Mechanical properties,corrosion resistance,and rubber pad forming of cold differential speed-rolled pure titanium for bipolar plates of proton-exchange membrane fuel cells

Due to problems such as pores on surface-treated coatings, the corrosion resistance of pure titanium bipolar plates for proton-exchange membrane fuel cells can be further improved by increasing the corrosion resistance of pure titanium by using differential speed-rolling (DSR); however, these materials have not yet reached the standard requirements of bipolar plates (corrosion current density i_corr＜10³ nA·cm^?2). In this work, the corrosion resistance of pure titanium was improved by optimizing the DSR process while the strength was maintained. The best corrosion resistance of the DSR pure titanium was achieved when the roller speed ratio was 2, while i_corr was 429 nA·cm^?2 in a solution of 0.5 M H₂SO₄ and 2 mg/L HF at room temperature. The formability of the DSR pure titanium for bipolar plates was verified. The optimal holding pressure range was 6.8–7.0 kN.     

Investigation of stress fields for non-standard sized glass plates loaded by ring-on-ring

A ring-on-ring (ROR) test is a prevailing test method for evaluating the equi-biaxial strength of glass materials. However, current ROR test standards limit the strength and size of glass to prevent a nonlinear behavior. In this study, the feasibility of ROR testing for non-standard, high-strength glass, such as tempered or ion-exchanged rectangular glass is investigated. To this end, ROR simulation based on theory and experiment is conducted for thirty non-standard glasses with widths of 100–300 mm and aspect ratios of 1.0–2.0. As a result, the maximum measurable stress was about 215.6 MPa for 100 × 200 mm glass and 481.3 MPa for 300 × 600 mm glass with a 3% deviation, which is well above the strength of regular tempered glass. The main purpose of this work is to understand the range of aspect ratio of horizontal and vertical widths of a glass plate that can be evaluated by the standard ROR test.     

Inconel 690传热管GTAW对接焊接头组织及力学性能研究

对Inconel 690传热管材进行钨极气体保护焊(GTAW)对接焊,采用拉伸试验机、压扁试验机和光学显微镜测试和分析传热管焊接接头,同时利用ANSYS软件开展焊接接头在设计工况失压时的一次应力强度校核。研究结果表明:焊缝中心为树枝胞状晶,熔合线附近为粗大柱状晶。室温时接头的平均抗拉强度为619 MPa,平均屈服强度为292 MPa,350℃时接头平均抗拉强度为475 MPa,平均屈服强度为206 MPa,拉伸接头断裂从熔合区开始贯穿整个焊缝组织,呈塑性断裂。压扁试验和反向压扁试验结果表明管接头完好。通过ANSYS分析可知,设计工况下传热管接头350℃许用应力强度150 MPa限值可满足其一次应力强度要求,且裕量较大。     

The analysis and comparison of two novel kinds of focusing elements as reflectors

In this article, two novel kinds of focusing elements as reflectors are analyzed and compared. One is the grooved Fresnel zone plate reflector with continuous phase‐correcting. The other called subzone paraboloid reflector, has the profile that consists of a series of paraboloids. Their diffraction efficiencies and bandwidths are described. The two elements still preserve the advantages of Fresnel zone plates, namely, low profile, high efficiency, and simple fabrication. Two dual‐reflector antennas using the proposed focusing elements as the main reflectors are simulated and the results show that these antennas have good radiation performances. © 2014 Wiley Periodicals, Inc. Int J RF and Microwave CAE 25:101–108, 2015.     

Thermal imaging of time-varying longitudinal defects in the internal coating of a tube

We deal with the mathematical model of the incremental degradation of the internal coating (e.g. a polymeric material) of a metallic pipe in which a fluid flows relatively fast. The fluid drags solid impurities so that longitudinal scratches, inaccessible to any direct inspection procedure, are produced on the coating. Time evolution of this kind of defects can be reconstructed from the knowledge of a sequence of temperature maps of the external surface. The time-varying orthogonal section of this damaged interface is determined as a function of time and polar angle through the identification of a suitable effective heat transfer coefficient by means of Thin Plate Approximation.     

