Determination of optical and structural properties of lithium silicate ceramics with different ratios of Sm doped

In this study, the synthesis and luminescence characterization of Samarium (Sm³⁺) doped lithium metasilicate (Li₂SiO₃) phosphor ceramic were investigated. It was presented and discussed the results obtained on the luminescence and other optical studies such as X-ray diffraction (XRD), optical absorption and luminescence properties of Li₂SiO₃:Sm³⁺ phosphor ceramic. The Li₂SiO₃ compound was shown a characteristic phase in XRD. The doping in the lithium compound was not having a significant effect on the basic crystal structure of the material. The maximum photoluminescence (PL) emission for Sm³⁺ doped Li₂SiO₃ was observed at 554, 583, 641, 725 nm and bore resemblance to the visible region of the spectrum. The glow curves of all synthesized materials have a complex peak structure after being irradiated with a ⁹⁰Sr–⁹⁰Y beta source. In addition, the peak between 400 and 600 nm was seen in the radioluminescence (RL) spectrum because of a wide peak thought to be caused by silicate.     

Structure,stability and optical parameters of cobalt zinc borate glasses

In this study, the impact of cobalt oxide (CoO) on the structure, stability, linear and nonlinear optical parameters of B₂O₃–Na₂O–ZnO glasses was scrutinized. A series of glass system (ZnCoNaB-glasses) was successfully prepared through the melt quenching approach. Optical absorbance, reflectance, transmittance and FTIR spectroscopy were performed for all ZnCoNaB-glasses. The FTIR results showed that the BO₄ units are enhanced while nonbridging oxygens are decreased with further CoO addition. Furthermore, ZnO exists as four-coordinated [ZnO₄] units and these units decreased with further doping of CoO. These structural variations produce a decreasing impact in Urbach energy and nonlinear refractive index, meanwhile enhance the glass stability. Further, the metallization criterion (M) values indicate that our glass samples can be used for a new generation of nonlinear optical glasses. The preceding results can predict that the investigated ZnCoNaB-glasses will be utilized in versatile applications; especially optical switching and computing.     

Synthesis and in vitro bioactivity assessment of injectable bioglass−organic pastes for bone tissue repair

The aim of this work was to study the bioactivity of systems based on a clinically tested bioactive glass (BG) particulates (mol%: 4.33 Na₂O−30.30 CaO−12.99 MgO−45.45 SiO₂−2.60 P₂O₅−4.33 CaF₂) and organic carriers. The cohesiveness of injectable bone graft products is of high relevance when filling complex volumetric bone defects. With this motivation behind, BG particulates with mean sizes within 11−14 μm were mixed in different proportions with glycerol (G) and polyethylene glycol (PEG) as organic carriers and the mixtures were fully injectable exhibiting Newtonian flow behaviors. The apatite forming ability was investigated using X-ray diffraction and field emission scanning electron microscopy under secondary electron mode after immersion of samples in simulated body fluid (SBF) for time durations varying between 12 h and 7 days. The results obtained revealed that in spite of the good adhesion of glycerol and PEG carriers to glass particles during preparation stage, they did not hinder the exposure of bioactive glass particulates to the direct contact with SBF solution. The results confirmed the excellent bioactivity in vitro for all compositions expressed by high biomineralization rates with the formation of crystalline hydroxyapatite being identified by XRD after 12 h of immersion in SBF solution.     

Hydroxyapatite/tricalcium silicate composites cement derived from novel two-step sol-gel process with good biocompatibility and applications as bone cement and potential coating materials

Tricalcium silicate (C₃S) and hydroxyapatite (HAp) composites were fabricated through the sol-gel process. The aim of this research is to improve the biocompatibility of C₃S through HAp addition and study the potential of using this as coating materials. The composites (HAp/C₃S) were characterised by Fourier transform infrared spectrometry, thermal gravity-differential thermal analysis and X-ray diffraction. The working and setting times of cement pastes were tested using Gillmore needle. Mechanical properties were examined by nanoindentation and material testing system. In vitro biocompatibility of the materials were studied by cell attachment and viability of L929 and MG-63 cells. HAp/C₃S as a coating material on gelatin film were measured with the surface roughness and imaged by scanning electron microscope. With the addition of HAp, no undesirable free CaO was detected with the synthesis by the sol-gel preparation. The pH values of HAp added groups were between 7.54 and 8.76, which were much lower than pure C₃S group (pH?=?11.75). For in vitro studies, the presence of HAp could effectively enhance the cell attachment and viability of both L929 and MG-63 cells grown in the extract or directly on the composites. However, the mechanical properties of the composites were impaired as compared to pure C₃S. Lastly, HAp/C₃S cement could be evenly coated on gelatin film. HAp is successfully demonstrated to improve C₃S biocompatibility with this new composites HAp/C₃S. C-75 (75% C₃S and 25% HAp), in particular, has good biocompatibility, relatively high compressive strength and can be uniformly coated onto gelatin film. Thus, C-75 is a promising material for further investigation as a coating on other biopolymers.     

