The effects of washing a collagen sample prior to TEM examination

Transmission electron microscopy (TEM) is an important analysis technique to visualize (bio)macromolecules and their assemblies, including collagen fibers. Many protocols for TEM sample preparation of collagen involve one or more washing steps to remove excess salts from the dispersion that could hamper analysis when dried on a TEM grid. Such protocols are not standardized and washing times as well as washing solvents vary from procedure to procedure, with each research group typically having their own protocol. Here, we investigate the influence of washing with water, ethanol, but also methanol and 2-propanol, for both mineralized and unmineralized collagen samples via a protocol based on centrifugation. Washing with water maintains the hydrated collagen structure and the characteristic banding pattern can be clearly observed. Conversely, washing with ethanol results in dehydration of the fibrils, often leading to aggregation of the fibers and a less obvious banding pattern, already within 1 min of ethanol exposure. As we show, this process is fully reversible. Similar observations were made for methanol and propanol. Based on these results, a standardized washing protocol for collagenous samples is proposed.     

Estimation of gradient size of interfacial strain and its optimization for effective magnetoelectric coupling in (CoFe2O4) – (0.93Na0.5Bi0.5TiO3 – 0.07BaTiO3), 2-2 nano-composites

Strain-mediated coupling between the magnetic and electrically ordered phases plays a significant role in magnetoelectric (ME) nano-composites. This study explores a method to analyse and quantify interfacial strain using a grazing angle scan (α) in a ME composite optimised for a specific microstructure. The details of strain around the interface CoFe₂O₄ (CFO) – 0.93Na_0.5Bi_0.5TiO₃ – 0.07BaTiO₃ (NBT-BT) was determined by performing ‘α’ scan, in order to gather information at various depths of the NBT-BT layer around maximum intensity (110) reflection. The strain around the interface was observed to dominate over a spatial region of ～20–30 nm away from the interface. The Piezoresponse force microscopy (PFM) studies performed near the interface reveal that the strain constrain experienced by the ferroelectric layer operates such that polarisation rotation and domain wall motion are constrained compared to the strain relaxed region of the film. For effective strain transfer, heterostructures grown with optimised thicknesses (～20–30 nm) exhibited a superior inverse piezomagnetic effect.     

A Bio-Conjugated Fullerene as a Subcellular-Targeted and Multifaceted Phototheranostic Agent

Fullerenes are candidates for theranostic applications because of their high photodynamic activity and intrinsic multimodal imaging contrast. However, fullerenes suffer from low solubility in aqueous media, poor biocompatibility, cell toxicity, and a tendency to aggregate. C₇₀@lysozyme is introduced herein as a novel bioconjugate that is harmless to a cellular environment, yet is also photoactive and has excellent optical and optoacoustic contrast for tracking cellular uptake and intracellular localization. The formation, water-solubility, photoactivity, and unperturbed structure of C₇₀@lysozyme are confirmed using UV-visible and 2D ¹H, ¹⁵N NMR spectroscopy. The excellent imaging contrast of C₇₀@lysozyme in optoacoustic and third harmonic generation microscopy is exploited to monitor its uptake in HeLa cells and lysosomal trafficking. Last, the photoactivity of C₇₀@lysozyme and its ability to initiate cell death by means of singlet oxygen (¹O₂) production upon exposure to low levels of white light irradiation is demonstrated. This study introduces C₇₀@lysozyme and other fullerene-protein conjugates as potential candidates for theranostic applications.     

Performance evaluation of basalt fiber-reinforced geopolymer composites with various contents of nano CaCO3

High carbon footprint of cement production is the major drawback of plain cement concrete resulting in environmental pollution. Geopolymer composites paste can be effectively used as an alternative to Portland cement in the construction industry for a sustainable environment. The demand for high-performance composites and sustainable construction is increasing day by day. Therefore, the present experimental program has endeavored to investigate the mechanical performance of basalt fiber-reinforced fly ash-based geopolymer pastes with various contents of nano CaCO₃. The content of basalt fibers was fixed at 2% by weight for all specimens while the studied contents of nano CaCO₃ were 0%, 1%, 2%, and 3%, respectively. The compressive strength, compressive stress-strain response, flexural strength, bending stress-strain response, elastic modulus, toughness modulus, toughness indices, fracture toughness, impact strength, hardness, and microstructural analysis of all four geopolymer composite pastes with varying contents of nano CaCO₃ using scanning electron microscopy (SEM) were evaluated. The results revealed that the use of 3% nano CaCO₃ in basalt fiber-reinforced geopolymer paste presented the highest values of compressive strength and hardness while the use of 2% nano CaCO₃ showed the highest values of flexural strength, impact strength, and fracture toughness of composite paste. The SEM results indicated that the addition of nano CaCO₃ improved the microstructure and provided a denser geopolymer paste by refining the interfacial zones and accelerating the geopolymerization reaction.     

