The surface carboxyl group of carbonaceous microspheres effects on the synthesis and structure of SiOC ceramics

In this study, C/SiOC and C/SiO₂ composites were prepared by using carbonaceous microspheres with different surface functional groups. Carbonaceous microspheres based on hydrothermal reaction of glucose contains hydroxyl group, while the surface carboxyl group increases after NaOH etching. The hydroxyl group increases the oxygen-enriched structural units of SiOC ceramics, and the C spheres are closely enwrapped in SiOC matrix after pyrolysis at 900 °C. However, the interfacial reaction of surface carboxyl with Si–OH results in the formation of cristobalite SiO₂, and C spheres are not only encased inside the SiOC matrix, but also dispersed outside of SiOC ceramics. After removal of C via calcination at 500 °C for 5 h, C/SiOC and C/SiO₂ composites are transformed into amorphous SiO₂ and cristobalite SiO₂, respectively. The thermogravimetric analysis indicates the oxidation resistance of SiOC is superior to that of C and SiO₂.     

Chitosan Microspheres as Carriers for pH‐Indicating Species in Corrosion Sensing

Chitosan microspheres containing bromocresol green, cresol red, and phenolphthalein for corrosion detection, through pH change, are synthesized in order to be used in protective coatings for aluminium alloys. Microspheres containing corrosion detection species are characterized morphologically (SEM) and physico‐chemically (FTIR, TGA). Release studies (UV–vis) are performed in corrosion‐promoting conditions (pH, NaCl), and detection studies by immersion in media associated with corrosion activity while microspheres' sensing activity is evaluated visually. Electrochemical characterization of AA2024 substrates in the presence of chitosan spheres is performed to understand material performance, and a color change is observed as a result of local pH increase in cathodic areas when corrosion takes place. These findings can be correlated with the results from release studies and seem a promising approach for corrosion sensing purposes, not only because pH increase is possible to detect due to corrosion, but also because chitosan is considered an environmentally friendly material.     

Synthesis,characterization and properties of functionalized styrene–maleimide copolymers

New functionalized styrene–maleimide copolymers were prepared by free radical copolymerization of styrene (St) and N‐4‐carboxybutylmaleimide (NBMI) in chloroform, using 2,2′‐azobisisobutyronitrile (AIBN) as initiator. Monomer and copolymer characterization was carried out by ¹H‐ and ¹³C‐NMR. Copolymer composition was determined by elemental analysis and Fourier‐transform infrared (FTIR) spectroscopy. The glass transition temperature (from DSC) and the thermogravimetric analysis (TGA) of the copolymers were consistent with the thermal behavior and stability observed for alternating St–maleimide copolymers. St–NBMI copolymers crosslinked with divinylbenzene (DVB) were also synthesized and their cation exchange properties evaluated in order to assess the capacity of the new copolymers to bind metallic ions. Copyright © 2005 Society of Chemical Industry     

PAA-PSF交联复合膜的制备及对低浓度有机醇水溶液反渗透分离性能研究

进行了ＰＡＡ（ＰｏｌｙａｃｒｙｌｉｃＡｃｉｄ）－ＰＳＦ（Ｐｏｌｙｓｕｌｆｏｎｅ）交联复合膜的制备，研究了交联剂、添加剂对膜性能的影响，并通过扫描电镜观察了膜的断面结构．研究了ＰＡＡ－ＰＳＦ交联复合膜对低浓度有机醇类水溶液反渗透分离性能．发现对于１０００×１０－６乙醇水溶液截留率达到６６．２％，透过流束可达０．９×１０－６（ｍ３·ｍ－２·ｓ－１）．随醇的分子量的增加，截留率不断上升，对戊醇的截留率达９４．３％，而透过流束则保持相对稳定．对不同结构醇类的分离性能研究表明，截留率存在有：ｔｅｒｔ－＞ｓｅｃ－＞ｉｓｏ－＞ｎ－的规律．     

Novel one-step route for synthesizing sub-micrometer PSt hollow spheres via redox interfacial-initiated method in inversed emulsion

Interfacial-initiated polymerization of styrene (St) was carried out in inversed emulsion with cumene hydroperoxide (CHPO) and ferrous sulfate (FeSO₄)/disodium ethylenediaminetetraacetate (NaEDTA)/sodium formaldehyde sulfoxylate (SFS) as the redox initiation system. The water-soluble Fe²⁺-NaEDTA-SFS acted as the reducing component and the oil-soluble CHPO as the oxidant component of the redox initiation system. Therefore, the primary radicals were produced mainly at the oil/water interface to initiate the polymerization of St. Thus, sub-micrometer hollow polystyrene (PSt) spheres were obtained by one-stage polymerization, which was supported by the techniques of transmission electron microscopy (TEM) and field emission scanning electron microscopy (FESEM).     

Effects of Heat Treatment Temperature and Time on Structure and Static Magnetic Property of W-type Ferrite Hollow Mierospheres

Hollow spheres of hexagonal ferrite BaCozFelrO27 were fabricated through a spray pyrolysis technique using co-precipitation ferrite powder precursor as materials, followed by calcinations in an air atmosphere. The phase composition, micro-morphology, and static magnetic property of the particles were measured by XRD, SEM, and VSM. The results indicate that the method for preparation of ferrite hollow microspheres （FHM） results in a broad particles size distribution. The density of FHM decreased from 5.31 g/ cm^3 to 2.31 g/cm^3. When the heating rate was 5℃/min, and temperature was 1 200℃ for 4 hours, pure W-type ferrites were formed. With the heat treatment temperature and time increasing, the crystal structure becomes perfect, the saturation magnetization is increased and the coercive force is decreased.     

吸水膨胀型膨润土/交联聚丙烯酰胺颗粒堵剂

使丙烯酰胺、少量N，N-亚甲基双丙烯酰胺在钙膨润土存在下进行水溶液引发接枝共聚合，聚合产物经造粒、粉碎、筛分，得到粒径0．5～1．0mm的颗粒堵剂。根据颗粒堵剂吸水量大小确定丙烯酰胺与膨润土最佳质量比为7：1，引发剂最佳用量为500g／t，交联剂最佳用量为300g／t，吸水量与这3个参数之间的关系曲线都经过最大值，颗粒堵剂在去离子水中的吸水量为560～650mL/g。该堵剂已大规模生产，在胜利、中原油田许多采油厂已用于调剖、堵水和调驱施工，在青海、江苏、大港、冀东等油田也已开始使用。在胜利东辛采油厂的一个井组，连续3个月在3口井注入该堵剂共27t，使井口压力上升3MPa，产油量大幅度增加。表l参l。     

动态交联热塑性弹性体增韧聚丙烯合金

用动态交联方法制备聚烯烃热塑性弹性体（ＴＰＯ）增韧聚丙烯，制备了具有低温冲击性能良好、综合力学性能比较均衡的聚丙烯合金。同时，研究了ＴＰＯ组成、工艺及基体组成与ＴＰＯ增韧聚丙烯共混物力学性能的关系。并通过差热扫描量热计和扫描电镜考察了共混物的形态结构。