在HCl—KCl(pH0.5)介质中,稀土—三溴偶氮胂二元络合物能较好地被阴离子交换树脂吸附。RE_2O_8在0～8μg/25ml范围内符合比尔定律,以双波长等吸收点法(测量波长λ_1=650nm,参比波长λ_2=740nm)扣除树脂背景影响,应用于稀土矿中稀土总量测定,结果令人满意。     

Fabrication of damascene Cu wirings using solid acidic catalyst

The copper damascene process is one of the most promising technologies for fabricating Cu wirings for electronic devices such as LSIs. In this research, the fabrication of damascene Cu wirings was conducted using solid acidic catalyst. When a Cu-plated wafer, whose oxide is a basic oxide is dipped into a mixture of oxidizing solution and acidic solution, surface atoms are ionized and etched off into the solution. However, because conventional nonelectrolytic etching does not have a reference surface, it is difficult to utilize for planarization. Therefore, a new nonelectrolytic machining method using a cation-exchange fabric instead of an acidic solution was developed. To be more precise, the planarization of a Cu-plated wafer was carried out by rubbing with the cation-exchange fabric in ozone water. Basically, this method exploits chemical reactions so that the physical properties of the workpiece surface are not deteriorated. Furthermore, this method uses no chemicals except for ozone water, which easily dissociates into water and oxygen molecules; thus, this method is a low-cost, environmentally friendly process. In this paper, as a preliminary experiment, the nonelectrolytic etching of a Cu sample using solutions of O₃ and CO₂ was carried out to inspect the dependence of the etching rate on [O₃] and [H⁺]. The results indicate that the etching rate increased as [O₃] and [H⁺] increased. When [H⁺] was high relative to [O₃], a smooth etch-pit-free surface was achieved. Next, nonelectrolytic etching using a cation-exchange fabric was carried out, and properties similar to those in the case of etching using solutions were obtained. Finally, damascene Cu wirings were fabricated using ozone water and a cation-exchange catalyst.     

甘蔗糖蜜生产核苷酸的分离方法研究

本文介绍了利用离子交换层析技术分离甘蔗糖蜜生产的核苷酸之现实性与可行性。探讨了分离核苷酸的最佳工艺条件。     

Use of electrodialysis to remove silver ions frommodel solutions and wastewater

The feasibility of the removal of Ag⁺ ions in a model solution and a sample of rinse water provided from an industrial plating plantwas investigated in a batch electrodialysis system. The experiments were carried out using two different types of ion-exchange membranes. The effects of applied potential, pH value and initial silver concentration on the duration of electrodialysis and energy consumption were examined. Full removal of Ag+ ions was achieved from model solutions and the sample of rinse water. The most convenient applied voltage and energy consumption values to remove silver ions are reported. These results will be useful for designing and operating different capacities of electrodialysis plants for recovering Ag⁺ ions.     

聚丙烯离子交换纤维研究

利用超声波分散原理将苯乙烯（St）分散到聚丙烯纤维（PP）中，以过氧化苯甲酰（BPO）作为引发剂，使苯乙烯接枝到PP纤维表面，得到PP－g-St纤维；然后用浓硫酸将PP－g-St纤维磺化，制成强酸型离子交换纤维。研究了反应时间、反应温度等对离子交换纤维的质量摩尔浓度的影响，并用红外光谱加以表征。结果表明：温度90℃下磺化反应2h，可得到离子交换质量摩尔浓度为0.95mmol/g的强酸型离子交换纤维。     

N503萃淋树脂分离富集金

研究了N_(503)萃淋树脂的合成方法及其分离富集金的条件.N_(503)萃淋树脂是萃取色层分离富集金的新固定相.2%硫脲、1%亚硫酸钠水溶液均可以定量解脱柱床上的金.经矿样验证,金的测定结果与717离子交换树脂吸附法一致.红外光谱表明该萃取色层与N_(503)液液萃取金有相同的机理.     

从稀土矿石浸出液中分离稀土元素 1.用离子交换树脂从矿石浸出液中吸附稀土

用001×7阳离子交换树脂可以从矿石浸出液中吸附稀土元素。小型试验与扩大试验表明,采用流化床设备进行连续逆流离子交换是可行的。     

Strengthening and toughening of a multi-component lithium disilicate glass-ceramic by ion-exchange

A multi-component lithium disilicate (LD) glass-ceramic with interlocking microstructure consisting of rod-like LD crystals and glassy matrix was ion-exchanged over wide temperature and time ranges in pure NaNO₃ or mixed NaNO₃ and KNO₃ baths below the glass transition temperature. Treatment temperature, time and salt bath dependences of surface characteristics and mechanical properties for the ion-exchanged glass-ceramic were investigated. It was found that the glass-ceramic with limited glassy matrix could be remarkably strengthened and toughened in NaNO₃ bath by adjusting the treatment temperature to a moderate level, at which Li⁺/Na⁺ exchange between the glassy matrix and the salt bath could form an ion-exchanged layer with larger depth and less stress relaxation. Furthermore, by using the mixed salt bath, the undesirable exchange of K⁺/Na⁺ in pure NaNO₃ bath could be limited; further enhanced strengthening effect was achieved. The results might renew the interest on strengthening LD glass-ceramics by traditional ion-exchange process.     

Mg2+在胜利褐煤中的负载量对其平衡复吸水含量的影响及其机理分析（英文）

Mg ion-exchanged samples were prepared with acid-washed Shengli lignite. The chemical composition of the ash of the raw sample was determined by X-ray fluorescence. The equilibrium adsorption water contents of sam-ples were determined in a range of relative humidity. The ion-exchange process was characterized by FT-IR, ash content, and pH value. A possible mechanism is proposed for equilibrium adsorption water of ion-exchanged samples at different humidities. The extent of ion-exchange reaction between Mg2+and lignite is control ed by the concentration of Mg2+in MgSO4 solution. The effect of Mg2+on equilibrium adsorption water content varies with relative humidity and content of Mg2+. The factor that controls equilibrium adsorption water content at low relative humidity is water interactions with sorption sites, which are Mg2+–carboxyl group complex. At middle relative humidity capil ary force between Mg2+–water clusters Mg+(H2O)n and capil ary is more impor-tant. At high relative humidity, free water–free water interactions are more significant.