Phosphorylated chitosan/poly(vinyl alcohol) based proton exchange membranes modified with propylammonium nitrate ionic liquid and silica filler for fuel cell applications

In our previous work, phosphorylated chitosan was modified through polymer blending with poly(vinyl alcohol) (PVA) polymer to produce N-methylene phosphonic chitosan/poly(vinyl alcohol) (NMPC/PVA) composite membranes. The aim of this work is to further investigate the effects of a propylammonium nitrate (PAN) ionic liquid and/or silicon dioxide (SiO₂) filler on the morphology and physical properties of NMPC/PVA composite membranes. The temperature-dependent ionic conductivity of the composite membranes with various ionic liquid and filler compositions was studied by varying the loading of PAN ionic liquid and SiO₂-PAN filler in the range of 5–20 wt%. As the loading of PAN ionic liquid increased in the NMPC/PVA membrane matrix, the ionic conductivity value also increased with the highest value of 0.53 × 10^?3 S cm^?1 at 25 °C and increased to 1.54 × 10^?3 S cm^?1 at 100 °C with 20 wt% PAN. The NMPC/PVA-PAN (20 wt%) composite membrane also exhibited the highest water uptake and ion exchange capacity, with values of 60.5% and 0.60 mequiv g^?1, respectively. In addition, in the single-cell performance test, the NMPC/PVA-PAN (20 wt%) composite membrane displayed a maximum power density, which was increased by approximately 14% compared to the NMPC/PVA composite membrane with 5 wt% SiO₂-PAN. This work demonstrated that modified NMPC/PVA composite membranes with ionic liquid PAN and/or SiO₂ filler showed enhanced performance compared with unmodified NMPC/PVA composite membranes for proton exchange membrane fuel cells.     

Chemoenzymatic Asymmetric Synthesis of Pyridine-Based α-Fluorinated Secondary Alcohols

Fluoro-substituted and heteroaromatic compounds are valuable intermediates for a variety of applications in pharma- and agrochemistry and synthetic chemistry. This study investigates the chemoenzymatic preparation of chiral alcohols bearing a heteroaromatic ring with an increasing degree of fluorination in α-position. Starting from readily available picoline derivatives prochiral α-halogenated acyl moieties were introduced with excellent selectivity and 64–95 % yield. The formed carbonyl group was subsequently reduced to the corresponding alcohols using the alcohol dehydrogenase from Lactobacillus kefir, yielding an enantiomeric excess of 95–>99 % and up to 98 % yield.     

Electrical Breakdown Properties and Space Charge Formation in High Temperature Region in Ultraviolet Ray Irradiated PVC

Polyvinyl chloride (PVC) is the most popular insulating material for electric wiring instruments. However, an exothermic reaction above 150 °C may cause deterioration of the insulating properties of PVC. Therefore, it is important to clarify the heat degradation in PVC, not only to investigate the ignition of electrical wiring products but also to use electrical products safely. It is known that ultraviolet (UV) irradiation causes chemical deterioration of PVC and an increase in its conductivity. Generally, it has been thought that the electrical breakdown properties, electrical conduction, and insulating performance are affected by space charge accumulation in an insulating material. A high temperature pulsed electroacoustic (PEA) system usable up to 250 °C has been developed, and the PEA system can measure the space charge distribution and conduction current in the high temperature range simultaneously. In this investigation, the space charge distribution and conduction current were measured up to electrical breakdown in a non‐UV irradiated sample (normal PVC) and in 353 nm and 253 nm UV‐irradiated PVC samples in the range from room temperature to 200 °C in a DC electric field. In the short wavelength UV irradiated PVC sample (253 nm, 300 h), a deterioration of breakdown strength at 90 °C to 150 °C and negative packet‐like charges were observed at 60 °C and 100 °C, a positive charge accumulated in front of both the anode and cathode above 90 °C, and a higher electric field near the cathode side because the positive charge of the cathode side was greater.     

阳离子型高温酸化缓蚀剂的合成及其性能评价

针对Mannich碱型缓蚀剂存在的溶解性不好和缓蚀率不高等问题,以甲醛、环己酮和苯胺为原料,合成了一种Mannich碱型缓蚀剂CH-9,将其阳离子化后,再与丙炔醇复配,得到了阳离子型高温酸化缓蚀剂CH-10。由室内性能评价可知,CH-10在盐酸中有良好的溶解分散性;与酸液中其他添加剂如粘土稳定剂和铁离子稳定剂的配伍性良好,不会对酸化地层造成堵塞;在90℃和常压下,在20%HCl溶液中加入浓度为1%的CH-10,其对N80钢片的腐蚀速率为4.765g/(m2·h);在120℃时,浓度为2%的CH-10对N80钢片的腐蚀速率为14.30g/(m2·h),均达到了SY/T5405-1996标准中的一级标准。     

SO4^2-／ZrO2固体超强酸的制备及其催化合成ETBE的研究

采用沉淀一浸渍法制备了负载型SO4^2-／ZrO2固体超强酸催化剂，运用IR、XRD等方法表征所制备催化剂的物化性质。结果表明，所制备的催化剂具有固体超强酸催化剂的特征，酸性与焙烧温度有关，适当提高焙烧温度有利于样品酸强度的提高，但焙烧温度过高会导致脱硫；浸渍液H2SO4浓度高有利于提高催化剂的硫含量，但是浓度过高，会在催化剂上形成硫酸盐，从而降低催化剂的比表面积和酸性。采用制备的催化剂气相催化乙醇与叔丁醇合成乙基叔丁基醚反应，乙基叔丁基醚的选择性为54．71％。     

甲磺酸铜催化合成草酸二异戊酯

制备了甲磺酸铜催化剂,对其结构进行了IR和热重分析,并用于催化草酸和异戊醇的酯化反应。结果表明,甲磺酸铜具有催化活性高、稳定,易分离,重复使用性能优良,对环境友好的特点。最佳酯化工艺条件为:n(异戊醇):n(草酸)=2．8:1,w(甲磺酸铜)=0．3％,以过量的异戊醇为带水剂,回流反应2．0 h,酯化率可达到96．8％。     

H型丝光沸石催化剂催化甲苯与叔丁醇的烷基化反应

针对合成对叔丁基甲苯传统工艺中存在的缺点,采用环境友好、可重复利用的H型丝光沸石催化剂(以下简称催化剂)进行了甲苯与叔丁醇的烷基化反应,并用X射线衍射和氨程序升温脱附等方法对不同焙烧温度下得到的催化剂的物相结构和酸性质进行了表征,研究了各种反应条件对催化剂的催化性能的影响。实验结果发现,在适宜的操作条件下,即催化剂的焙烧温度823K、反应温度180℃、反应时间3h、初始压力1.0MPa、原料与催化剂的质量比为8、叔丁醇与甲苯的摩尔比为4、溶剂环己烷与甲苯的摩尔比为5时,甲苯转化率达42.73%,叔丁基甲苯的选择性为96.30%,对叔丁基甲苯的选择性为80.37%。     

N-苄基丙烯酰胺的合成

以丙烯腈和苯甲醇为原料，浓硫酸作催化剂，合成了N-苄基丙烯酰胺（N-BAA）。考察了反应温度、反应时间和催化剂用量等因素对产物收率的影响，得出了最佳反应条件：n（丙烯腈）：n（苯甲醇）：n（浓硫酸）=3：1：1．2，反应时间3h，反应温度60℃。在最佳条件下，N-BAA的收率可达92％。每100g粗产物用10％氢氧化钠溶液提纯，精制产物纯度可达99．80％，熔点为64～65℃。通过红外光谱对产物结构进行了表征。