Low cost foam-gelcasting preparation and characterization of porous magnesium aluminate spinel (MgAl2O4) ceramics

Porous MgAl₂O₄ ceramics were prepared via a low cost foam-gelcasting route using MgAl₂O₄ powders as the main raw material, ammonium polyacrylate as a dispersant, a small amount of modified carboxymethyl cellulose as a gelling agent, and TH-IV polymer as a foaming agent. The effects of additive's content, solid loading and gelling temperature on slurry's rheological behavior were investigated, and microstructures and properties of as-prepared porous MgAl₂O₄ ceramics examined. Based on the results, the roles played by the foaming agent in the cases of porosity, pore structure, pore size, mechanical properties and thermal conductivity were clarified. Porosity and pore sizes of as-prepared porous MgAl₂O₄ ceramics increased with increasing the foaming agent from 0.05 to 0.6 vol%. Porous MgAl₂O₄ ceramics with porosity of 75.1% and average pore size of 266 µm exhibited a compressive strength as high as 12.5±0.8 MPa and thermal conductivity as low as 0.24 W/(m K) (at 473 K).     

Porous anorthite ceramics with ultra-low thermal conductivity

Porous anorthite ceramics with an ultra-low thermal conductivity of 0.018 W/m K have been fabricated by hydrous foam-gelcasting process and pressureless sintering method using γ-alumina, calcium carbonate and silica powders as raw materials. Microstructure and phase composition were analyzed by SEM and XRD respectively. Properties such as porosity, pore size distribution and thermal conductivity were measured. High porosity (69–91%) and low thermal conductivity (0.018–0.13 W/m K) were obtained after sintering samples with different catalyst additions at 1300–1450 °C. Porosity, pore size, pore structure and grain size had obvious effect on heat conduction, resulting in the low thermal conductivity. The experimental thermal conductivity data of porous anorthite ceramics were found to be fit well with the computed values derived from a universal model.     

One-pot foam-gelcasting/nitridation synthesis of high porosity nano-whiskers based 3D Si3N4 porous ceramics

Nano-whiskers based 3D Si₃N₄ porous ceramics (3D-NWSNPC) with high-porosity (about 91–93 %), low density (0.17–0.25 g/cm³), low thermal conductivity, and a certain degree of recoverability under cyclic compressive loading and reasonably strengths were prepared at 1423–1523 K via a one-pot foam-gelcasting/nitridation route using inexpensive commercial Si powders as starting materials and hexadecyl trimethyl ammonium bromide as foaming agent. After nitridation at 1523 K, the sample with an original solid loading of 12.5 wt% exhibited the highest compressive strength of 1.9 MPa, even though its density was lowered to 0.25 g/cm³. The sample nitrided at 1473 K had a relative density of 7.3 %. Its compressive and specific strength were respectively 1.1 MPa and 5.5 MPa·cm³ g^?1, and its thermal conductivity was as low as 0.074 W/(m K) (measured at 323 K). These outstanding properties would make the as-prepared 3D-NWSNPC a promising candidate for applications in catalysis, filtration, thermal insulation and many other important areas.     

The preparation and properties of high-strength porous mullite ceramics by a novel non-toxic gelcasting process

A novel approach to fabricate porous mullite ceramics with homogeneous pore size and high-strength using green non-toxic and cost-effective poly-γ-glutamic acid (γ-PGA) gelling system was reported for the first time. Effect of γ-PGA addition, additive amount and solid loading on rheological behavior of the slurries, and microstructure and properties of samples were investigated systematically. By optimizing the solid loading of mullite samples, we are able to get the sample with small pores (< 200 µm) dominating (93.3% of the total pores), and compressive strength of the sample reaches up to 26.62 MPa. In addition, the mullite ceramics exhibited high porosity of 75.7% with low thermal conductivity of 0.279 W/(m·K) at room temperature. This study not only provides a green and non-toxic gelling system but also offers porous mullite ceramics with low thermal conductivity and excellent mechanical strength as an energy-saving thermal insulation material.     

Low-temperature preparation of Si3N4/SiC porous ceramics via foam-gelcasting and microwave-assisted catalytic nitridation

Si₃N₄/SiC porous ceramics were fabricated by a novel foam-gelcasting and microwave-assisted catalytic nitridation method at a temperature as low as 1273?K for 60?min or after only 10?min at 1373?K utilizing commercial Si and SiC with trace of impurity Fe (0.33?wt%) as starting materials. The Si₃N₄/SiC porous ceramics containing porosity of 68.54?±?0.73% which were fabricated at 1373?K for 10?min had flexural and compressive strengths of 5.28?±?0.17?MPa and 12.86?±?1.55?MPa.     