Mixed-Metal MOF-74 Templated Catalysts for Efficient Carbon Dioxide Capture and Methanation

The vast chemical and structural tunability of metal–organic frameworks (MOFs) are beginning to be harnessed as functional supports for catalytic nanoparticles spanning a range of applications. However, a lack of straightforward methods for producing nanoparticle-encapsulated MOFs as efficient heterogeneous catalysts limits their usage. Herein, a mixed-metal MOF, NiMg-MOF-74, is utilized as a template to disperse small Ni nanoclusters throughout the parent MOF. By exploiting the difference in Ni O and Mg O coordination bond strength, Ni²⁺ is selectively reduced to form highly dispersed Ni nanoclusters constrained by the parent MOF pore diameter, while Mg²⁺ remains coordinated in the framework. By varying the ratio of Ni to Mg in the parent MOF, accessible surface area and crystallinity can be tuned upon thermal treatment, influencing CO₂ adsorption capacity and hydrogenation selectivity. The resulting Ni nanoclusters prove to be an active catalyst for CO₂ methanation and are examined using extended X-ray absorption fine structure and X-ray photoelectron spectroscopy. By preserving a segment of the Mg²⁺-containing MOF framework, the composite system retains a portion of its CO₂ adsorption capacity while continuing to deliver catalytic activity. The approach is thus critical for designing materials that can bridge the gap between carbon capture and CO₂ utilization.     

双膦胺镍-甲基铝氧烷体系催化苯乙烯聚合

研究了具有新型结构的双膦胺镍配合物N,N-双(二苯膦基)-对甲氧基苯胺二氯化镍-甲基铝氧烷(PNP-N i-MAO)催化体系对苯乙烯聚合的催化性能,考察了聚合温度、n(A l)∶n(PNP-N i)、PNP-N i的浓度和苯乙烯的浓度对催化活性、苯乙烯转化率、聚苯乙烯相对分子质量及其分布的影响,并用核磁共振和凝胶色谱对聚苯乙烯的结构进行了表征。实验结果表明,在聚合温度25℃、聚合时间1h、n(A l)∶n(PNP-N i)=300、c(苯乙烯)=2.3m ol/L、c(PNP-N i)=0.4mm ol/L、甲苯为溶剂的适宜条件下,苯乙烯的转化率可达95%以上,催化活性达到5×105g/(m ol.h)左右。核磁共振和凝胶色谱表征结果显示,所得聚苯乙烯为无规结构,重均相对分子质量约为1×104,相对分子质量分布Mw/Mn约为2。     

沉管隧道水下最终接头施工技术初探

简述了沉管隧道水下最终接头施工技术的应用现状，结合具体隧道工程实例，从外模工程、混凝土结构两方面介绍了最终接头施工技术，表明了该技术具有运用价值。     

热镀锌板(卷)工程设计中的环境保护问题

对热镀锌板(卷)的生产工艺、主要生产设备进行了简要介绍，并就其污染源(工序)、生产过程中产生的污染物及其控制措施进行了评述，同时就设计和生产中宜注意的几个环保问题进行了分析。     

微桥法镍膜的弹性模量和残余应力测量

利用MEMS技术制作了不同尺寸的镍(Ni)膜微桥结构样品。采用纳米压痕仪XP系统测量了微桥载荷与位移的关系,并结合微桥力学理论模型得到了两种不同尺寸的Ni膜的弹性模量和残余应力。结果表明,两种不同尺寸的Ni膜的弹性模量结果一致,为190 GPa左右,但是残余应力变化较大。与采用纳米压痕仪直接测得的带有硅(Si)基底的Ni膜弹性模量186.8 7.5 GPa相比较,两者符合较好。