三维石墨烯-碳纳米管/水泥净浆的压敏性能

为了探索三维石墨烯-碳纳米管(G-CNTs)/水泥净浆的压敏性能,采用四电极法研究了荷载作用下GCNTs/水泥净浆的电阻率变化,并分析不同G-CNTs掺量、加载幅度、加载速度以及恒定荷载对电阻率变化的影响。研究表明:随着G-CNTs掺量的增加,电阻率呈先减小后稳定的变化趋势,在G-CNTs掺量由0.2wt%增加至1.6wt%时,电阻率下降51.8%;电阻率与温度呈负相关;G-CNTs掺量高于0.8wt%时可以显著提高水泥净浆的压敏性能,且电阻率变化率与应力应变有明显的对应关系,1.2wt%G-CNTs掺量下试件的应力灵敏系数和应变灵敏系数分别为2.3%/MPa和291;G-CNTs/水泥净浆电阻率变化率幅值随着加载幅度增大而相应增加,其电阻率变化率曲线在不同加载速度以及恒定荷载作用下均与应力-应变曲线一一对应,具有良好的压敏特性。     

Carbon nanotube filter for heavy metal ion adsorption

This study investigated carbon nanotube filtration technology using catalyst particles supported on silicalite-1–biomorphic carbon materials (BCMs). Aqueous solutions of Mn(II), Cu(II), Cr(III), Cd(II), and Pb(II) were used to test the efficiency of heavy metal ions removal. Carbon nanotubes (CNTs) were synthesized and grown on BCMs by the chemical vapor deposition method catalyzed with the catalyst (Co, Fe, and Ni). The synthesized CNTs with Co– and Fe– nanoparticles were typically multi-walled carbon nanotubes, and they showed good crystallinity (I_D/I_G = 1.05) and yield of (11.10 and 8.86) %. The removal efficiency of Mn(II), Cu(II), Cr(III), Cd(II), and Pb(II) ions using Co-catalyzed CNT filter was 97.57%, 98.01%, 97.89%, 97.42%, and 99.99%, respectively.     

Poly(3-hydroxyalkanoate)-grafted carbon nanotube nanofillers as reinforcing agent for PHAs-based electrospun mats

Poly(3-hydroxyalkanoate)s, PHAs, have been covalently grafted onto the surface of multi-walled carbon nanotubes, MWCNTs, providing nanofillers (MWCNT-graft-PHAs) with enhanced compatibility and reinforcement effect towards PHAs. MWCNTs were first modified by in-situ generated diazonium cations obtained from a hydroxyl-containing aniline derivative, yielding MWCNTs with reactive hydroxyl surface groups, MWCNT-OH. Then, MWCNT-graft-PHAs were obtained by direct, i.e. without using any catalyst, transesterification approach. The successful chemical modification of MWCNTs surface was evidenced by Raman spectroscopy and XPS analysis confirming the covalent grafting of PHA on MWCNT. 3-Dimension mats were further produced through electrospinning of a PHA/MWCNT-graft-PHA solution providing nanocomposites with well-defined nanofibrous morphology. No aggregation of the MWCNTs was evidenced by SEM attesting that the grafting of PHA onto MWCNT improved their dispersion within the PHA matrix and consequently, the properties of the corresponding nanomaterials. Indeed, mechanical analysis results have shown that nanofibers loaded with MWCNT-graft-PHA (3 wt%) displayed excellent properties with an increase (+41%) of the tensile strain at break without any decrease of the high elastic modulus as compared to pristine PHA (131 MPa).     

碳纳米管(CNT)场发射显示器的关键技术的研究

对碳纳米管阴极的制备以及场发射显示器的真空封装技术进行了研究.利用一种新的碳纳米管生长工艺制备出了具有优良场发射性能的碳纳米管阴极.并将这种直接生长的碳纳米管薄膜作为阴极,结合一种弹性封装工艺,开发了一种具有简单字符显示功能的场发射显示器.该显示器在较低的工作电压下就可获得高亮度的显示效果,并且器件的亮度与驱动电压成较好的线性关系,这将有利于未来的碳纳米管场发射显示器实现高亮度和多级灰度显示.器件的持续工作寿命测试已经超过5500小时,充分验证了碳纳米管作为场发射阴极的应用潜力.     

The Synthesis of Sulfated Titanium Oxide Nanotubes

TiO₂ nanotubes can be prepared in gram quantities by treating anatase TiO₂ powder with concentrated NaOH solution. These TiO₂ nanotubes acquired strong acidity after being impregnated with sulfuric acid solution and calcined at 300 °C. The anatase TiO₂ powder used to prepare the nanotube did not catalyze the esterification between cyclohexanol and acetic acid, while sulfated TiO₂ nanotubes were very reactive toward the esterification reaction.     

碳纳米管的制备及研究

介绍了在直流电弧放电法制备富勒烯过程中，从阴电极表面收集到大量的碳纳米管及巴基葱，产生率达到５０％，并用电子显微镜对其进行了观察和初步研究。     

Effects of various post-treatments on carbon nanotube films for reliable field emission

In this report, the FE characteristics of carbon nanotubes (CNTs) treated using both thermal annealing and mechanical coatings on the as-grown CNTs systematically studied. It was found that in the high temperature annealed samples, CNTs were attacked at its root during annealing due to a small amount of oxygen, and were pulled out of the substrate in places after FE measurements because of the contact resistance. However, for the mechanically coated samples both with spin on glass (SOG) and polymethyl methacrylate (PMMA), CNTs were found to be nearly intact after FE measurements and showed reliable FE characteristics over repeatable voltage scan. The reliability of CNTs during FE could be owing to the strong adhesion of CNTs to the substrate both by SOG and PMMA coatings.     

Synthesis and Characterization of Nanosized ZSM-5 Zeolite with Mesoporous Carbon Nanotube as Templates

Preparation of nanocrystalline ZSM-5 has been proven possible with carbon matrix by using confined space synthesis. In combination with the hydrothermal method, by the use of a mesoporous carbon nanotube as the inert support material, ZSM-5 with SiO₂/Al₂O₃ ratios of 100 was successfully synthesized with an average crystal size of 27 nm. Their structures were preliminarily characterized by x-ray power diffraction (XRPD) and infrared spectroscopy (IR), and scanning electron microscopy (SEM), respectively. At the same time, we put forward the mechanism about the confined space synthesis in terms of the results.     

单壁碳纳米管的制备及生长特性研究

采用Fe/MgO作为催化剂 ,催化裂解CH4制备了较纯的单壁碳纳米管 ,用TEM和Raman对碳纳米管进行了表征 ,对不同生长温度下制备的碳纳米管Raman径向呼吸振动峰 (RBM)进行了分析 ,研究了生长温度对单壁碳纳米管生长特性和结构特性的影响     

纳米材料的力学性能

综述了纳米晶体材料和纳米碳管材料的力学性能研究的最新进展。实验数据表明纳米晶体材料的强度与其晶粒尺寸大小的关系并不遵循Hall-Petch方程。相对于常规晶体材料 ,纳米材料的超塑性发生在更低的温度和更高的应变速率下。理论计算和实验数据表明 :纳米碳管是一种有着高刚性、高强度、高韧性和低密度的材料。纳米晶体材料和纳米碳管的异常的力学性能已经有了一些应用实例