Effects of firing temperature on the microstructures and properties of porous mullite ceramics prepared by foam-gelcasting

Porous mullite ceramics were prepared at 1300–1600°C for 2?h via a foam-gelcasting route using industrial-grade mullite powders as the main raw material, Isobam 104 as the dispersing and gelling agent, triethanolamine lauryl sulphate as the foaming agent and sodium carboxymethyl cellulose as the foam stabilising agent. The effects of firing temperature on the sintering behaviour of green samples as well as microstructures and properties of final porous mullite products were investigated. With increasing the temperature from 1300 to 1600°C, linear shrinkage and bulk density values of fired samples increased, whereas their porosity decreased. Mechanical strength and thermal conductivity values of fired samples decreased with increasing their porosities. Even at a porosity level as high as 79.4%, compressive and flexural strengths of fired samples (with average pore size of 314?μm) remained as high as 9.0 and 3.7?MPa, respectively, and their thermal conductivity (at 200°C) remained as low as 0.21?W?(m^?1?K^?1).     

Foam-gelcasting preparation of high-strength self-reinforced porous mullite ceramics

High-strength self-reinforced porous mullite ceramics were prepared via foam-gelcasting using mullite powder as a main raw material, AlF₃·3H₂O (0–8 wt%) as an additive, Isobam-104 as a dispersing and gelling agent, sodium carboxymethyl cellulose as a foam stabilizing agent, and triethanolamine lauryl sulfate as a foaming agent. The effects of AlF₃·3H₂O content on rheological and gelling behaviors of the slurries, and porosity and mechanical properties of self-reinforced porous mullite samples were examined. Addition of AlF₃·3H₂O promoted the in-situ formation of elongated mullite in the fired porous samples, which improved considerably their mechanical properties. Compressive strength and flexural strength of 67.0% porous mullite ceramics prepared with addition of 6 wt% AlF₃·3H₂O was as high as 41.3 and 13.9 MPa, respectively. Its hot modulus rupture (HMOR) increased initially with the testing temperature, and peaked (with a maximum value of 16.6 MPa) at 800 °C above which it started to decrease with the testing temperature. Nevertheless, it was still retained as high as 6.7 and 2.8 MPa at 1200 and 1400 °C, respectively.     

Preparation and characterization of porous mullite ceramics via foam-gelcasting

Porous mullite ceramics were prepared via foam-gelcasting using industrial grade mullite powder as the main raw materials, Isobam-104 as the dispersing and gelling agent, sodium carboxymethyl cellulose as the foam stabilizing agent, and triethanolamine lauryl sulfate as the foaming agent. The effects of processing parameters such as type and amount of additive, solid loading level and gelling temperature on rheological properties and gelling behaviors of the slurries were investigated. The green samples after drying at 100 °C for 24 h were fired at 1600 °C for 2 h, and the microstructures and properties of the resultant porous ceramic samples were characterized. Based on the results, the effects of foaming agent on the porosity level, pore structure and size and mechanical properties of the as-prepared porous mullite ceramics were examined. Porosity levels and pore sizes of the as-prepared samples increased with increasing the foaming agent content up to 1.0%, above which both porosity levels and pore sizes did not change. The compressive strength and flexural strength of the as-prepared sample with porosity of 76% and average pore size of 313 μm remained as high as 15.3±0.3 MPa and 3.7±0.2 MPa, respectively, and permeability increased exponentially with increasing the porosity.     

Effects of V2O5 addition on the synthesis of columnar self-reinforced mullite porous ceramics

Spearhead columnar mullite was synthesized by in-situ reaction with V₂O₅ as additive. When the content of V₂O₅ was 7 wt%, the length of the spearhead columnar mullite was the longest with an aspect ratio of about 3.5. Furthermore, columnar self-reinforced mullite porous ceramics were prepared by a foam-gelcasting method, and the effects of V₂O₅ content on the rheological and gelling properties of mullite slurries as well as the microstructure, physical property and thermal insulation property of the prepared mullite porous ceramics were studied. The results showed that the flexural strength and compressive strength of the porous ceramics with 63% porosity prepared by using 2 wt% V₂O₅ additive were respectively as high as 13.9 and 41.3 MPa, and the thermal conductivity was about 1.04 W m^?1 K^?1.     

Preparation of Si3N4 porous ceramics via foam-gelcasting and microwave-nitridation method

Si₃N₄ porous ceramics with improved mechanical strength were fabricated for the first time by a combined foam-gelcasting and microwave-nitridation method at 1273–1373?K. The Si₃N₄ porous samples prepared at 1373?K/20?min with the porosity of 68.9% had respectively flexural and compressive strength as high as 8.1 and 20.8?MPa, which values were comparable or even superior to those of Si₃N₄ porous ceramics prepared previously by the conventional heating technique at a much higher temperature of 1773–1973?K, indicating that present preparation strategy is feasible to prepare high quality Si₃N₄ porous ceramic at a much milder condition. Moreover, the thermal conductivity of as-prepared Si₃N₄ porous ceramics at 1073?K was as low as 1.697?W/(m?K), suggesting it could be a potentially good heat insulating material for aluminum electrolyte cells.