丙烯腈－苯乙烯共聚物水解磺化产物对泥浆的稳定作用

在实验室条件下对用丙烯腈－苯乙烯共聚物在硫酸存在下的水解磺化产物（ＨＳＡＳ）处理的泥浆性能进行了评定。ＨＳＡＳ处理的泥浆有较小的滤失性，较好的耐盐和抗高温性。     

Reactivity of steam in exhaust gas catalysis III. Steam and oxygen/steam conversions of propane on a Pd/Al2O3 catalyst

A 1% Pd catalyst (38% dispersion) was prepared by impregnating a γ-alumina with palladium acetylacetonate dissolved in acetone. The behaviour of this catalyst in oxidation and steam reforming (SR) of propane was investigated. Temperature-programmed reactions of C₃H₈ with O₂ or with O₂ + H₂O were carried out with different stoichiometric ratios S(S =[O₂]/5[C₃H₈]). The conversion profiles of C₃H₈ for the reaction carried out in substoichiometry of O₂ (S < 1) showed two discrete domains of conversion: oxidation at temperatures below 350°C and SR at temperatures above 350°C. The presence of steam in the inlet gases is not necessary for SR to occur: there is sufficient water produced in the oxidation to form H₂ and carbon oxides by this reaction. Contrary to what was observed with Pt, an apparent deactivation between 310 and 385°C could be observed with Pd in oxidation. This is due to a reduction of PdO_x into Pd⁰, which is much less active than the oxide in propane oxidation. Steam added to the reactants inhibits oxidation while it prevents the reduction of PdO_x into Pd⁰. Compared to Pt and to Rh, Pd has a higher thermal resistance: no deactivation occurred after treatment up to 700°C and limited deactivation after treatment up to 900°C, provided that the catalyst is maintained in an oxygen-rich atmosphere during the cooling.     

槽孔式水力驱动控制棒槽孔阻力系数实验研究

对槽孔式水力驱动控制棒槽对孔阻力系数进行了大量实验研究，获得了槽孔式水力驱动控制棒槽对孔阻力系数和其随槽对孔位移的变化规律，分析了槽对孔阻力系数与控制棒槽对孔结构参数之间的关系。结果表明：随槽对孔位移的增加，槽对孔阻力系数从某一较大的定值迅速降低到某一较小的定值，然后再迅速反回到初始的定值，形成一个对称的宽幅波谷；槽高使阻力系数曲线波谷幅宽发生变化，也使完全不重合段的阻力系数发生变化；随内套孔径的增大，阻力系数有所降低，其对阻力系数的影响也进一步减弱。孔径增大到一定程度，阻力系数基本不受孔径参数的影响。     

水溶性涂料使用性能研究

本文通过试验对水溶性涂料的耐盐雾腐蚀性能，耐热性能，高低温冲击性能，耐油性能，涂膜与铁基体，面漆的给合力及涂膜表面电阻进行研究，同时指出了该涂料在军用电子产品上的应用前景。     

Characterization of Ceramic Composite-Membranes Prepared by ORMOSIL Coating Sol

Sol-gel methods offer many advantages over conventional slip-casting, including the ability to produce ceramic membranes. They are purer, more homogeneous, more reactive and contain a wider variety of compositions. We produced ormosil sol using sol-gel process under different molecular weight of polymer species [polyethylene glycol (PEG) ] in total system [Tetraethyl ortho silicate(TEOS)-polyethylene glycol (PEG)]. The properties of as-prepared ormosil sol such as,viscosity, gelation time were characterized. Also, the ceramic membrane was prepared by dip-coating with synthetic sol and its micro-structure was observed by scanning electron microscopy. The permeability and rejection efficiency of membrane for oil/water emulsion were evaluated as cross-flow apparatus. The ormosil sol coated Membrane is easily formed by steric effect of polymer and it improves flux efficiency because infiltration into porous support decreased. Its flux efficiency is elevated about 200(1/m2·h) compared with colloidal sol coated membrane at point of five minutes from starting test.     

用边界元法提取VLSI版图电阻

介绍了ＶＬＳＩ版图验证中电阻提取的基本原理和主要方法，给出了一种新颖的基于边界元法的电阻提取算法。该算法采用变节点单元，较好地解决了实际问题中经常出现的角点问题。通过应用该算法对几个实例进行提取，证明使用本文的算法不仅在精度上而且在占用ＣＰＵ时间上都取得了令人满意的效果     

覆膜滤料的滤尘性能测试方法研究

由于覆膜滤料的结构和性能有别于普通滤料，因而普通滤料的滤尘性能测试方法不完全适用于覆滤料。本文作者在总结实践经验的基础上，提出了在覆膜滤料的滤尘性能测试中应注意的一些问题和应增加的测试项目。     

S—135钢板热轧工艺研究

S—135钢板是水电站用高强耐磨不锈钢板,既要求强度高、韧性好,又要求耐磨、耐蚀性强,生产难度较大。除我厂外,目前国内尚无其它厂家能够生产这种钢板。该钢板在加热轧制,冷却过程中要解决很多技术难点。我们通过采用特殊的控制轧制和控制冷却工艺,很好地解决了诸多技术难点,使S—135钢板的开发研制取得了成功。为电站用高强度耐磨不锈钢生产提供了宝贵的经验,也为控制轧制及控制冷却技术在中板生产行业的应用起到了积极的推动作用。     

残余应力对55SiMnVB弹簧钢疲劳性能的影响

研究了５５ＳｉＭｎＶＢ弹簧钢板疲劳断口特征及裂扩展过程。结果表明，喷丸强化在表层产生的残余压应力可明显提高疲劳抗力，增强裂纹闭合效应，降低裂纹扩展速度。     

功率GaAs MESFET的热阻测试

阐述了功率ＧａＡｓＭＥＳＦＥＴ器件热阻测试中温敏参数ＶＧＳＦ和测试电流Ｉｍ的选取，给出了１～５Ｗ器件典型温敏参数的温度测试系数Ｍ与测试电流Ｉｍ的关系。讨论了测试延迟时间ｔｍｄ对△ＶＧＳＦ测量值的影响和三种校正方法。