Maskless Preparation of Spatially-Resolved Plasmonic Nanoparticles on Polydimethylsiloxane via In Situ Fluoride-Assisted Synthesis

Here, a fluoride-assisted route for the controlled in-situ synthesis of metal nanoparticles (NPs) (i.e., AgNPs, AuNPs) on polydimethylsiloxane (PDMS) is reported. The size and coverage of the NPs on the PDMS surface are modulated with time and over space during the synthetic process, leveraging the improved yield (10×) and faster kinetics (100×) of NP formation in the presence of F⁻ ions, compared to fluoride-free approaches. This enables the maskless preparation of both linear and step gradients and patterns of NPs in 1D and 2D on the PDMS surface. As an application in flexible plasmonics/photonics, continuous and step-wise spatial modulations of the plasmonic features of PDMS slabs with 1D and 2D AgNP gradients on the surface are demonstrated. An excellent spatially resolved tuning of key optical parameters, namely, optical density from zero to 5 and extinction ratio up to 100 dB, is achieved with AgNP gradients prepared in AgF solution for 12 minutes; the performance are comparable to those of commercial dielectric/interference filters. When used as a rejection filter in optical fluorescence microscopy, the AgNP-PDMS slabs are able to reject the excitation laser at 405 nm and retain the green fluorescence of microbeads (100 µm) used as test cases.     

High-resolution FIB-TEM-STEM structural characterization of grain boundaries in the high dielectric constant perovskite CaCu3Ti4O12

In this work, the grain boundaries composition of the polycrystalline CaCu₃Ti₄O₁₂ (CCTO) was investigated. A Focused Ion Beam (FIB)/lift-out technique was used to prepare site-specific thin samples of the grain boundaries interface of CCTO ceramics. Scanning transmission electron microscopy (STEM) coupled with energy dispersive X-ray spectrometry (EDXS) and Electron Energy Loss Spectroscopy (EELS) systems were used to characterize the composition and nanostructure of the grain and grain boundaries region. It is known that during conventional sintering, discontinuous grain growth occurs and a Cu-rich phase appears at grain boundaries. This Cu-rich phase may affect the final dielectric properties of CCTO but its structure and chemical composition remained unknown. For the first time, this high-resolution FIB-TEM-STEM study of CCTO interfacial region highlights the composition of the phases segregated at grain boundaries namely CuO, Cu₂O and the metastable phase Cu₃TiO_4.     

Dynamic probe of ZnTe(110) surface by scanning tunneling microscopy

The reconstructed surface structure of the II–VI semiconductor ZnTe (110), which is a promising material in the research field of semiconductor spintronics, was studied by scanning tunneling microscopy/spectroscopy (STM/STS). First, the surface states formed by reconstruction by the charge transfer of dangling bond electrons from cationic Zn to anionic Te atoms, which are similar to those of IV and III–V semiconductors, were confirmed in real space. Secondly, oscillation in tunneling current between binary states, which is considered to reflect a conformational change in the topmost Zn–Te structure between the reconstructed and bulk-like ideal structures, was directly observed by STM. Third, using the technique of charge injection, a surface atomic structure was successfully fabricated, suggesting the possibility of atomic-scale manipulation of this widely applicable surface of ZnTe.     

Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

Biodegradation of poly(lactic acid)—cassava bagasse composites produced by injection molding

Neat poly (lactic acid) (PLA) and PLA/cassava bagasse (CB) composites were used to produce seedling tubes by extrusion and injection molding. The tubes were buried in simulated soil, and their biodegradation was investigated by weight loss, scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR). After 180 days, the composites' biodegradation was higher than neat PLA material, and the higher the CB content, the higher the biodegradation, which caused fissures and voids in the material. The biodegradation of PLA/CB composites increased the phosphorus content in the soil after 180 days. Composites of PLA with CB, an abundant agro-industrial residue in Brazil, are promising because they can reduce the environmental impact due to CB's proper destination, and the composites' costs and biodegradation are faster than pure PLA material. Both the faster biodegradation of the tube and the higher P content are advantageous for seedling tubes.     

Variation of internal structure and performance of polyethylene- and polypropylene-modified bitumen during blending process

Linear-viscoelastic characteristics and performance are evaluated throughout the blending process of polyethylene and polypropylene with bitumen. Results indicate that type, form and percentage of polyolefin play a significant role in the time evolution of the composite's mechanical response. Toluene extraction of modified bitumen revealed, for the first time, the formation of a sponge-like polymer network. Visual inspection and Fourier transform infrared analysis of the polyolefins recovered after extraction indicates higher affinity of the polyethylene with bitumen in agreement with the rheological test results. The use of polypropylene is discouraged if rutting performance is a concern, and polyethylene in both pellets and powder form at 4%, and after 210 min of blending produces a modified bitumen with acceptable performance.