Some experiment results of the test problem are given in order to confirm our claim.     

复合无机无卤阻燃剂改性聚氨酯泡沫及性能研究

以聚磷酸铵(APP)为主要阻燃剂,复配可膨胀石墨(EG)和膨润土作为阻燃剂和改性剂,制备了完全无机且无卤阻燃剂改性的硬质聚氨酯泡沫(RPUF)。在固定无机阻燃剂及改性剂总量的条件下,研究了膨润土和EG用量及比例对RPUF的热稳定性、阻燃性能、力学性能、泡孔结构等的影响。结果表明,随膨润土或EG含量的增大,泡沫的压缩强度先增大后减小,二者含量分别为10%和5%时压缩强度最大。EG对泡沫阻燃性能的提高有显著影响,但同时也会使泡孔孔径增大;而膨润土作为泡沫成核剂能明显减小孔径。通过热重分析表明膨润土和EG的加入能明显增强泡沫的热稳定性。当APP为泡沫总质量的15%,膨润土为5%,EG为5%时,可以制得阻燃性能、力学性能和泡沫孔径较佳平衡的阻燃泡沫材料。在该条件下,泡沫的压缩强度为0.42 MPa,泡沫平均孔径为434μm,LOI值达到29%。     

电导率法快速测定工业用乙二醇中的电解质

提出了乙二醇电导率分析方法,给出了乙二醇的电导率合格判定标准。电导率法简单、快速,并应用于聚酯生产行业进货质量检验以及乙二醇货运行业的装运前货物品质验证。