Zeolitic-imidazolate frameworks-derived Co3S4/NiS@Ni foam heterostructure as highly efficient electrocatalyst for oxygen evolution reaction

Transition metals sulfide-based nanomaterials have recently received significant attention as a promising cathode electrode for the oxygen evolution reaction (OER) due to their easily tunable electronic, chemical, and physical properties. However, the poor electrical conductivity of metal-sulfide materials impedes their practical application in energy devices. Herein, firstly nano-sized crystals of cobalt-based zeolitic-imidazolate framework (Co-ZIF) arrays were fabricated on nickel-form (NF) as the sacrificial template by a facile solution method to enhance the electrical conductivity of the electrocatalyst. Then, the Co₃S₄/NiS@NF heterostructured arrays were synthesized by a simple hydrothermal route. The Co-ZIFs derived Co₃S₄ nanosheets are grown successfully on NiS nanorods during the hydrothermal sulfurization process. The bimetallic sulfide-based Co₃S₄/NiS@NF-12 electrocatalyst demonstrated a very low overpotential of 119 mV at 10 mA cm^?2 for OER, which is much lower than that of mono-metal sulfide NiS@NF (201 mV) and ruthenium-oxide (RuO₂) on NF (440 mV) electrocatalysts. Furthermore, the Co₃S₄/NiS@NF-12 electrocatalyst showed high stability during cyclic voltammetry and chronoamperometry measurements. This research work offers an effective strategy for fabricating high-performance non-precious OER electrocatalysts.     

Iron(II) Sulfate(VI) from Titania Production as a Raw Material for Preparation of Hydrogen Sulfide Sorbents

A hybrid sorbent material for removal of hydrogen sulfide from air was developed. The material is based on activated carbon and iron compounds obtained from waste iron(II) sulfate(VI) heptahydrate. The iron salt is deposited on the carbonaceous support and subjected to oxidation (Fe²⁺ to Fe³⁺) using atmospheric oxygen under alkaline conditions. An effect of H₂O₂ addition to the process on the composition of the resultant material was also examined. X-ray diffraction (XRD) analyses confirmed easy conversion of waste FeSO₄·7H₂O to iron oxides Fe₃O₄ and FeOOH. The activated carbon supporting iron oxides revealed a higher efficiency in H₂S elimination from air compared to the commercial activated carbon, without any modification.     

Effects of anion and cation doping on the thermoelectric properties of n-type PbS

The PbCl_xS_1-x and Pb_1-xBi_xS (x? =?0–0.05) bulks were fabricated with a facile method of hydrothermal synthesis and microwave sintering, and the effect of anionic and cationic donors on the thermoelectric performance of PbS was investigated. Although Cl^? and Bi³⁺ both effectively improved the thermoelectric properties of n-type PbS, more excellent thermoelectric performance was obtained from Cl^? doped samples because of higher electrical property and lower thermal conductivity at higher temperature (T? >?600?K). The thermoelectric figure of merit (ZT) reaches 1.04 for PbCl_0.015S_0.985 at 800?K and increases with temperature increasing without sign of saturation, which is probably the highest value ever reported for single-phase polycrystalline n-type PbS. The results also indicate that the hydrothermal synthesis and microwave sintering can realize anion doping as well as cation doping for n-type PbS at low cost, and PbS should be a robust alternative for PbTe thermoelectric materials.     

Mixed-Metal MOF-74 Templated Catalysts for Efficient Carbon Dioxide Capture and Methanation

The vast chemical and structural tunability of metal–organic frameworks (MOFs) are beginning to be harnessed as functional supports for catalytic nanoparticles spanning a range of applications. However, a lack of straightforward methods for producing nanoparticle-encapsulated MOFs as efficient heterogeneous catalysts limits their usage. Herein, a mixed-metal MOF, NiMg-MOF-74, is utilized as a template to disperse small Ni nanoclusters throughout the parent MOF. By exploiting the difference in Ni O and Mg O coordination bond strength, Ni²⁺ is selectively reduced to form highly dispersed Ni nanoclusters constrained by the parent MOF pore diameter, while Mg²⁺ remains coordinated in the framework. By varying the ratio of Ni to Mg in the parent MOF, accessible surface area and crystallinity can be tuned upon thermal treatment, influencing CO₂ adsorption capacity and hydrogenation selectivity. The resulting Ni nanoclusters prove to be an active catalyst for CO₂ methanation and are examined using extended X-ray absorption fine structure and X-ray photoelectron spectroscopy. By preserving a segment of the Mg²⁺-containing MOF framework, the composite system retains a portion of its CO₂ adsorption capacity while continuing to deliver catalytic activity. The approach is thus critical for designing materials that can bridge the gap between carbon capture and CO₂ utilization.     