Nature of heterophase inclusions in high-purity optical fiber materials as studied with 3D laser ultramicroscopy

3D laser ultramicroscopy (3D LUM) is intended specially for determining the concentration and size distribution of submicron inclusions in the bulk samples of high-purity materials for visible and IR fiber optics. In this work the 3D LUM technique is shown to be able to identify the nature of individual inclusions detected. The measurement of the light scattered by an inclusion at a varied probe beam wavelength and polarization and at a varied scattered light collection angle makes it possible to determine the inclusion refractive index. The 3D LUM possibilities are illustrated by the example of studying the inclusion nature in the As₂S₃ glass samples prepared by the direct synthesis from elements in a quartz container at elevated temperatures.     

Tribological behavior of Zr-based bulk metallic glass sliding against polymer,ceramic, and metal materials

The tribological properties of zirconium-based bulk metallic glass (BMG) sliding against polymers, steels, and ceramics at different loads and speeds were investigated. Acoustic emission (AE) technology was used to analyze wear states. The frictional coefficients of the BMG slid against the steel and ceramic balls were high but decreased with increased applied normal load and sliding speed. As the steel balls were more ductile than the ceramic ones, the steel–BMG sliding pairs generated weaker AE signals and exhibited larger wear rates. The BMG tested against the polymer balls had much lower and more stable frictional coefficients than the ones against the steel or ceramic balls because of transferred polymer layers on the BMG surfaces. The BMG against the polymer balls also exhibited the highest AE signals among the three types of counter materials used, indicating that abrasive wear dominated in the polymer-BMG sliding pairs. These results demonstrated the potential application of the BMG as a new tribomaterial that could be an alternative to the traditional crystalline metals for various counter materials.     

聚烯烃催化剂硅胶载体的制备和表征

采用并流共沉淀法制备了适用于聚烯烃催化剂的硅胶载体,为减少颗粒的聚集,在制备过程中添加一种表面活性剂。利用透射电子显微镜(TEM)、比表面积测定(BET)和X射线粉末衍射(XRD)法对制备的硅胶载体进行了表征;考察了在制备硅胶载体过程中原料硅酸钠溶液的浓度、溶液pH以及焙烧温度对产物硅胶载体的物理性能的影响。实验结果表明,硅酸钠溶液的浓度影响硅胶的初始粒子的大小,溶液pH直接影响硅酸钠的水解速率,焙烧温度影响硅胶的孔结构和比表面积。当硅酸钠溶液的浓度为0．2mol／L、溶液pH为8-9、反应温度为70℃、焙烧温度为700℃时,硅胶载体的BET比表面积为242．22m2／g、最可几孔径为16．45 nm、堆密度为0．492 1g/mL,与进口硅胶(Silica Gel 955)的物理性能相近。     

Influence of thermal treatments on the elastic parameters in iron rich metallic glasses

The change of magnetoelastic properties after thermal treatments has been investigated for two groups of metallic glasses. (Fe₇₉Co₂₁)_75+xSi_15−1.4xB_10+0.4x (x (at.%)=0, 2, 4, 6, 8, 10) has been studied both in the as-prepared state and after thermal annealing in an applied magnetic field, to achieve a particular domain structure, at temperatures well below the crystallization temperatures. Changes in the ΔE effect, magnetomechanical coupling (k) and internal friction coefficient (Q⁻¹) are reported, reaching values of about 60% of the saturation value E_S. Fe₆₄Ni₁₀Nb₃Cu₁Si₁₃B₉ alloys annealed in vacuum for 1 h in the temperature range 350–550 °C showed maximum values of the ΔE effect and k of 61% and 0.85, respectively, accompanied by a minimum value of Q of around 2 for the sample annealed at 460 °C. These variations are related to the progress of nanocrystalization. The properties achieved are among the best reported for magnetomechanical applications.     

离子交换铒掺杂磷酸盐玻璃波导特性研究

给出有关离子交换铒掺杂磷酸盐玻璃波导的制备以及发光特性的基本结果。用Ag+ Na+ 离子交换在含有适量氧化钠的铒掺杂磷酸盐玻璃上很容易实现低损耗平面波导 ,并且离子交换过程对这种玻璃的光谱特性没有影响。     

Physical Aging of Amorphous Fructose

ABSTRACT: Physical aging of amorphous anhydrous fructose at temperature 5 °C and at 22 °C was studied using differential scanning calorimetry (DSC). The dynamic glass transition temperature, T_g0 for unaged samples was 16 °C and 13.3 °C for heating rate of 10 °C/min and 1 °C/min, respectively. The fictive temperature, T_f0 for unaged samples calculated by Richardson and Savill method was 12 °C, which is close to the dynamic value obtained from the lower DSC heating rate. The fictive temperature T_f of the aged fructose glasses at temperatures both below and above the transition region was fitted well by a non-exponential decay function (Williams-Watts form). Aging above the transition region (22 °C) for 18 d increased both the dynamic glass transition temperature T_g and the fictive temperature T_f. However, aging below the transition region (5 °C) for 1 d increased the dynamic glass transition temperature T_g but decreased the fictive temperature T_f.