Complex study of protective Cr3C2–NiAl coatings deposited by vacuum electro-spark alloying,pulsed cathodic arc evaporation,magnetron sputtering,and hybrid technology

Coatings were obtained by vacuum electro-spark alloying (VESA), pulsed cathodic arc evaporation (PCAE), magnetron sputtering (MS) techniques and VESA-PCAE-MS hybrid technology using Cr₃C₂–NiAl electrodes. The structure of the coatings was analyzed using scanning and transmission electron microscopy, X-ray diffraction and energy-dispersive spectroscopy. Mechanical properties were determined by nanoindentation, while tribological properties were assessed using pin-on-disk tribometer. Corrosion resistance was estimated by voltammetry in 1 N H₂SO₄ and 3.5%NaCl solutions. Oxidation resistance tests were performed at 800°С in air. The VESA coating had the highest thickness, low friction coefficient and high wear resistance. PCAE coating demonstrated the highest hardness (24 GPa) and elastic recovery (59%), oxidation resistance and superior corrosion resistance both in 1 N H₂SO₄ (i_corr = 70 μА/cm²) and 3.5%NaCl (i_corr = 0.74 μА/cm²) solutions. The MS coating had average mechanical properties and low corrosion current density (71 μА/cm²) in 1 N H₂SO₄. Deposition of coatings using VESA-PCAE-MS hybrid technology led to an increase in corrosion and oxidation resistance at least by 1.5 times in comparison with the VESA coating.     

Parameter estimation for a morphochemical reaction-diffusion model of electrochemical pattern formation

The process of electrodeposition can be described in terms of a reaction-diffusion partial differential equation (PDE) system that models the dynamics of the morphology profile and the chemical composition. Here we fit such a model to the different patterns present in a range of electrodeposited and electrochemically modified alloys using PDE constrained optimization. Experiments with simulated data show how the parameter space of the model can be divided into zones corresponding to the different physical patterns by examining the structure of an appropriate cost function. We then use real data to demonstrate how numerical optimization of the cost function can allow the model to fit the rich variety of patterns arising in experiments. The computational technique developed provides a potential tool for tuning experimental parameters to produce desired patterns.     

Microstructure,tribological behavior and magnetic properties of Fe−Ni−TiO2 composite coatings synthesized via pulse frequency variation

The Fe−Ni−TiO₂ nanocomposite coatings were electrodeposited by pulse frequency variation. The results showed that the nanocomposite with a very dense coating surface and a nanocrystalline structure was produced at higher frequencies. By increasing the pulse frequency from 10 to 500 Hz, the iron and TiO₂ nanoparticles contentswere increased in expense of nickel content. XRD patterns showed that by increasing the frequency to 500 Hz, an enhancement ofBCC phase was observed and the grain size of deposits was reduced to 35 nm. The microhardness and the surface roughness were increased to 647 HV and 125 nm at 500 Hz due to the grain size reduction and higher incorporation of TiO₂ nanoparticles into the Fe−Ni matrix (5.13 wt.%). Moreover, the friction coefficient and wear rate values were decreased by increasing the pulse frequency;while the saturation magnetization and coercivity values of the composite deposits were increased.     

Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

地下输水管网的腐蚀调查

介绍了中国石油天然气股份有限公司大庆石化分公司地下输水管网的腐蚀现状与调查分析情况,提出了对地下输水管网实施以深井阳极地床外加电流阴极保护为主、局部欠保护区辅以镁合金牺牲阳极的阴极保护方案。经分析,采取上述防护措施后,每年可产生2488万元的经济效益。     

电沉积纳米ZnO薄膜

在硝酸锌溶液中电沉积ZnO，通过正交试验方法研究槽液浓度、pH值以及电流密度对纳米ZnO薄膜电沉积的作用。用XRD分析了纳米ZnO的组织、结构与成分，SEM获得了纳米ZnO的表面形貌。     

新库区储罐及地下钢结构阴极保护的应用及系统运行状况

新库区位于海滩上的回填土区 ,土壤pH值 5～ 6 ,地电阻≤ 2 5Ω·m ,土样含水量 12 %～ 2 4 % ,形成电导率高、透气性好和弱酸性的潮湿土壤 ,具有强的腐蚀性。此外 ,该区的土壤随着时间的推移 ,原海滩的盐碱通过扩散及毛细作用 ,使土壤的腐蚀性随含盐量增加而增强 ;因此 ,对新库区地下钢结构实施电化学阴极保护是很有必要的     

电沉积法制备铜分散电极

研究了电沉积制备铜分散电极的方法,通过对阴极极化曲线的测试,考察了电流密度及不同冲击电流方式对铜粉粒度的影响。结果表明:适当的电流密度、合适的分散剂、间歇式的电流是得到较细铜粉的条件。同时对铜分散电极的电化学性质进行初步测试,结果表明铜粉细化以后,铜分散差电池的电动势值有所上升。