双膦胺镍-甲基铝氧烷体系催化苯乙烯聚合

研究了具有新型结构的双膦胺镍配合物N,N-双(二苯膦基)-对甲氧基苯胺二氯化镍-甲基铝氧烷(PNP-N i-MAO)催化体系对苯乙烯聚合的催化性能,考察了聚合温度、n(A l)∶n(PNP-N i)、PNP-N i的浓度和苯乙烯的浓度对催化活性、苯乙烯转化率、聚苯乙烯相对分子质量及其分布的影响,并用核磁共振和凝胶色谱对聚苯乙烯的结构进行了表征。实验结果表明,在聚合温度25℃、聚合时间1h、n(A l)∶n(PNP-N i)=300、c(苯乙烯)=2.3m ol/L、c(PNP-N i)=0.4mm ol/L、甲苯为溶剂的适宜条件下,苯乙烯的转化率可达95%以上,催化活性达到5×105g/(m ol.h)左右。核磁共振和凝胶色谱表征结果显示,所得聚苯乙烯为无规结构,重均相对分子质量约为1×104,相对分子质量分布Mw/Mn约为2。     

Method for Preparation of Semiconductor Quantum‐Rod Lasers in a Cylindrical Microcavity

An efficient method for preparation of semiconductor quantum rod films for robust lasing in a cylindrical microcavity is reported. A capillary tube, serving as the laser cavity, is filled with a solution of nanocrystals and irradiated with a series of intense nanosecond laser pulses to produce a nanocrystal film on the capillary surface. The films exhibit intense room‐temperature lasing in whispering‐gallery modes that develop at the film–capillary interface as corroborated from the spacing detected for the lasing modes. Good lasing stability is observed at moderate pump powers. The method was applied successfully to several quantum‐rod samples of various sizes.     

软锰矿氧化硫化钡制高纯碳酸锰和氢氧化钡工艺研究

软锰矿同硫化钡溶液在较低温度下进行氧化还原反应，当硫化钡含量控制在26-75g／L范围内，软锰矿与硫化钡的物质的量比为2．5-3，反应时间50-60min，软锰矿被硫化钡还原为MnO，其还原率可达93．5％以上；还原后的锰用硫酸浸取，溶液经除杂后，与碳酸铵反应而制成高纯碳酸锰。硫化钡则被氧化为氢氧化钡，经蒸发、结晶而制得入水氢氧化钡，其回收利用率高速95％。     

微桥法镍膜的弹性模量和残余应力测量

利用MEMS技术制作了不同尺寸的镍(Ni)膜微桥结构样品。采用纳米压痕仪XP系统测量了微桥载荷与位移的关系,并结合微桥力学理论模型得到了两种不同尺寸的Ni膜的弹性模量和残余应力。结果表明,两种不同尺寸的Ni膜的弹性模量结果一致,为190 GPa左右,但是残余应力变化较大。与采用纳米压痕仪直接测得的带有硅(Si)基底的Ni膜弹性模量186.8 7.5 GPa相比较,两者符合较好。     

硫化氢吸收液的电化学分解条件研究

理想的脱硫工艺应满足体积小、费用低、净化度高、无二次污染等要求。在碱性溶液吸收微量硫化氢时同步进行电解，可有效减小设备体积，并将硫化氢转变为氢气和硫磺，不产生恶性气味。为此，实验研究了温度、浓度、电流密度、pH值等因素对电解阳极过程的影响，确定了适宜的电解条件，并在该条件下进行了吸收实验。结果表明，在最佳电解条件下，硫化钠溶液能充分吸收天然气中经变压吸附提浓的硫化氢（800 mg/m³），吸收率大于99.9％。